Environmental friendly lead-free solder and its preparation method

A lead-free solder, environment-friendly technology, applied in the direction of welding equipment, welding/cutting medium/material, welding medium, etc., can solve the problems of poor welding quality, excessive welding slag, and many bridging defects, so as to improve the welding quality , The surface of the solder joint is bright, and the effect of avoiding lead poisoning

Inactive Publication Date: 2006-07-12
THOUSAND ISLAND METAL FOIL
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the existing lead-free solder is soldered at high temperature, there are often too much solder slag, more bridging defects, and poor soldering quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be described in further detail below in conjunction with specific examples, but the content of the present invention is not limited to the examples.

[0017] Element

1#

2#

3#

4#

5#

6#

Ag

2

2

5

5

2.3

3.6

Cu

0.1

0.1

2

2

0.16

1

Ce

0.001

0.001

0.1

0.1

0.07

0.09

Ni

0.001

0.001

0.5

0.5

0.05

0.15

sn

97.898

97.898

92.4

92.4

97.42

95.16

[0018] Performance of this product

[0019] Adding a certain amount of cerium and phosphorus solder alloy to tin-silver-copper will greatly improve the physical properties, mechanical properties, wettability and structure of solder joints.

[0020] 1. Its conductivity and resistivity are lower than 63Sn-37Pb eutectic alloy.

[0021] 2. The melting temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to welding material, especially providing a high-temperature resistance oxidation environment-friendly leadless solder and relative preparation method. said leadless solder comprises following elements in weight percents: 2-5% AG, 0.1-2% Cu, 0.001-0.1% Ce, 0.001-0.5% Ni and Sn. Compared to present technique, the invention is environment-friendly, which can effectively avoid lead poisoning of operator and when the solder is welded in high temperature (380-500Deg. C), it has minute oxidation sludge. The invention has high-temperature resistance oxidation ability which can keep the surface of tin furnace bright without oxidation in this temperature, and the welded tin furnace can last non-oxidation condition for longer time. The invention has less welding defects compared to common Sn-Ag-Cu system, bright surface of welding point and improved welding quality.

Description

technical field [0001] The invention relates to soldering materials, in particular to a high-temperature oxidation-resistant, environment-friendly lead-free solder and a preparation method thereof. Background technique [0002] The soldering materials in the electronics industry are mainly tin-lead alloys. Although tin-lead alloys have excellent soldering performance, lead is a toxic substance. After entering the human body, it accumulates in the bones and is not easily discharged, causing lead poisoning of operators. Lead-free is the development trend of brazing technology in the microelectronics assembly industry at home and abroad. However, when the existing lead-free solder is soldered at high temperature, there are often too much solder slag, more bridging defects, and poor soldering quality Contents of the invention [0003] The object of the present invention is to provide an environment-friendly high-temperature anti-oxidation lead-free solder and a preparation me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/26C22C1/03
Inventor 黄守友
Owner THOUSAND ISLAND METAL FOIL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com