Biodegradable composition, and its preparing method and foamed product

A biodegradable and composite technology, applied in the field of foaming products, can solve the problems of poor expansion ratio and compressive strength, poor resilience of open-cell foam, and achieve good expansion ratio and compressive strength, high mold The effect of degradable grade and high biodegradation rate

Inactive Publication Date: 2007-03-28
李小鲁
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And because the composition forms a large number of open-cell foams in the process of foam molding, the resilience of the open-cell foam is poor, so it is not suitable for the preparation of foamed products or foamed products. Poor expansion ratio and compressive strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biodegradable composition, and its preparing method and foamed product
  • Biodegradable composition, and its preparing method and foamed product
  • Biodegradable composition, and its preparing method and foamed product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This example is used to illustrate the preparation of the biodegradable composition of the present invention.

[0047] (1) 30 parts by weight of starch phosphate monoester (produced by Beijing Quanxing Starch Factory; the number average molecular weight is 200000, and the degree of substitution is 1.0), 56 parts by weight of polylactic acid (ECO-PLA produced by Kaji Company; at 190°C The melt index is 10 grams / 10 minutes), 7 parts by weight sorbitol, 3.5 parts by weight glycerin, 0.8 parts by weight zinc stearate, 0.2 parts by weight calcium stearate, 0.5 parts by weight epoxy soybean oil add in mixer Stir evenly at room temperature. The mixer first mixes at a low speed of 100 rpm for about 7 minutes, and then mixes at a high speed of 200 rpm for 8 minutes;

[0048] (2) The above-mentioned uniformly stirred mixture is sent into a twin-screw extruder, the length-to-diameter ratio of the extruder is L:D=48:1, and the screw diameter is Φ75 mm. Adjust the screw speed to gr...

Embodiment 2

[0051] This example is used to illustrate the preparation of the biodegradable composition of the present invention.

[0052] (1) 70.0 parts by weight of starch sulfate (dry basis weight) (produced by Beijing Quanxing Starch Factory; the number average molecular weight is 150000, and the degree of substitution is 0.5), 20 parts by weight of polylactic acid (2002D produced by Nature Company; at 190 The melt index at ℃ is 20 grams / 10 minutes), 5 parts by weight of sorbitol, and 1 part by weight of glycerin are added in the blender and stirred evenly at room temperature. RPM high-speed mixing for 6 minutes;

[0053] (2) The above-mentioned uniformly stirred mixture is sent into a twin-screw extruder, the length-to-diameter ratio of the extruder is L:D=48:1, and the screw diameter is Φ75 mm. Adjust the screw speed to gradually increase from 100 rpm to 200 rpm, 300 rpm, 400 rpm, 500 rpm, 700 rpm, 900 rpm, and control the temperature of each section separately At 150°C, 165°C, 165...

Embodiment 3

[0056] This embodiment is used to illustrate the preparation of the biodegradable composition of the present invention

[0057] (1) 50.0 parts by weight (dry weight) of starch acetate (produced by Beijing Quanxing Starch Factory; the number average molecular weight is 190000, and the degree of substitution is 1.5), 30 parts by weight of polylactic acid (ECO-PLA produced by Kaji Company; The melt index at 190°C is 5 g / 10 minutes), 7 parts by weight of sorbitol, 10 parts by weight of glycerin, 1 part of zinc stearate, 0.5 parts of calcium stearate, 0.5 parts by weight of Beijing Tin 8831, 0.5 parts by weight Add one part of antioxidant DSTP into the mixer and stir evenly at room temperature. The mixer first mixes at a low speed of 80 rpm for about 5 minutes, and then mixes at a high speed of 15 rpm for 6 minutes;

[0058] (2) The above-mentioned uniformly stirred mixture is sent into a twin-screw extruder, the length-to-diameter ratio of the extruder is L:D=48:1, and the screw d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to biodegradable combination which contains starch that is esterifying starch and / or etherified starch with 0.1-3 degree of substitution, poly lactic acid, polyhydric alcohol, and foaming agent. The foaming series products formed by the combination have good expansion ratio, compressive strength, high biodegradation rate, and mold degrading stage.

Description

technical field [0001] The present invention relates to a starch-containing resin composition and a preparation method thereof, in particular to a biodegradable composition, a preparation method thereof and foamed products containing the composition. Background technique [0002] The development of modern industry, especially the rapid development of petrochemical and plastic industries, especially the extensive use of disposable plastic products, has promoted the development of industrial and agricultural production and greatly enriched people's material life, but also caused serious damage to the human living environment. "white pollution". In recent years, countries around the world have legislated to restrict the production, sale and use of disposable plastic products. Therefore, many countries in the world are studying the use of degradable plastics to gradually replace traditional disposable plastics. [0003] At present, degradable plastics are mainly divided into t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L3/04C08L67/04C08J9/04
Inventor 李小鲁
Owner 李小鲁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com