High strength steel plate for big thickness tall building structure and production method thereof

A high-strength steel plate, high-rise building technology, applied in rolling mill control device, heat treatment process control, metal rolling and other directions, can solve the problems of inability to meet the requirements of high-rise buildings, unable to ensure the normal progress of the project, long purchase cycle, etc. Welding performance and lamellar tear resistance, increased atmospheric corrosion resistance, simple production process effect

Inactive Publication Date: 2008-12-17
WUYANG IRON & STEEL
View PDF0 Cites 72 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The application of this kind of steel in China has always relied on foreign imports, and it has never been used in the domestic construction field. If you rely on imports, not only the price is expensive, but also the purchase cycle is long, which cannot guarantee the normal progress of the project.
Moreover, the thickness of the steel plate with this kind of performance in foreign countries is 89.4mm; some indicators cannot meet the requirements of high-rise buildings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The actual composition (by weight percentage) of the low-C high-strength steel of the present invention is: C 0.14%, Si 0.28%, Mn 1.52%, P 0.012%, S 0.003%, Al 0.053%, Nb 0.043%, V 0.076%, Ni 0.27%, Ti 0.02%, Ceq 0.43%, rolled into 110mm steel plate. Its mechanical properties: yield strength 420MPa, tensile strength: 595MPa, yield strength ratio = 0.72, δ5 = 27%, impact energy AKV (longitudinal) 143, 136, 92J at -40°C, Z direction: 40, 40, 46%.

[0021] GB6803-86 was used for the non-plastic transition temperature drop weight test. The NDT temperature was -65°C. The weldability test of the steel plate was conducted by the Construction Research Institute of China Metallurgical Group. The conventional welding heat input was welded at room temperature, and the heat affected zone and near the heat The highest hardness HV10 in the affected area is greater than 350; when the preheating temperature is higher than 150°C, the highest hardness HV ≤ 350 in the heat-affected zone a...

Embodiment 2

[0031] The actual composition (percentage by weight) of the low-C high-strength steel in this example is: C 0.18%, Si0.40%, Mn 1.62%, P 0.01%, S 0.002%, Al 0.04%, Nb 0.05%, V 0.085 %, Ni 0.45%, Ti 0.014, rolled into 110mm steel plate.

[0032] The production method of this embodiment is as follows: (1) Smelting process: the molten steel containing the above components is first smelted in an electric furnace, sent to an LF refining furnace for refining, and fed with an Al wire of 800 meters, and when the ladle temperature is ≥ 1600°C, the ladle VD Furnace vacuum treatment, adding 150kg of SiCa blocks before vacuuming, the vacuum degree is not more than 0.5 Torr, and the vacuum is broken when the vacuum holding time is ≥20 minutes, which solves the phenomenon that the molten steel is deoxidized by Al wire alone and the content of non-metallic inclusions in the steel is high, ensuring Ensure the purity of steel;

[0033] (2) Casting process: after the vacuum is broken, the tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a steel plate with high intensity and used in construction structures of high buildings with large thickness and a production method thereof. The steel plate of the invention consists of the following components according to weight percentage: less than or equal to 0.20 percent of C, less than or equal to 0.55 percent of Si, 1.00 to 1.70 percent of Mn, less than or equal to 0.025 percent of P, less than or equal to 0.010 percent of S, less than or equal to 0.70 percent of Ni, less than or equal to 0.70 percent of Cr, less than or equal to 0.20 percent of V, more than or equal to 0.015 percent of Nb, less than or equal to 0.20 percent of Ti, 0.020 to 0.060 percent of Al, and the rest is Fe and inevitable impurity. The produced Q460E-Z35 steel plate with a thickness of 100 to 110 mm is capable of meeting the requirement of high intensity steel of large-thickness construction structure (Ceq is less than or equal to 0.50 percent); the steel plate of the invention can be applied to constructing the structure of high building, has good performance of welding and anti-layer tearing, can meet the requirement of on-site key stress points, has simple production process and is capable of realizing bulk production. The high intensity steel plate of the invention has the following advantages that (1) the steel quality of the invention is purer with less than or equal to 0.025 percent of P and less than or equal to 0.010 percent of S; (2) yield ratio of the invention is relatively low and less than 0.78 actually; (3) the anti-layer tearing performance is good, and Z is larger than or equal to 35 percent in whole thickness direction; (4) low-temperature toughness at the temperature of minus 40 DEG C is good; (5) maximum thickness of the steel plate can reach 110mm.

Description

technical field [0001] The invention relates to a Q460E-Z35 steel plate for high-rise buildings with a thickness of 100-110 mm, and also relates to a production method of the high-strength steel plate for high-rise building structures with large thickness. Background technique [0002] At present, steel plates with the same or similar performance and grade as high-strength steel plates are used abroad, but they are mostly used in structures such as pressure vessels, offshore platforms, and bridges, and have never been used in China. The application of this kind of steel in China has always relied on foreign imports. It has never been used in the construction field in China. If it relies on imports, it will not only be expensive, but also have a long purchase cycle, which cannot guarantee the normal progress of the project. Moreover, the thickness of steel plates with such properties in foreign countries is up to 89.4 mm; some indicators cannot meet the requirements of high-r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/12C22C38/14C22C38/24C22C38/28C22C38/46C22C38/50C22C33/04C21C7/06C21C7/10B22D37/00B21B37/00C21D8/02C21D11/00
Inventor 梁永昌谢良法韦明赵文忠郭桐李玉谦张华红林建农赵全卿赵向政宋向前刘利香侯彩霞吕建会
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products