Plastic container comprising cyclic polyolefin layer
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Image
Examples
example 1
[0072]A solution obtained by diluting commercially available Radicut (registered trademark) injection 30 mg (manufactured and distributed by Mitsubishi Tanabe Pharma Corporation) with 100 mL of a normal saline was filled into an infusion bag formed with each of various types of films A01 to A05 and Comparative Example 1 shown in Table 1, and it was then sterilized (115° C., 30 minutes). The content of a main component (Edaravone) was measured before and after the sterilization. The results are shown in Table 2. In the case of using a film comprising a cyclic polyolefin polymer or a cyclic polyolefin copolymer as a barrier layer, a significant reduction in the content of the component was not observed after the sterilization. On the other hand, in the case of using a film constituted only with polypropylene (ZELAS (registered trademark) RT-267A-1, MC717, 7023), a reduction in the content of the component was observed after sterilization.
TABLE 2Medicament adsorption on bag during ster...
example 2
[0074]A solution obtained by diluting commercially available Radicut (registered trademark) injection 30 mg (manufactured and distributed by Mitsubishi Tanabe Pharma Corporation) with 100 mL of a normal saline was filled into an infusion bag formed with each of various types of films of C01, C02 and Comparative Example 1 shown in Table 1, and it was then sterilized (115° C., 30 minutes). Thereafter, a severe test (60° C., 4 weeks) was carried out on each sample wrapped with a second wrapping material containing AGELESS as an oxygen absorber and having a suppressed gas permeability, which had been formed by silica evaporation. As shown in Table 4, in the case of the bag of Comparative Example 1, a reduction in the content of the component was observed over time. However, such reduction in the content of the component was not observed in the case of the bags of C01 and C02.
TABLE 4Severe stability test of bags containing COP as barrier layers (60° C.)AfterAfterfillingsterilizationWeek ...
PUM
Property | Measurement | Unit |
---|---|---|
Temperature | aaaaa | aaaaa |
Temperature | aaaaa | aaaaa |
Temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap