Welding technology for broken and waste core rod

A welding process and mandrel technology, which is applied in the field of reuse of waste mandrels, and can solve problems such as unusable waste mandrels

Active Publication Date: 2009-02-25
TIANJIN STEEL PIPE MFG CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] In order to solve the technical problem that the waste mandrel cannot be used, the purpose of the present invention is to provide a welding process for the waste mandrel,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding technology for broken and waste core rod
  • Welding technology for broken and waste core rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The welding process of the waste mandrel of the present invention will be described in conjunction with the accompanying drawings and embodiments.

[0032] The structure of the broken mandrel after welding is as follows figure 1 As shown, in order to ensure that there will be no broken mandrel accidents in production, reduce welding workload, reduce repair costs, and ensure the straightness of the mandrel, firstly, the rear section of the broken mandrel 1 is machined into a threaded connection with a ladder buckle. Column 3, on the front broken mandrel 2, a threaded hole matching the threaded connection column 3 with a partial ladder buckle is processed, and an undercut 4 is left, between the rear broken mandrel 1 and the front broken mandrel 2 A U-shaped welding groove 5 is processed at the butt joint. The advantage of the U-shaped groove is that it can save welding materials and reduce the labor intensity of welders.

[0033] Then use the mandrel screwing machine to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a broken core bar welding process that comprises the thread processing and extension, preheating and welding bar selection, heat treatment after the welding, rotary cooling and grinding. In the process of preheating and welding bar selection, it welds continuously at one time to maintain the temperature between layers. In after welding heat treatment, it is cooled gradually using heat insulating material covering the welding spot under working environment lower than 5deg.C. It uses broken core bar to weld into qualified core bar blank, after lathe processing to reach the durability of the imported ones. If there isn't any crack occur, it means that the welding has reached expectation. It reduces the imported core bar blank with reduced capital and improved productivity.

Description

technical field [0001] The invention relates to the reutilization of the waste mandrel rods interrupted by the production of steel pipes, in particular to a welding process for the broken waste mandrel rods. Background technique [0002] The mandrel is one of the main deformation tools of the limited mandrel continuous rolling mill in the pipe mill. For example, the mandrel used in the Φ250MPM continuous rolling mill has always been imported, and the value is expensive. Rational use of mandrels to fully increase the service life of mandrels is one of the important tasks to reduce production costs. [0003] The steel number of mandrel material is X35CrMOVo5 H13, its chemical composition: (%) [0004] C: 0.30——0.38 Mn: 0.60Max [0005] Si: 0.70 - 1.20C r: 4.50 - 5.50 [0006] V: 0.80——1.20 Mo: 1.00——1.50 [0007] S: 0.008MaxS+P: 0.02max [0008] By calculating the carbon equivalent C E At 1.88%, much higher than the ? 0.6%, extremely poor solderability. [0009] The wo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23P6/00B21B25/00
Inventor 张金钢郭会勇田志国
Owner TIANJIN STEEL PIPE MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap