Pressure-sensitive adhesive composition for optical film, pressure-sensitive adhesive layer for optical film, production method thereof, pressure-sensitive adhesive optical film and image display

A technology of optical film and adhesive layer, applied in the direction of film/sheet adhesive, adhesive type, ester copolymer adhesive, etc., can solve the problem of insufficient reworkability adhesive optical film Machinability The workability of the spacer, the unsatisfactory durability, etc., achieve the effect of suppressing the increase of the peeling force, good productivity, and fast decomposition speed

Active Publication Date: 2009-04-29
NITTO DENKO CORP
View PDF13 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the acrylic adhesives described in these patent documents can improve the initial durability, but cannot satisfy the long-term durability, and cannot fully satisfy the reworkability, workability as an adhesive optical film, relative The workability of the spacer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pressure-sensitive adhesive composition for optical film, pressure-sensitive adhesive layer for optical film, production method thereof, pressure-sensitive adhesive optical film and image display
  • Pressure-sensitive adhesive composition for optical film, pressure-sensitive adhesive layer for optical film, production method thereof, pressure-sensitive adhesive optical film and image display
  • Pressure-sensitive adhesive composition for optical film, pressure-sensitive adhesive layer for optical film, production method thereof, pressure-sensitive adhesive optical film and image display

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0168] Hereinafter, although an Example demonstrates this invention concretely, this invention is not limited to these Examples. However, the parts and % in each example are based on weight. Evaluation items in Examples and the like were measured as follows.

[0169]

[0170] The weight average molecular weight of the obtained (meth)acrylic polymer was measured by GPC (gel permeation chromatography). As the sample, a sample was dissolved in dimethylformamide to obtain a 0.1% by weight solution, which was allowed to stand overnight, and then filtered through a 0.45 μm membrane filter.

[0171] ・Analyzer: HLC-8120GPC manufactured by Tosoh Co., Ltd.

[0172] ·Column: Made by Tosoh Co., Ltd., SuperAWM-H, AW4000, AW2500

[0173] ·Column size: each 6.0mmΦ×150mm

[0174] Eluent: 30mM-lithium bromide, 30mM-phosphoric acid in dimethylformamide

[0175] ·Flow rate: 0.4ml / min

[0176] Detector: Differential Refractometer (RI)

[0177] ·Column temperature: 40℃

[0178] ·Injectio...

manufacture example 1

[0182]

[0183] Put 99.7 parts of butyl acrylate, 0.1 part of N,N-dimethylaminoethyl acrylate, 0.1 part of acrylic acid, and 4-hydroxybutyl acrylate into a four-necked flask equipped with a stirring paddle, a thermometer, a nitrogen gas introduction tube, and a cooler. 0.1 part of ester, 0.1 part of 2,2'-azobisisobutyronitrile as a polymerization initiator, and 200 parts of ethyl acetate were slowly stirred while nitrogen gas was introduced, and after nitrogen substitution, the liquid temperature in the flask was maintained to The polymerization reaction was carried out at around 60° C. for 6 hours to prepare an acrylic polymer solution. The weight average molecular weight of the acrylic polymer is 2.05 million.

manufacture example 2～14、 and comparative manufacture example 1～7

[0185] In Production Example 1, an acrylic polymer solution was prepared in the same manner as in Production Example 1, except that at least one of the type and usage-amount of monomer components was changed as shown in Table 2. However, in Production Example 14, toluene was used as a solvent instead of ethyl acetate. Table 2 shows the weight average molecular weight of the acrylic polymer obtained in each example.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A pressure-sensitive adhesive composition can form an pressure-sensitive adhesive layer that has satisfactory reworkability such that optical films can be easily peeled from liquid crystal panels with no adhesive residue and also has satisfactory processability such that it can be worked without pressure-sensitive adhesive fouling or dropout. The pressure-sensitive adhesive composition for an optical film of the present invention comprises 100 parts by weight of a (meth)acrylic polymer comprising 45 to 99.99% by weight of an alkyl (meth)acrylate monomer unit and 0.01 to 2% by weight of a tertiary amino group-containing monomer unit; and 0.01 to 2 parts by weight of a peroxide as a crosslinking agent.

Description

technical field [0001] The present invention relates to an adhesive composition for an optical film requiring transparency, an adhesive layer for an optical film formed from the adhesive composition, and a method for producing the same. Furthermore, the present invention relates to a pressure-sensitive adhesive optical film in which the above-mentioned pressure-sensitive adhesive layer for an optical film is formed on at least one surface of the optical film. Furthermore, the present invention relates to image display devices such as liquid crystal display devices and organic EL display devices using the pressure-sensitive adhesive optical film. As the above-mentioned optical film, a polarizing plate, a retardation film, an optical compensation film, a brightness improving film, and further, a member in which these are laminated can be used. Background technique [0002] In terms of liquid crystal displays, etc., it is necessary and indispensable to arrange polarizing eleme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/06C09J7/00G02B5/30G09F9/00
Inventor 井上真一外山雄祐长田润枝细川敏嗣诸石裕中野史子
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com