Plastic film preventing cultivated crabs from escaping and preparation thereof

A plastic film and raw material technology, applied in the field of plastic film and its preparation to prevent the escape of cultured crabs, can solve the problems of high cost of anti-escape facilities, increase of production costs, poor anti-escape effect, etc., and achieve the effect of excellent anti-aging performance

Inactive Publication Date: 2009-01-28
江东头
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above forms are either not effective in preventing escape or the cost of preventing escape is too high
Ordinary plastic film is used in crab breeding. Due to its low strength, it is easy to be cut by the fingertips of the crab when it escapes and climbs, and it is easily torn by the bite of dogs, cats, mice and other animals.
In addition, plastic films used in agriculture and aquaculture are prone to aging and deterioration due to exposure to the sun and rain for a long time, and they must be replaced at least two to three times a year, which not only increases production costs, wastes manpower and material resources, but also causes environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plastic film preventing cultivated crabs from escaping and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Raw material ratio:

[0028] ① Base material: LLDPE 55

[0029] LDPE 15

[0030] ② Catalyst: MLLDE 10

[0031] ③Antioxidant: 2,6-di-tert-butyl-p-cresol 2.5

[0032] Tris(3,3-di-tert-butyl-4-hydroxybenzyl)isocyanurate 0.01

[0033] ④ Enhancer: Nano-montmorillonite 10

[0034] Terpineol / crude dipentene mixture 15

[0035] (2) Process parameters:

[0036] ①Extrusion equipment extrusion internal temperature: controlled at 170°C;

[0037] ②Inflation ratio: controlled at 2.50;

[0038] ③ Traction ratio; controlled at 4.

Embodiment 2

[0040] (1) Formula ratio:

[0041] ① Base material: LLDPE 57

[0042] LDPE 17

[0043] ② Catalyst: MLLDE 12

[0044] ③Antioxidant: 2,6-di-tert-butyl-p-cresol 2.7

[0045] Tris(3,3-di-tert-butyl-4-hydroxybenzyl) isocyanurate 0.015

[0046] ④ Enhancer: Nano-montmorillonite 9

[0047] Terpineol / crude dipentene mixture 16

[0048] (2) Process parameters:

[0049] ①Extrusion equipment extrusion internal temperature: controlled at 175°C;

[0050] ②Inflation ratio: controlled at 2.7;

[0051] ③ Traction ratio; controlled at 4.5.

Embodiment 3

[0053] (1) Formula ratio:

[0054] ① Base material: LLDPE 59

[0055] LDPE19

[0056] ② Catalyst: MLLDE 14

[0057] ③Antioxidant: 2,6-di-tert-butyl-p-cresol 2.7

[0058] Tris(3,3-di-tert-butyl-4-hydroxybenzyl) isocyanurate 0.02

[0059] ④ Enhancer: Nano-montmorillonite 8

[0060] Terpineol / crude dipentene mixture 17

[0061] (2) Process parameters:

[0062] ① Extrusion internal temperature of extrusion equipment: controlled at 180°C;

[0063] ②Inflation ratio: controlled at 2.7;

[0064] ③ Traction ratio; controlled at 5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
thicknessaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a plastic membrane for preventing cultured crabs escaping and a preparation method thereof. The plastic membrane comprises the components with the following weight portions: 70 to 90 portions of polyolefin base material, 2.5 to 3.5 portions of antioxidant 2, 6 di-butyl-p-cresol, 0.01 to 0.03 portions of isocyanuric three(3,3- di-butyl-4-hydroxy benzyl) ester, 5 to 10 portions of reinforcing agent nano-montmorilonite and 15 to 20 portions of the mixture of terpineol / rough dipentene with the weight ratio of 50:50. The polyolefin base material is preferably 55 to 65 weight portions of liner low density polyethylene and 15 to 25 weight portions of low density polyethylene. As the improvement of the invention, the raw material of the plastic membrane also comprises 10 to 25 weight portions of metallocene catalyst for liner low density polyethylene. With the invention, the plastic membrane has good aging inhibiting effect and better solves the problem that the plastic membrane is easy to age and deteriorate due to sun burning and watering outside for a long time.

Description

technical field [0001] The invention relates to a plastic film for preventing cultured crabs from escaping and a preparation method thereof. Background technique [0002] For the breeding technology of famous, special and high-quality aquatic products, there are certain rules for crabs to escape. Mastering the law and taking corresponding preventive measures can effectively control the escape of crabs. In the 1980s, the method of building high mud ridges was adopted to prevent crabs from escaping. In the 1990s, there were generally three types of fences: cement brick walls, calcium-plastic board fences, and polyethylene mesh fences. The above several forms are either not effective in preventing escape or the cost of preventing escape facilities is too high. And common plastic film is used in crab breeding, because intensity is low, is easily cut off by its fingertip when crab escapes climbing and is bitten and torn by animals such as dog, cat, mouse. In addition, the plas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/00C08L23/06C08K13/02C08K5/13C08K5/3477C08K3/34C08K5/05C08K5/01C08K5/56B29C49/00B29L7/00A01K61/00
Inventor 江东头
Owner 江东头
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com