Anti hemorrhagic healing traumatic material of chitosan based fiber in water-solubility, preparation method and application

A technology of water-soluble chitosan and chitosan fiber, which is applied in the field of medical materials, can solve the problems of long degradation time of carboxymethyl chitosan fiber, inflammatory response, and inapplicability, so as to promote wound healing and good compatibility , the effect of convenient operation

Active Publication Date: 2007-10-10
青岛博益特生物材料股份有限公司
View PDF1 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, carboxymethyl chitosan fiber with low degree of substitution takes a long time to degrade in the body, and it will also cause the body's inflammatory response, so it is not suitable for in vivo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti hemorrhagic healing traumatic material of chitosan based fiber in water-solubility, preparation method and application
  • Anti hemorrhagic healing traumatic material of chitosan based fiber in water-solubility, preparation method and application
  • Anti hemorrhagic healing traumatic material of chitosan based fiber in water-solubility, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The preparation of carboxymethyl chitosan fiber non-woven fabric: take chitosan fiber non-woven fabric 12g, place in the wide mouth reagent bottle of 500ml, add the KOH aqueous solution 200g of 45% (weight percent concentration, the same below) , stirring to immerse the chitosan fiber non-woven fabric completely in the lye, place it at -20° C. for 24 hours, and alkalize it to obtain an alkalized chitosan fiber non-woven fabric. Take out this alkalized chitosan nonwoven fabric, put into the jar of 500ml, add 55% acetone aqueous solution 180g as reaction medium, add the ethanol solution 85g of the monochloroacetic acid of 50% under shaking condition as reaction reagent, room temperature Under reaction 9hr, obtain carboxymethyl chitosan fiber non-woven fabric. Take out the carboxymethyl chitosan fiber non-woven fabric, fully wash it to neutrality with 60% acetone aqueous solution as washing liquid, dehydrate with anhydrous acetone, squeeze or centrifugally dry, remove exce...

Embodiment 2

[0014] The preparation of carboxymethyl chitosan fiber: take chitosan fiber 5g, place in the wide-mouth reagent bottle of 500ml, add 30% NaOH aqueous solution 160g, stir to make chitosan fiber all immerse in the lye, under room temperature Place it for 48 hours to alkalize to obtain alkalized chitosan fiber. Take out this alkalized chitosan fiber, put into the jar of 500ml, add methanol 160g as reaction medium, add the methanol solution 46g of 50% monochloroacetic acid under shaking condition as reaction reagent, react 8hr under the room temperature, obtain carboxylate Methyl chitosan fiber. Take out the carboxymethyl chitosan fiber, use methanol as washing liquid to fully wash to neutral, squeeze or centrifugally dry, remove excess liquid, and then put it in a container containing P 2 o 5 Vacuum-dried in a special vacuum desiccator, and evaporated the residual organic solvent in the dried product at 50°C to obtain carboxymethyl chitosan fibers with a carboxymethyl substitut...

Embodiment 3

[0017] Preparation of carboxymethyl chitosan fiber knitted fabric: take 10 g of chitosan fiber knitted fabric, place it in a 500 ml wide-mouth reagent bottle, add 200 g of 40% NaOH aqueous solution, stir to make the chitosan fiber knitted fabric fully immersed In the lye, place it at 0-4°C for 48 hours to alkalize to obtain alkalized chitosan fiber knitted fabric. Take out the alkalized knitted fabric, put it into a 500ml wide-mouth bottle, add 135g of 90% ethanol aqueous solution and 50g of dimethyl sulfoxide as the reaction medium, and add 70g of 50% ethanol solution of monochloroacetic acid under shaking conditions as the reaction reagent , and reacted at room temperature for 10 hours to obtain carboxymethyl chitosan fiber knitted fabric. Take out the carboxymethyl chitosan knitted fabric, use 75% ethanol aqueous solution as washing liquid to fully wash to neutral, dehydrate with absolute ethanol, squeeze or centrifugally dry, remove excess liquid, then put it in a containe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A water-soluble chitosan based fiber material for stopping hemorrhage and promoting healing of wound is made of carboxymethyl chitosan fibers, or hydroxypropyl chitosan fibers, hydroxyethyl chitosan fibers, or carboxymethyl hydroxyethyl chitosan fibers. Its preparing process is also disclosed.

Description

technical field [0001] The invention relates to a medical material, in particular to a water-soluble chitosan-based fiber hemostatic and healing material and a preparation method and application thereof. Background technique [0002] Controlling bleeding, hemostasis, and promoting incision healing during and after clinical operations are very necessary and important for shortening operation time and reducing postoperative complications. Conventional hemostasis methods such as ligation, suture, and electrocoagulation are often used in clinical operation and trauma hemostasis, but these hemostatic methods are not always effective in controlling bleeding, especially in the operation of solid organs with multiple vessels, so according to According to clinical needs, a variety of local hemostatic materials have been used clinically. These hemostatic materials mainly include gelatin sponge, collagen sponge, fibrin glue, oxidized cellulose and other products. Gelatin sponge has be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/28
CPCD01F9/00A61L15/28A61L31/042D01D1/02D01D5/06C08L5/08
Inventor 刘万顺韩宝芹顾其胜
Owner 青岛博益特生物材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com