Wear-resistant water-based resin for special labor protective gloves and preparation method of wear-resistant water-based resin

A technology of water-based resin and protective gloves, applied in gloves, protective clothing, applications, etc., can solve the problems of large influence on emulsion performance, difficulty in controlling, low raw rubber strength, etc., and achieve low tensile strength and good fluidity , good adhesion effect

Pending Publication Date: 2022-05-27
江苏昌华化工有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are few institutions in China that specialize in the research and application of nitrile synthesis technology and application in the field of special labor protection gloves. The mainstream nitrile latex synthesis method adopts the low temperature method, which takes a long time, low efficiency, high consumption, and low raw rubber strength. It also needs to be vulcanized for a long time to be useful, but the vulcanization time has a great impact on the performance of the emulsion and is not easy to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A method for preparing a wear-resistant water-based resin for special labor protection gloves, in terms of mass percentage, the specific steps are as follows:

[0033] (1) First add 40% of the formula amount of soft water, 55% of the formula amount of pH adjuster, 45% of the formula amount of dispersant, 6% of the formula amount of mixed monomer, 25% of the formula amount of compound emulsifier, and 15% of the formula amount. amount of initiator, evacuated, heated to 48°C, and incubated for 30 minutes;

[0034] (2) Slowly add 75% of the mass of the remaining formula raw materials at a constant speed, the feeding time is 4 hours, keep stirring until the monomer conversion rate reaches 50%, heat up to 55 ° C, and slowly add 25% of the mass of the remaining formula raw materials at a constant speed, feeding time For 1.5 hours, keep stirring until the monomer conversion rate reaches more than 90%, add antifoaming agent and stabilizer that are 0.1% and 0.2% of the total weig...

Embodiment 2

[0041] A method for preparing a wear-resistant water-based resin for special labor protection gloves, in terms of mass percentage, the specific steps are as follows:

[0042] (1) First add 60% of the formula amount of soft water, 65% of the formula amount of pH adjuster, 50% of the formula amount of dispersant, 20% of the formula amount of mixed monomer, 35% of the formula amount of compound emulsifier, 20% of the formula amount amount of initiator, evacuated, heated to 50°C, and incubated for 60 minutes;

[0043] (2) Slowly add 75% of the mass of the remaining formula raw materials at a constant speed, the feeding time is 5 hours, keep stirring until the monomer conversion rate reaches 50%, heat up to 65 ° C, and slowly add 25% of the mass of the remaining formula raw materials at a constant speed, feeding time For 2 hours, keep stirring until the monomer conversion rate reaches more than 90%, add defoamer and stabilizer respectively 0.2% and 0.4% of the total weight of the m...

Embodiment 3

[0050] A method for preparing a wear-resistant water-based resin for special labor protection gloves, in terms of mass percentage, the specific steps are as follows:

[0051] (1) First add 50% of the formula amount of soft water, 60% of the formula amount of pH adjuster, 48% of the formula amount of dispersant, 15% of the formula amount of mixed monomer, 30% of the formula amount of compound emulsifier, 18% of the formula amount amount of initiator, evacuated, heated to 49°C, and incubated for 45 minutes;

[0052] (2) Slowly add 75% of the mass of the remaining formula raw materials at a constant speed, the feeding time is 4.5 hours, keep stirring until the monomer conversion rate reaches 50%, heat up to 60 ° C, and slowly add 25% of the mass of the remaining formula raw materials at a uniform speed, feeding time For 2 hours, keep stirring until the monomer conversion rate reaches more than 90%, add defoamer and stabilizer respectively 0.15% and 0.3% of the total weight of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses wear-resistant water-based resin for special labor protection gloves and a preparation method of the wear-resistant water-based resin. The preparation method comprises the following steps: firstly, adding a part of soft water, a pH value regulator, a dispersing agent, a mixed monomer, a compound emulsifier and an initiator into a polymerization kettle, vacuumizing, and heating for reaction; then slowly adding a part of residual formula raw materials at a constant speed, carrying out heat preservation reaction, then heating, slowly adding the residual formula raw materials at a constant speed, carrying out heat preservation stirring until the monomer conversion rate reaches 90% or above, adding a defoaming agent and a stabilizing agent, eliminating residual monomers, cooling, adjusting the pH value, and filtering. The water-based resin obtained by the invention can be used for special labor protection gloves, and has good wear resistance and relatively high tensile strength and elongation.

Description

technical field [0001] The invention relates to a water-based resin, in particular to a wear-resistant water-based resin for special labor protection gloves and a preparation method thereof. It belongs to the technical field of glove processing. Background technique [0002] With more and more attention paid to safety in production, it has become particularly important to wear high-quality labor protection products to prevent accidents. The hand is a part of the human body with a high injury rate, so it is particularly important to choose and correctly use safety gloves to prevent hand injuries. From food preparation to medical to industrial production, rubber labor protection gloves have a wide range of uses. [0003] There are many rubbers used for special labor protection gloves, but from an economic point of view, most of them use styrene-butadiene latex with simple, easy-to-obtain and low-cost raw materials. The traditional protective gloves made of styrene-butadiene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F236/12C08F220/46C08F220/06C08F220/56C08F210/14C08F222/02C08F220/58C08F2/44C08L13/02C08L77/10C08K3/14C08K3/30C08J5/02A41D19/015
CPCC08L13/02C08F236/12C08J5/02A41D19/0062C08K2201/011C08K2003/3009C08J2313/02C08J2477/10C08L2205/16C08L77/10C08K3/14C08K3/30C08F220/46C08F220/06C08F220/56C08F210/14C08F222/02C08F220/58C08F2/44
Inventor 刘江程昌华张荣新丁子豪
Owner 江苏昌华化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com