Coating for artificial pearl and its production

An artificial pearl and coating technology, applied in jewelry, application, coating and other directions, can solve the problems of unreasonable formula, long drying time and high cost, and achieve the effect of increasing appearance effect, reducing raw material cost and short drying time

Inactive Publication Date: 2007-01-17
QINGDAO MINOA ART CRAFTS +1
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, artificial pearls are generally made by dissolving nitrocellulose with various solvents, and then adding pigments in the solution to coat the resin beads. Most of the pigments in the above ingredients are hydroxides containing lead components. The compound of alkaline salt and alkaline lead carbonate, the use of this compound can make pearls have a good texture and luster, but after people wear it, it will cause harm to the human body and cause pollution to the environment has become a problem that is difficult to solve
[0003] Chinese patent ZL200410024173.3, titled "Paint for artificial pearls and its production method", discloses a paint and production method that does not contain lead. However, due to the large amount of celluloid and unreasonable formula, the viscosity of the paint is relatively high Large, long time for pearl dyeing, thick surface coating, long drying time, high cost, low work efficiency, and low product yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Put 0.8 kg of celluloid fragments and 0.08 kg of camphor into a 20-liter container, add 3 kg of acetone, 7 kg of ethyl acetate, and stir. In the process of continuing to stir, add 7 kg of butyl acetate and amyl acetate. 3 kilograms of esters, stirring in a viscous state, then adding 1.2 kilograms of bismuth oxychloride as the main component of the liquid pigment and stirring until the pigment particles are completely dissolved in the container, and finally a viscous liquid can be obtained, i.e. the first Sub-coat paint.

[0029] Mix celluloid, camphor, ethyl acetate, acetone, butyl acetate and amyl acetate the same as above-mentioned steps, react, but the content of acetone and ethyl acetate that puts in is respectively 2.4 kilograms and 5.6 kilograms, butyl acetate and The content of amyl acetate is 8.4 kilograms and 3.6 kilograms respectively, then add 1.2 kilograms of liquid pigments with bismuth oxychloride as the main component to obtain the second coating.

[003...

Embodiment 2

[0034]The difference between this embodiment and Example 1 is that the content of celluloid in the first coating paint is 0.8 grams, the content of camphor is 0.1 kilograms, acetone is 3.2 kilograms, ethyl acetate is 7.36 kilograms, and butyl acetate is 8.5 kilograms. kg, the content of amyl acetate is 3.66 kg, and the content of pigment is 1.28 kg; the content of celluloid in the second coating paint is 0.8 kg, the content of camphor is 0.11 kg, the content of acetone is 2.25 kg, and the content of ethyl acetate is 0.8 kg. The content is 5.25 kg, the content of butyl acetate is 9.45 kg, the content of amyl acetate is 3.05 kg, and the content of pigment is 3 kg; the content of celluloid in the third coating paint is 0.8 kg, and the content of camphor is 0.12 kg, The content of ethyl acetate was 5.46 kg, the content of butyl acetate was 12.55 kg, and the content of the pigment mainly composed of bismuth oxychloride was 0.27 kg. All the other steps are the same as in Example 1. ...

Embodiment 3

[0036] The difference between this embodiment and Example 1 is that the content of celluloid in the first coating paint is 0.9 kg, the content of camphor is 0.07 kg, acetone is 3.15 kg, ethyl acetate is 7.35 kg, and butyl acetate is 6.93 kg , amyl acetate is 2.97 kg, the content of the pigment with bismuth oxychloride as the main component is 0.6 kg; the content of celluloid in the second coating paint is 0.8 kg, the content of camphor is 0.1 kg, acetone and ethyl acetate The contents of butyl acetate and amyl acetate are 2.4 kg and 5.6 kg respectively, and the contents of butyl acetate and amyl acetate are 8.4 kg and 3.6 kg respectively, and then add 1.2 kg of liquid pigment mainly composed of bismuth oxychloride, without the need for the third coating , Just use the first coating material and the second coating material to repeatedly coat the ball to obtain the artificial pearl with the same effect as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Paint for artificial pearl and its production are disclosed. The paint consists of celluloid 1.5-6wt%, camphor 0.1-0.6wt%, fat solvent 86-95wt% and pigment 1-8wt%, and fat solvent comprises mixture of methyl acetyl or acetic ether and mixture of butyrin acetate and / or banana oil or acetic ether and butyrin acetate. It is cheap, non-toxic and harmless, has short dyeing and drying time and higher production efficiency.

Description

technical field [0001] The invention belongs to the technical field of coating for shaped products of polymer substances, and in particular relates to a surface coating for artificial pearls. Background technique [0002] With the development of modern technology and the improvement of people's living standards, the decorations worn by people are also constantly changing. Among them, artificial pearls that can reflect the quality of natural pearls and can be mass-produced are used in jewelry, rings, collar pins, toys and other fields. more and more widely. In the prior art, artificial pearls are generally made by dissolving nitrocellulose with various solvents, and then adding pigments in the solution to coat the resin beads. Most of the pigments in the above ingredients are hydroxides containing lead components. The compound of alkaline salt and alkaline lead carbonate, the use of this compound can make the pearl have a good texture and luster, but after people wear it, it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D101/18A44C27/00
CPCC09D101/18
Inventor 李永南李相玟
Owner QINGDAO MINOA ART CRAFTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com