Manufacturing method of modified terylene segment thrown silk

A manufacturing method and polyester technology, which can be used in melt spinning, textiles and papermaking, etc., can solve the problems of high price of natural hemp fabrics, unfavorable promotion and application, etc., and achieve the effect of unique color effect, rough and bright style, and strong texture of fabric.

Inactive Publication Date: 2009-01-21
卢新荣
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high price of natural hemp fabrics, it is not conducive to popularization and application, and the imitation hemp fiber fabrics with better cost performance have emerged as the times require.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of modified terylene segment thrown silk

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A method for manufacturing modified polyester section twisted yarn, comprising a spinning process part and a post-processing process part, in the spinning process, the pre-crystallization temperature of cationic modified polyester chips is 150-190 °C, and the drying temperature is 152-150 °C. 192°C, the drawing ratio of the spinning spinneret is above 100, high twist is used in the post-processing process, the wire guide is refitted on the cooling plate to increase the temperature of the setting hot box, and the appropriate second overfeed of 3.0% is selected to increase the strength of the tow Twist effect and twist transfer, forced heat setting at 195°C. The pre-crystallization temperature of the cation-modified polyester chips is 158°C, and the drying temperature is 160°C. The drying conditions of the cation-modified polyester chips in the spinning process are that the water content of the dry chips is controlled below 30 ppm, and the intrinsic viscosity drop of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing modified polyester section thrown silk, comprising a spinning technical part and a post-processing technical part. In the spinning technical part, the temperature of pre-crystallization for a cationic modified polyester chip is between 150 and 190 DEG C, and the drying temperature for the cationic modified polyester chip is between 152 and 192 DEG C; and the draw ratio of a spinning nozzle is over 100. In the post-processing technical part, high twist number is adopted, a cooling plate is provided with a guide block to improve the temperature of a setting hot box, and 3.0 percent of the second overfeeding rate is suitably selected to improve the heavy twisting effect and the twist transfer for filament bundles; and heat setting is forcibly carried out at 195 DEG C. The method can produce the modified polyester section thrown silk which can maintain the excellent performance of bast fibers and make beneficial modification to the bast fibers, and is applicable to textiles.

Description

technical field [0001] The invention relates to a method for manufacturing hemp-like chemical fiber, in particular to a method for manufacturing modified polyester twisted yarn. Background technique [0002] Hemp fiber has excellent properties such as water absorption, moisture absorption, breathability, antibacterial, antibacterial, and anti-corrosion properties. The textile products made of hemp fiber are unique in their unique crisp, rough and natural style. And hemp fabric has good drape, no flash, no aurora, good wrinkle resistance, good water swelling, etc., so hemp fabric is suitable for summer clothing, bed sheets, bedding, mosquito nets, curtain screens, decorative fabrics, etc. But because the natural hemp fabric is expensive, it is not conducive to popularization and application, so the hemp-like fiber fabric with better cost performance has emerged at the historic moment. Contents of the invention [0003] The technical problem to be solved by the present inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G1/04D01D5/08
Inventor 卢新荣
Owner 卢新荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com