Pollution-free pine timber modifying method and composition

A wood modification and non-polluting technology, applied in wood treatment, wood processing equipment, wood treatment details, etc., to achieve the effects of ecological forest protection, suppression of deforestation of resource forests, mildew and moth resistance

Inactive Publication Date: 2003-02-26
陈万利 +2
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has been found that a neutral composition containing water-soluble nitrogen-containing organic compounds, inorganic magnesium salts, boric acid, a small amount of emulsifier and penetrant is used to degrease and solidify pine wood. Non-toxic, low-viscosity polymer resin for degreasing, that is, after removing the flowable turpentine in the pine wood and fixing the rosin, re-inject a curable water-soluble resin, so that the treated pine wood can not only solve the problem of grease deformation, The strength and durability are also improved, and the wood has flame retardancy, which meets the flame retardancy requirements of fire protection for interior decoration materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1 The embodiment of deoiling and solidifying process of pine wood.

[0016] Composition (wt%): n-butylamine: 0.8%, magnesium sulfate: 0.5%, boric acid: 1%, sodium dodecylbenzenesulfonate: 0.1%, OK oil: 0.1%, phosphoric acid: 0.3%, water 97.2 %. Processing temperature: 95°C. Processing time: 4 hours.

Embodiment 2

[0017] Example 2 Example of deoiling and solidifying process of pine wood.

[0018] Composition (wt%): laurylamine: 0.5%, magnesium sulfate: 0.8%, boric acid: 1%, sodium lauryl sulfate: 0.2%, OK oil: 0.08%, phosphoric acid: 0.15%, water 97.3%. Processing temperature: 80°C. Processing time: 10 hours.

Embodiment 3

[0019] Example 3 Example of deoiling and solidifying process of pine wood.

[0020] Composition (wt%): 1,6 hexamethylenediamine: 1%, magnesium chloride: 0.7%, boric acid: 0.5%, sodium dodecylbenzenesulfonate: 0.5%, OK oil: 0.05%, phosphoric acid: 0.7%, Water 96.6%. Processing temperature: 105°C. Processing time: 6 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A pine timber modification method is to eliminate its turpentine oil, fix its rosin and inject water-soluble resin capable of being cured. After deoiling and rosin fixing at 80-105 deg.C and under normal pressure for 3-10 hr, the pine timber is vacuum pumped for 0.5-1 hr, made to suck water-soluble fireproof polymer resin under 0.09-0.095 MPa vacuum and soaked for 1-5 hr under normal pressure. The deoiling and rosin fixing composition contains water-soluble nitogen-contained organic compound, magnesium, salt, boric acid, emulsifier, penetrant, and has pH value of 7.5-8.0. The pint timber thus processed has no rosin overflow and deformation, high strength and durability, and certain fireproof performance.

Description

technical field [0001] The invention relates to the modification of wood, especially the pollution-free modification method of pine wood, and also relates to the composition for modifying pine wood. Background technique [0002] Pine has the characteristics of fast growth and strong adaptability. It is a temperate tree species widely planted as economic forests in many forest farms and as income-generating forests in front of and behind houses in rural areas. However, due to the well-developed resin channels in the pine wood structure, the high content of turpentine, and the large deformation of the wood, it is easy to pollute the surface of the material with grease when the temperature is high, and can cause the paint layer to peel off, so the application is limited, usually only for building studs and Templates, packing box material use. [0003] In order to expand the utilization of pine wood resources, North America began to study the processing methods of pine wood in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K5/00
Inventor 陈万利吴子良
Owner 陈万利
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com