Method for producing nano-scale rare earth doping composite oxides sosoloid with low-temperature carbothermic method

A composite oxide, rare earth doping technology, applied in the direction of calcium/strontium/barium oxide/hydroxide, etc., can solve the problems of cumbersome steps, difficult to control particle size, etc., to achieve high reactivity, short reaction cycle, process simple effect

Inactive Publication Date: 2011-04-27
FUJIAN NORMAL UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The formation of multi-component oxide solid solution, in the existing literature, is obtained by dissolving various metal oxides with strong acid and then calcining at high temperature, the steps are cumbersome and the particle size is difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing nano-scale rare earth doping composite oxides sosoloid with low-temperature carbothermic method
  • Method for producing nano-scale rare earth doping composite oxides sosoloid with low-temperature carbothermic method
  • Method for producing nano-scale rare earth doping composite oxides sosoloid with low-temperature carbothermic method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Prepare 0.25M Ca(NO 3 ) 2 , 0.5M Ce(NO 3 ) 3 , 0.625M CaAC 2 Take 15ml of each solution and mix in a ceramic reactor, add 15ml of distilled water to further dissolve and mix, heat with an electric heating mantle, control the heating temperature to 150°C, the solution changes from sol to gel until self-propagating combustion occurs, and releases A large amount of brown gas produces a fluffy powder. After the gas is dissipated, the powder is collected, which is the self-combustion precursor powder; weigh an appropriate amount of the precursor powder and put it into a porcelain boat, and calcinate at 750°C for 2 hours in a muffle furnace to obtain a calcium oxide-based cerium-doped composite oxide solid solution.

Embodiment 2

[0022] Prepare 0.25M Ca(NO 3 ) 2 , 0.75M La(NO 3 ) 3 , 1.25M CaAC 2 Take 15ml of each solution and mix in a ceramic reactor, add 15ml of distilled water to further dissolve and mix, heat with an electric heating mantle, control the heating temperature to 140°C, the solution changes from sol to gel until self-propagating combustion occurs, and releases A large amount of brown gas produces a fluffy powder. After the gas is dissipated, the powder is collected, which is the self-combustion precursor powder; weigh an appropriate amount of the precursor powder and put it into a porcelain boat, and calcinate at 800°C for 1.5h in a muffle furnace to obtain calcium oxide-based lanthanum doped Composite oxide solid solution.

Embodiment 3

[0024] Prepare 0.4M Ca(NO 3 ) 2 , 1.0M Ce(NO 3 ) 3 , 1.0M CaAC 2 Take 15ml of each solution and mix in a ceramic reactor, add 15ml of distilled water to further dissolve and mix, heat with an electric heating mantle, control the heating temperature to 160°C, the solution changes from sol to gel until self-propagating combustion occurs, and releases A large amount of brown gas produces a fluffy powder. After the gas is dissipated, the powder is collected, which is the self-combustion precursor powder; weigh an appropriate amount of the precursor powder and put it into a porcelain boat, and calcinate at 900°C for 1 hour in a muffle furnace to obtain a calcium oxide-based cerium-doped composite oxide solid solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method using a low temperature carbothermic method to prepare a solid solution of nanometer calcium oxide based rare earth mixed with composite oxide. The method has the technical proposal that 0.25M to 0.5M of Ca(NO3)2, 0.5M to 1.0M of rare earth nitrate and 0.625 M to 1.25M of CaAC2 solution are prepared, and the same amount of solution is taken to be well mixed; distilled water is added, and the solution is further dissolved and well mixed; the solution is heated to 140 DEG C to 160 DEG C with an electric jacket, and after self-propagating combustion happens to release large amounts of brown gas and generate fluffy powder, a proper amount of precursor powder is weighted to be put into a porcelain boat; after the proper amount of precursor powder is calcined for 1 to 2 hour(s) at 750 DEG C to 900 DEG C with a muffle furnace, the solid solution of nanometer calcium oxide based rare earth mixed with composite oxide is obtained. In the invention, a new synthetic route and technology is adopted, thereby the method has the advantages of comparatively lower cost, simple technology, mild conditions, short experimental period and time and energy conservation. Simultaneously, utilizing the analysis of a modern instrument can indicate that the synthesized solid solution of nanometer calcium oxide based rare earth mixed with composite oxide is provided with a nanometer structure, and the size is uniform, thereby providing possibility for improving the application in the field of tail gas treatment and environmental friendly plastics.

Description

technical field [0001] The invention relates to a method for preparing a nano-scale calcium oxide-based rare earth-doped composite oxide solid solution by a low-temperature carbothermal reduction method. Background technique: [0002] Calcium oxide (Calcium oxide) has important applications in the environment and chemical industry. It is widely used in the treatment of solid waste incineration tail gas or flue gas. It is an acid gas such as CO under high temperature conditions (600 ° C). 2 , SO 2 , H 2 A good absorbent for S; Chen Qinghua et al. found that calcium oxide-filled environmentally digestible plastics have good performance, economic performance and environmental performance, and can also solve the processing difficulties of starch-based plastics due to high water absorption of starch. Environmentally digestible plastics can adapt to various solid waste disposal methods such as landfill and incineration, and improve the environmental digestibility of plastics. H...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F11/04
Inventor 陈庆华许兢钱庆荣肖荔人刘欣萍黄宝铨
Owner FUJIAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com