A cubic zirconia and single crystal technology, applied in the field of producing cubic zirconia single crystals, can solve the problems of components being easily broken down by high voltage, complex harmonic components, poor working stability, etc., and achieve easy automatic control of production and high product yield. , the effect of stable working condition

Inactive Publication Date: 2007-03-07
冯春生
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing method for producing cubic zirconia single crystals is to use an electron tube high-frequency power supply to inductively heat and melt the zirconia raw materials in the water-cooled crucible, and then use the lifting and pulling crystal pulling process to produce cubic zirconia single crystals. The power efficiency of this production method is low. It can only reach about 40%, the working frequency is 300KHZ-1000KHZ, the harmonic components are complex, the power supply and electronic equipment are greatly disturbed, the working stability is poor, the working voltage is too high, reaching 13KV, the components are easily broken down by high voltage, which is not conducive to Safe production, high production cost, low yield, only 40-45%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The new method for producing cubic zirconia single crystals of the present invention is further illustrated by the following two schemes.

[0027] The method for producing cubic zirconia single crystal in the first embodiment is to use the electric arc furnace power supply as the heating power supply, and the zirconia raw material in the water-cooled crucible is melted by the high-temperature electric arc generated by the electric arc furnace, and then combined with the lifting method to produce cubic zirconia. single crystal method.

[0028] The equipment used in the production method includes: A. AC or DC electric arc furnace heating power supply with a voltage of 10V-200V; B. Water-cooled crucible, which can be made of stainless steel or copper to be round or rectangular; C. Elevator.

[0029] The specific production method is:

[0030] 1. Put the water-cooled crucible on the elevator, and connect the water inlet and outlet pipes;

[0031] 2. Put a 50mm base materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a new manufacturing method of cubic zirconia monocrystal, which comprises the following steps: adopting electric arc furnace power as heating source; or mating electric arc furnace power and middle-frequency power as heating power; fusing zirconium dioxide in the water-cooled copple; combining with lifting crystal pulling technology to obtain the product.

Description

1. Technical field [0001] The present invention relates to a new method for producing single crystals of cubic zirconia. 2. Background technology [0002] Cubic zirconia single crystal, due to its high refractive index and hardness similar to natural diamonds, is widely used in the gem industry to polish and make jewelry. The existing method for producing cubic zirconia single crystals is to use an electron tube high-frequency power supply to inductively heat and melt the zirconia raw materials in the water-cooled crucible, and then use the lifting and pulling crystal pulling process to produce cubic zirconia single crystals. The power efficiency of this production method is low. It can only reach about 40%, the working frequency is 300KHZ-1000KHZ, the harmonic components are complex, the power supply and electronic equipment are greatly disturbed, the working stability is poor, the working voltage is too high, reaching 13KV, the components are easily broken down by high vol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C30B11/00C30B29/16
Inventor 冯春生
Owner 冯春生
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com