Silicon-barium-strontium-calcium-magnesium-iron alloy as deoxidant in steelmaking

A technology of ferroalloy and deoxidizer, which is applied in the field of ferroalloy, silicon barium strontium calcium magnesium iron alloy, can solve the problems of affecting steel quality, insufficient desulfurization ability of silicon barium alloy, high price, etc., and achieve the effect of preventing splashing and hurting people

Inactive Publication Date: 2003-11-19
本溪冶炼厂
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has gradually developed from single deoxidation with aluminum to binary, ternary and multi-component composite deoxidized alloys, but these products can only play a role in deoxidation, and the price is relatively high. Phosphorus, which affects the quality of steel
[0003] Silicon-barium alloy is well known as a deoxidizer, although it has a fairly good deoxidation ability, it still cannot meet the further requirements for the oxygen content of molten steel
In addition, the desulfurization ability of existing silicon-barium alloys is obviously insufficient
At present, the published Chinese invention patent application No. 99109706.8 provides that the silicon-barium-magnesium-iron alloy used as a deoxidizer for steelmaking contains 2 to 8% aluminum, which requires aluminum-free steel types and acid-melted aluminum in steel for smelting. It is unfavorable for steel grades with very low content and strict

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Adopt the preparation method that the present invention provides, the chemical composition (weight %) of the silicon barium strontium calcium magnesium iron alloy of smelting output is: Si 45.6%, Ba 25.3%, Sr 5.6%, Ca 6.1%, Mg 6.8%, balance For Fe.

Embodiment 2

[0020] Adopt the preparation method that the present invention provides, the chemical composition (weight %) of the silicon barium strontium calcium magnesium iron alloy of smelting output is: Si 47.2%, Ba 22.6%, Sr 6.1%, Ca 8.3%, Mg 10.5%, balance For Fe.

[0021] Above embodiment all obtains better technical and economic effect through a certain steel mill trial.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A SiBaSrCaMgFe alloy used as deoxidant in smelting steel contains Si (40-60 wt.%), Ba (10-28), Sr (1-8), Ca (1-15), Mg (5-20) and Fe (rest). Its advantages are high deoxidizing power, sure desulfurizing effect and low cost.

Description

technical field [0001] The invention relates to a ferroalloy used as a steelmaking deoxidizer, in particular to a silicon-barium-strontium-calcium-magnesium-iron alloy used as a steelmaking deoxidizer, which is a supplement to existing ferroalloy varieties and belongs to the technical field of steelmaking. Background technique [0002] In recent years, the deoxidizers used for making killed steel have developed rapidly and have good effects. It has gradually developed from single deoxidation with aluminum to binary, ternary and multi-component composite deoxidized alloys, but these products can only play a role in deoxidation, and the price is high. In addition, although the molten steel for steelmaking still has a certain amount of sulfur, Phosphorus, thus affecting the quality of steel. [0003] Silicon-barium alloy is known as a deoxidizer, although it has a fairly good deoxidation ability, it still cannot meet the further requirements for the oxygen content of molten st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C7/06
Inventor 姜殿波
Owner 本溪冶炼厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products