Battery sheath made of formed cold-rolled metal sheet and method for producing battery sheaths
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A metal plate and battery technology, which is applied in the direction of battery box/cover, battery box/cover material, battery pack parts, etc., can solve the problems of expensive and complicated methods
Inactive Publication Date: 2004-10-13
HILLE & MUELLER
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The method is complex and therefore expensive
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0043] Example 1
[0044] After degreasing, cleaning, pickling and cleaning, nickel-plate the 0.2-0.45mm thick strip in the nickel bath as follows:
[0045] Nickel bath composition:
[0046] Nickel 60g / l (nickel sulfate)
[0047] Chloride 30g / l (nickel chloride)
[0048] Boric acid 40g / l
[0049] Graphite 40g / l, particle size 1-8μm
[0050] pH 2.3
[0051] Temperature 60°C
[0052] Current density 15A / dm 2
[0053] stirring turbulence
[0054] Electrolyte flow 6-10m / s
[0055] The prepared coating contained about 1.7% graphite.
[0056] Example 2
[0057] The nickel bath composition corresponds to that given in Example 1. However, suspension stabilizers and aggregation preventing substances are added. Stir more gently; electrolyte flow is only about 4m / s. The graphite content in the deposited nickel layer was 9.0%.
[0058] The layer structures prepared according to Examples 1 and 2 had the following composition:
[0059] The total thickness of the layers produ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
thickness
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
A battery sheath made of formed and cold-rolled sheet metal as well as a process for manufacturing the battery sheath are proposed. In the process, cold-rolled strip stock is provided on at least one side with a coating of Ni, Co, Fe, Sn, In, Pd, Bi or their alloys in an electroplating bath, e.g., a Watts-type bath. As an additional component, the electroplating bath contains electrically conductive particles such as carbon, carbon black, graphite, TiS2, TaS2, MoSi2. These particles are deposited on the base material during electroplating together with Ni, Co, Fe, Sn, In, Pd, Bi or their alloys. The sheet metal side with, for example, the carbon-containing electroplated coating faces preferably inwardly when the sheet is formed into a battery sheath. Batteries with battery sheaths produced in this manner exhibit reduced increase in internal resistance, even with prolonged storage, as compared to known batteries.
Description
technical field [0001] The invention relates primarily to battery casings made of formed cold-rolled sheet metal, at least internally provided with a coating comprising Ni, Co, Fe, Sn, In, Pd, Bi and / or their alloys produced by electroplating. Background technique [0002] The invention also relates to a method for the production of strip material for battery bushings, in which cold-rolled metal sheets are provided with a coating formed in an electroplating bath. [0003] The quality of the battery depends especially on how long the rated voltage and capacity of the warranty can be maintained. The higher the internal resistance of the battery, the lower the battery voltage in the charged state. A more important property of battery quality is performance during long-term storage. Long-term storage causes the internal resistance of the battery to increase. The internal resistance and its increase during long-term storage depend on several factors: During the preparation of ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.