Composite water-retaining thickening material for commodity mortar and using method thereof

A water-retaining, thickening, commercial mortar technology, which is applied in the field of building materials, can solve the complex and strict technical requirements for commercial mortar preparation, and achieve the effects of reasonable product components, reduced cracking hazards, and reduced shrinkage

Active Publication Date: 2008-05-28
上海曹杨建筑粘合剂厂
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the technical requirements for the preparation of commercial mortar are very complicated and strict.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1, a composite water-retaining thickening material for commercial mortar (by weight percentage, the same below). Calcium-based bentonite 68.07%, sodium-based bentonite 6.82%, kaolin 3.40%, sepiolite 2.72%, zeolite 3.41%, cellulose ether (viscosity 200000mPa.s) 1.97%, lignosulfonate 0%, fly ash 13.61 % After mixing, it is put into a pulverizer for grinding (until the 0.08mm square hole sieve percentage is less than 40%). Compared with the ground mortar without any admixture, the ground mortar mixed with the product of the present invention (the amount is 6% of the weight of the cementitious material) is not only improved in workability and viscosity, but also has a degree of delamination of 10mm. The water retention rate increased from 65% to 92%, the 28d compressive strength increased by 5%, the bond strength increased from about 0.2MPa to 0.5MPa, the shrinkage rate decreased by 30%, and the strength loss rate decreased by 40% after 50 freeze-thaw cycles. St...

Embodiment 2

[0033] Embodiment 2, the compound type water-retaining thickening material that is used for commercial mortar presses calcium-based bentonite 39.00%, sodium-based bentonite 15.60%, kaolin 15.60%, sepiolite 7.80%, zeolite 7.80%, cellulose ether (viscosity 100000mPa.s ) 2.50%, lignosulfonate 0%, and fly ash 11.70% are mixed and put into a pulverizer for grinding (until the sieve percentage of 0.08mm square hole sieve is less than 40%). Compared with the masonry mortar without any admixture, the masonry mortar mixed with the product of the present invention (the amount is 9% of the weight of the cementitious material) is not only improved in workability and viscosity, but also has only 13mm, the water retention rate increased from 68% to 94%, the 28d compressive strength increased by 8%, the bond strength increased from about 0.2MPa to 0.5MPa, the shrinkage rate decreased by 25%, and the strength loss rate decreased by 35% after 50 freeze-thaw cycles , meeting the standard requir...

Embodiment 3

[0034]Embodiment 3, the compound type water-retaining thickening material that is used for commodity mortar presses calcium base bentonite 34.96%, sodium base bentonite 17.48%, kaolin 12.24%, sepiolite 10.49%, zeolite 8.74%, cellulose ether (viscosity 75000mPa.s ) 2.80%, fly ash 8.74%, and lignosulfonate 4.55% are mixed and put into a pulverizer for grinding (until the sieve percentage of 0.08mm square hole sieve is less than 40%). Compared with the plastering mortar without any admixture, the product of the present invention (dosage is 40kg / m 3 )’s plastering mortar not only has greatly improved workability and viscosity, but also has a layered degree of only 15mm, water retention rate increased from 70% to 95%, setting time extended from 6.5h to 9.0h, and 28d compressive strength increased 6%, the bonding strength is increased from about 0.15MPa to 0.4MPa, the shrinkage rate is reduced by 35%, and the strength loss rate is reduced by 32% after 50 freeze-thaw cycles, meeting ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of building materials, in particular to a compound water-preservation and viscosity promoting material used in commercial mortar and a preparation method thereof. Ca-bentonite, na-bentonite, kaolin, sepiolite, zeolite, cellulose ether (viscosity 10000mPa.s-200000mPa.s), fly ash and lignosulfonate are mixed and then ground till sieve residue is less than 40 percent with 0.08mm square opening sieve. The invention can greatly improve the cohesiveness and consistency of mortar, reduce the stratification of mortar and improve the water retaining rate of the mortar and perfect the uniformity, stability and constructability of mortar mixture, thus promoting construction efficiency and reducing environmental pollution. Being added with the material of the invention, the strength and durability of the mortar can be improved and the hazard of shrinkage and crack can be obviously reduced. The invention is specially used in the preparation of (dry-mixed, ready-mixed) mortar for masonry, plastering and ground commodities and also applied to the preparation of thermal insulation mortar and decorative plaster, etc.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a composite water-retaining and thickening material for commercial mortar and its application method. Background technique [0002] In order to speed up the energy saving and emission reduction of my country's construction industry and promote the construction of a harmonious society, since 2000, Shanghai, my country has started the research and trial production application of commercial mortar. During this process, it was found that compared with traditional mortar, commercial mortar has great advantages in terms of ease of construction, strength, durability, construction progress, labor intensity, resource and energy saving, and environmental protection. Subsequently, my country's Beijing, Guangzhou, Shenzhen and other cities successively promoted the production and use of commercial mortar. On June 6, 2007, six ministries and commissions including the M...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/38C04B14/04C04B14/10C04B18/08C04B24/18
CPCC04B2103/44C04B2103/46C04B40/0039Y02W30/91C04B14/042C04B14/047C04B14/104C04B14/106C04B18/08C04B24/18C04B24/383C04B28/02C04B2103/0006C04B2103/001
Inventor 孙振平蒋正武于龙庞敏
Owner 上海曹杨建筑粘合剂厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com