Environment-friendly rubber reinforcing agent and preparation method thereof

A rubber reinforcing agent and an environment-friendly technology, which is applied in the field of environment-friendly rubber reinforcing agent and its preparation, can solve the problems of long process flow, unfavorable industrial production, and strong pertinence, so as to reduce environmental pollution and benefit the environment The effect of protecting and reducing production costs

Pending Publication Date: 2022-08-09
SHENYANG JIANZHU UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Prior art CN109134932A discloses a preparation method of modified fly ash, but the formula is complex, the process flow is long, and there are special requirements for equipment and stirring, which is not conducive to industrial production
Prior art CN109370230A discloses a preparation method of modified silica, which is modified by using a traditional coupling agent. The modified silica has a general reinforcing effect and needs to be used in conjunction with graphene and chopped carbon fibers, and Can only be used in silicone rubber system, highly targeted, not universal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1 Preparation of environmentally friendly rubber reinforcing agent

[0034] Proceed as follows:

[0035] (1) Preparation of raw materials: the recovered paint slag, remove the impurities visible to the naked eye, and stand by;

[0036] (2) High temperature pyrolysis: Mix the paint slag with fly ash removed from mechanical impurities in a ratio of 50:50, then send it to a high temperature furnace and heat it to 800°C, maintain it for 2 hours and then naturally cool down.

[0037] (3) ball milling and sieving: 100 parts of step (2) products obtained therefrom are mixed with 10 parts of white carbon black and 1 part of graphene at high speed, after mixing, ball milled by a ball mill for 3 hours, finally crossed a 500 mesh sieve to obtain a kind of black solid powder. The black solid powder is an environmentally friendly rubber reinforcing agent.

Embodiment 2

[0038] Example 2 Preparation of environmentally friendly rubber reinforcing agent

[0039] Proceed as follows:

[0040] (1) Preparation of raw materials: the recovered paint slag, remove the impurities visible to the naked eye, and stand by;

[0041] (2) High-temperature pyrolysis: Mix 100 parts of paint slag with mechanical impurities removed with 50 parts of fly ash, then send it to a high-temperature furnace and heat it to 800°C, maintain it for 2 hours, and then naturally cool down.

[0042] (3) ball milling and sieving: the product obtained in step (2) is mixed at high speed with 15 parts of white carbon black and 2 parts of graphene, and after mixing, it is ball-milled by a ball mill for 4 hours, and finally crosses a 500-mesh sieve to obtain a black solid powder. The black solid powder is an environmentally friendly rubber reinforcing agent.

Embodiment 3

[0043] Example 3 Preparation of environmentally friendly rubber reinforcing agent

[0044] Proceed as follows:

[0045] (1) Preparation of raw materials: the recovered paint slag, remove the impurities visible to the naked eye, and stand by;

[0046] (2) High-temperature pyrolysis: Mix 50 parts of paint slag with mechanical impurities removed with 100 parts of fly ash, then send it to a high-temperature furnace and heat it to 800°C, maintain it for 2 hours, and then naturally cool down.

[0047] (3) ball milling and sieving: the product obtained in step (2) is mixed at high speed with 20 parts of white carbon black and 3 parts of graphene, and after mixing, it is ball-milled by a ball mill for 2 hours, and finally crosses a 500-mesh sieve to obtain a black solid powder. The black solid powder is an environmentally friendly rubber reinforcing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly rubber reinforcing agent and a preparation method thereof.The preparation method comprises the steps that recycled waste paint slag is subjected to mechanical impurity removal and then mixed with fly ash according to a certain proportion, then the mixture is fed into a high-temperature furnace to be heated to the temperature not lower than 800 DEG C, the temperature is maintained for not less than 2 hours, and then natural cooling is conducted; and cooling to room temperature, taking out, mixing with a proper amount of white carbon black and graphene at a high speed, ball-milling for 2-4 hours by a ball mill after mixing, and finally sieving by a 500-mesh sieve to obtain black solid powder. The solid powder has a certain reinforcing effect on rubber and can be used as a reinforcing agent. The method has the advantages that the paint slag is well recycled, the recycling process is environment-friendly, simple and feasible, the production cost is reduced, the method has a good development prospect, and an economic and effective method is provided for recycling the paint slag.

Description

technical field [0001] The invention relates to an environment-friendly rubber reinforcing agent and a preparation method thereof, belonging to the technical field of powder filling reinforcing agent. Background technique [0002] For general synthetic rubber and natural rubber, its tensile strength and tensile stress are very low, and it is difficult to manufacture products with use value. Therefore, reinforcement is required, and reinforcement is a function of significantly improving the tensile strength, tear strength, abrasion, etc. of the rubber at the same time. Commonly used reinforcing agents are carbon black, silica and reinforcing resins. Among them, carbon black is the most commonly used because of its low price. However, the production of carbon black will bring serious environmental pollution problems, and efforts should be made to reduce the use of carbon black. [0003] CN109134932A, Modified fly ash for reinforcing rubber products and preparation method th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K9/10C08K11/00C08K7/26C08K3/04C08L7/00
CPCC08K9/10C08K11/005C08K7/26C08K3/042C08K3/04C08L7/00C08K2201/014Y02W30/91
Inventor 刘运学范兆荣谷金谷亚新王晴于云武万晔
Owner SHENYANG JIANZHU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products