Superhigh intensity electric ceramic formulation

An ultra-high-strength, electric porcelain technology, applied in the field of electric porcelain, can solve the problems of loss of funds, inability to meet the requirements of 220-1000KV power transmission and transformation systems, and failure of porcelain insulators to meet the requirements of porcelain performance.

Active Publication Date: 2007-08-15
抚顺高科电瓷电气制造有限公司
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of the electric power industry and the continuous improvement of voltage levels, my country's requirements for porcelain insulators used in high-voltage and ultra-high-voltage power transmission and transformation systems are also getting higher and higher, but the porcelain performance of existing porcelain insulators has not reached Requirements, especially the flexural strength of porcelain, is generally only at the level of 140Mpa ~ 160Mpa, which cannot meet the requirements of 220 ~ 1000KV power transmission and transformation system at all.
At present, such products can only rely on imports to meet domestic demand, which not only causes a large loss of funds, but also seriously hinders the development of the electric power industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Ash clay 8% Feldspar powder 9%

[0020] Burnt Alum Stone Powder 47% Zhangwu Clay 6%

[0021] Faku Clay 5% Kuancheng Clay 7%

[0022] Baofeng Clay 8.5% Yongji Clay 8%

[0023] Modified Bentonite 1.5%

[0024] The product made according to the proportioning of the present embodiment, the main porcelain properties are as follows:

[0025] Flexural strength: 170Mpa (unglazed); 231Mpa (glazed)

[0026] Hot and cold performance: 180K (unglazed); 230K (glazed)

[0027] Volume resistivity: 1.26×1016Ω·cm

[0028] Surface resistivity: 1.21×1013Ω·cm

[0029] Electrical strength: 28KV / mm

[0030] According to this embodiment, products such as 110KV and 220KV circuit breaker porcelain sleeves, 220KV outlet porcelain sleeves, wall bushings, 500KV~1000KV circuit breaker pillars and other products have been produced in small batches. The damage value is not less than 5.0Mpa.

Embodiment 2

[0032] Ash clay 10% Feldspar powder 12%

[0033] Burnt Alum Stone Powder 42% Zhangwu Clay 9%

[0034] Faku Clay 9% Kuancheng Clay 4%

[0035] Baofeng Clay 7% Yongji Clay 6%

[0036] Modified bentonite 1.0%

[0037] The product made according to the proportioning of the present embodiment, the main porcelain properties are as follows:

[0038] Flexural strength: 168.3Mpa (unglazed); 225.1Mpa (glazed)

[0039] Hot and cold performance: 180K (unglazed); 225K (glazed)

[0040] Volume resistivity: 2.34×1016Ω·cm

[0041] Surface resistivity: 3.21×1013Ω·cm

[0042] Electrical strength: 29KV / mm

[0043] According to this embodiment, porcelain insulator products of 220-1000KV grade have been produced in small batches, and the flexural failure value is not less than 55KN.m, and the internal pressure failure value is not less than 3.7Mpa.

Embodiment 3

[0045] Ash clay 12% Feldspar powder 13%

[0046] Burnt Alum Stone Powder 37% Zhangwu Clay 10%

[0047] Faku Clay 10% Kuancheng Clay 8%

[0048] Baofeng Clay 5.5% Yongji Clay 4%

[0049] Modified bentonite 0.5%

[0050] The product made according to the proportioning of the present embodiment, the main porcelain properties are as follows:

[0051] Flexural strength: 165.7Mpa (unglazed); 221.8Mpa (glazed)

[0052] Hot and cold performance: 185K (unglazed); 230K (glazed)

[0053] Volume resistivity: 3.23×1016Ω·cm

[0054] Surface resistivity: 4.52×1013Ω·cm

[0055] Electric strength: 30KV / mm

[0056] According to this embodiment, 110-1000KV grade porcelain insulator products have been produced in small batches, the bending failure value of the lever arm extending to 3680mm is not less than 30.1KN.m, and the internal pressure failure value is not less than 4.25Mpa.

[0057] The porcelain properties of the electric porcelain products produced according to the formula of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hyperhigh-strength electric porcelain formula, which comprises the following parts: 8-12% Fraxinus mandshurica clay, 9-13% feldspar powder, 37-47% sintered vitriol powder and 6-10% zhangwu clay, 5-10% faku clay, 4-8% kuancheng clay, 5.5-8.5% baofeng clay, 4-8% yongji clay and 0.5-1.5% modified alta-mud. Each property of electric porcelain reaches and exceeds V-typed standard in the GB8411 with transverse strength at 165-170Mpa without glaze or 221 231Mpa with glaze, which supplements the blank of this kind of product in our country.

Description

1. Technical field [0001] The invention belongs to the technical field of electric porcelain, in particular to a formula for producing ultra-high-strength electric porcelain. 2. Background technology [0002] With the rapid development of the electric power industry and the continuous improvement of the voltage level, my country's requirements for porcelain insulators used in high-voltage and ultra-high-voltage power transmission and transformation systems are getting higher and higher, and the porcelain performance of the existing porcelain insulators has not reached the same level. Requirements, especially the flexural strength of porcelain, are generally only at the level of 140Mpa ~ 160Mpa, which cannot meet the requirements of 220 ~ 1000KV power transmission and transformation systems. At present, such products can only be imported to meet domestic demand, which not only causes a large loss of funds, but also seriously hinders the development of the electric power indust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/16
Inventor 路延枢路世伟
Owner 抚顺高科电瓷电气制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com