A technology for producing test, crucible
Inactive Publication Date: 2010-12-01
武钢集团有限公司
View PDF1 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
3. The above-mentioned crucible coke temperature control method is only suitable for the production of crucible coke with a very small amount of coal, but for the production of crucible coke with a large amount of coal, the constant temperature time at 950°C is too short, and the coke formed is in an obvious black semi-coke state. The coke is not yet ripe;
4. In the production of crucible coke, a solid briquette is added directly above the coal sample, or fine sand is laid first and then the briquette is placed to ensure the bulk density of coal powder. During the coking process, the volatile matter is wrapped in the colloid, which makes the center and bottom of the crucible coke block form a large sponge-like hole
In short, coking is carried out according to the above-mentioned crucible coke production method, and single coal and coal blending coking cannot be carried out.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
Embodiment 2
Embodiment 3
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a method to produce experimental crucible coke. The invention resolves the existing problems at present, such as the uneven quality of the coke due to the rough particles of coal with lower content of the fine powder, the requirement of water control on the coal sample, and the short period of constant temperature. The method to produce experimental crucible coke comprises the following steps that: air-dried coal sample with the granularity less than or equal to 1.5mm is added into a crucible, and the bulk density is 0.75-0.80t / m<3>; an asbest paper with the thicknessof 0.5-1.0mm is arranged on the coal sample, a layer of fine coke powder with the thickness of 5-10mm is arranged on the asbest paper, a perforated weight is arranged on the fine coke powder, a layerof fine coke powder with the thickness of 1-5mm is arranged on the perforated weight; after the cover is closed, the crucible is placed into an experimental coke oven and fractioned heating is carried out, with the temperature-rising speed of 4-5 DEG C / min before 300DEG C, 3 DEG C / min before 300-750 DEG C, 3.8-4.5 DEG C / min before 750-950 DEG C, and the constant temperature is maintained for 3-4 hours under 950 DEG C. The refined coke provided by the invention has even texture, good quality, and great adaptability to large-scale production.
Description
A method of producing test crucible coke technical field The present invention relates to a method for producing coke, more specifically, it belongs to a method for producing test crucible coke. Background technique With the increasing shortage of coking coal resources, there are many types and large quantities of single coking coal commonly used in coking plants, so choose a reasonable coal blending plan, especially evaluate the thermal properties of single coal coke and coal blending with different ratios , the workload is very large, so using the crucible coke experiment for research can save a lot of manpower and energy consumption. At present, the operating procedures for preparing crucible coke are mainly derived from the simulation of coking in industrial large-scale coke ovens. The particle size of coal samples is less than 3mm and greater than 85%, the water content of coal samples is about 10%, and the bulk density is about 0.75t / m3. block; control the temperat...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10B57/00
Inventor 项茹薛改凤陈鹏张前香刘尚超宋子逵鲍俊芳
Owner 武钢集团有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com