Abstract

The invention relates to a coating agent composition comprising an isocyanate-group-containing prepolymer obtained by reacting a polyol comprising a polyoxyalkylene polyol having 2-4 hydroxyl groups on average, an oxyethylene group content of 85-100% by mass based on all oxyalkylene groups (100% by mass), and an arithmetic-average molecular weight of 800-2,500 with an alicyclic isocyanate and / or an aliphatic isocyanate in the presence of an organic acid bismuth salt catalyst, the isocyanate(s) being used in such an amount as to result in an isocyanate index of 150-300. The invention can provide a coating agent composition which forms a coating film or film having moisture permeability, excellent in mechanical properties and yellowing resistance, having laundering durability and resistance to sweat deterioration, and containing no organotin compounds.

Description

TECHNICAL FIELD [0001] The present invention relates to a coating agent composition, an article having a coating film obtained from the coating agent composition, and a film obtained from the coating agent composition. BACKGROUND ART [0002] A moisture-permeable material which comprises a porous base, e.g., a fabric, having a substantially non-porous layer of a hydrophilic polyurethane resin on a surface thereof and which is suitable for use as a material for garments, etc. is known. The layer of a hydrophilic polyurethane resin absorbs moisture from the high-humidity side and releases moisture to the low-humidity side. The layer thus functions to transmit moisture. [0003] The main raw materials for the layer of a hydrophilic polyurethane resin comprise a polyol having high hydrophilicity and an isocyanate compound. In many cases, a two-pack type coating agent composition comprising a combination of an isocyanate-group-containing prepolymer obtained by reacting a polyol having high h...

AI Technical Summary

Benefits of technology

[0012] The invention provides a coating agent composition for forming a substantially non-porous polyurethane resin coating film or film which has moisture permeability, is excellent in mechanical properties such as tensile strength, elongation, and abrasion resistance, has a low degree of swelling with water, has laundering durability, and has such sweat deterioration resistance that it neither swells nor deteriorates with sweat components, and which retains excellent yellowing resistance over a long period even when exposed to sunlight or NOx and contains no organotin compounds.

[0012] The invention provides a coating agent composition for forming a substantially non-porous polyurethane resin coating film or film which has moisture permeability, is excellent in mechanical properties such as tensile strength, elongation, and abrasion resistance, has a low degree of swelling with water, has laundering durability, and has such sweat deterioration resistance that it neither swells nor deteriorates with sweat components, and which retains excellent yellowing resistance over a long period even when exposed to sunlight or NOx and contains no organotin compounds.

Problems solved by technology

However, the coating films obtained from the related-art coating agent compositions have a problem that they change in color to yellow by the action of sunlight or NOx because an aromatic polyisocyanate was used as a raw-material isocyanate compound for the isocyanate-group-containing prepolymer, that is, the coating films have poor yellowing resistance (light resistance and NOx resistance).

However, since an aliphatic polyisocyanate brings about a low cohesive force, it is difficult to obtain a coating film which retains laundering durability and resistance to sweat deterioration.