High oil absorption resin based on rubber and its preparation method

A high oil-absorbing resin and rubber technology, which is applied in the field of high oil-absorbing resin and its preparation, can solve the problems of poor oil absorption reversibility, low oil absorption ratio, and slow oil absorption rate, and achieve high oil absorption ratio, fast oil absorption speed, and reduced steric hindrance Effect

Inactive Publication Date: 2010-05-12
DONGHUA UNIV
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing oil-absorbing materials generally have problems such as poor oil retention, high price, poor reversibility of oil absorption, low oil absorption ratio, and slow oil absorption rate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High oil absorption resin based on rubber and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Before the reaction, 80 parts of EPDM was dissolved in 60 parts of toluene. In a four-necked round bottom flask equipped with a stirrer, a condenser, a thermometer and an inert gas inlet tube, 0.05 parts of gelatin, tricalcium phosphate, and 0.025 parts of dodecyl were added. Sodium sulfate, 180 parts of deionized water, under the protection of nitrogen, heat up to 30°C in an oil bath, and after 20 minutes of constant temperature, dissolve EPDM with toluene, 20 parts of 4-tert-butylstyrene, and 0.01 parts of divinylbenzene , 0.05 part of benzoyl peroxide was added to a four-necked flask, first stirred at 400rpm and then at 350rpm under the protection of nitrogen, and reacted at 70℃ for 6 hours. After the reaction is complete, it is heated to 80℃ for maturation 1 Hours, filtered, washed with hydrochloric acid solution and deionized water for three times, and dried in vacuum to obtain the resin. The particle size was determined to be 0.5-1mm; the oil absorption ratio of the...

Embodiment 2

[0031] Before the reaction, 90 parts of polybutadiene rubber was dissolved in 360 parts of xylene. In a four-necked round bottom flask equipped with a stirrer, a condenser, a thermometer and an inert gas inlet tube, 0.1 part of gelatin, tricalcium phosphate, and 0.05 were added. Parts of sodium lauryl sulfate, 1500 parts of deionized water, under the protection of nitrogen, heat up to 40°C in an oil bath, after 30 minutes of constant temperature, dissolve xylene in polybutadiene rubber, 10 parts of 4-tert-butyl Styrene, 3 parts of divinylbenzene, 0.05 part of benzoyl peroxide were added to a four-necked flask, and stirred at 380 rpm and then at 360 rpm under the protection of nitrogen, and reacted at 70°C for 8 hours, and so on. After completion, it was heated to 80°C for 1 hour, filtered, washed three times with hydrochloric acid solution and deionized water, and dried in vacuum to obtain the resin. The particle size was determined to be 0.5-1mm; Oil absorption rate * as follo...

Embodiment 3

[0039] Before the reaction, dissolve 50 parts of polyisobutylene in 200 parts of cyclohexane, add 0.08 parts of methyl cellulose and 0.03 parts to a four-necked round bottom flask equipped with a stirrer, condenser, thermometer, and inert gas inlet tube Calcium dodecylbenzene sulfonate, 1000 parts of deionized water, under the protection of nitrogen, heat up to 35℃ in an oil bath, hold the temperature for 25 minutes, dissolve the polyisobutylene in cyclohexane, and 50 parts of 4-tert-butyl Styrene, 2 parts divinylbenzene, 2 parts benzoyl peroxide were added to a four-necked flask, and stirred at 380 rpm and then at 360 rpm under nitrogen protection, and reacted at 70°C for 7 hours, etc. After the reaction is completed, the temperature is raised to 80° C. and matured for 1 hour, filtered, washed with hydrochloric acid solution and deionized water three times, and dried in vacuum to obtain the resin. The particle size is 0.5-2mm after measurement. The oil absorption ratio of this...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A rubber-based resin with high oil absorptivity is proportionally prepared from rubber, alkylstyrene, cross-linking agent, disperser, co-disperser, free radical polymerization trigger, dispersing medium and solvent through adding dispersing medium, disperser and co-disperser into flask, heating to 30-40 deg.C by oil bath under protection of inertial gas, keeping the temp for 20-30 min, adding others in 4-opening flask, variable-speed stirring, reacting, ageing, filtering, washing and vacuum drying.

Description

Technical field [0001] The invention relates to a high oil-absorbing resin and a preparation method thereof, in particular to a rubber-based high oil-absorbing resin and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of offshore oil exploration and development, the pollution of oceans, rivers, lakes, and groundwater caused by oil tankers, oil tanks, oilfield leaks, oil pipeline accidents, and the discharge of oily wastewater and waste liquids has become increasingly serious. Causes extremely bad effects on human life, the ecological environment and economic development. Since oil pollution is extremely destructive to the ecology and the environment, it is forcing humans to urgently need to develop a large number of excellent oil-absorbing materials whose de-oiling effect can change over time and oil. Product, oil pollution level, location and weather conditions. [0003] Super oil-absorbing resin is a new type of functional ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F255/02C08F255/10C08F279/02C08F4/28C08F4/04C08F2/44
Inventor 吴波周美华鲁丹
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com