Electrode and manufacturing method thereof, electrode element, and non-aqueous electrolyte electricity storage element

An electrode and liquid material technology, applied in non-aqueous electrolyte batteries, non-aqueous electrolyte battery electrodes, non-aqueous electrolytes, etc., can solve problems such as difficult short-circuits, and achieve the effect of suppressing thermal runaway reactions

Pending Publication Date: 2022-05-13
RICOH KK
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is extremely difficult to completely prevent self-shorting by simply providing a separator or porous layer that physically separates the electrodes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrode and manufacturing method thereof, electrode element, and non-aqueous electrolyte electricity storage element
  • Electrode and manufacturing method thereof, electrode element, and non-aqueous electrolyte electricity storage element
  • Electrode and manufacturing method thereof, electrode element, and non-aqueous electrolyte electricity storage element

Examples

Experimental program
Comparison scheme
Effect test

no. 1 approach

[0036] figure 1 A cross-sectional view for explaining the negative electrode used in the non-aqueous electrolyte storage element according to the first embodiment. refer to figure 1 The negative electrode 10 is configured to include a negative electrode substrate 11 , a negative electrode mixture layer 12 formed on the negative electrode substrate 11 , and a porous insulating layer 13 formed on the negative electrode mixture layer 12 . The shape of the negative electrode 10 is not particularly specified and may be appropriately selected according to purposes; for example, the shape of the negative electrode 10 may be a flat plate or the like.

[0037] In the negative electrode 10 , at least a part of the porous insulating layer 13 exists inside the negative electrode mixture layer 12 and is integrated (integrated) with the surface of the active material constituting the negative electrode mixture layer 12 . Note that "integrated with the surface" in this case is not a membra...

Embodiment 1

[0128] The negative electrode 10, the positive electrode 20, the electrode element 40, and the nonaqueous electrolyte power storage element 1 were prepared as follows.

[0129] ink preparation

[0130] As the ink for forming the insulating layer, the following solutions were prepared:

[0131] - Tricyclodecane dimethanol diacrylate (Daicel-Ornix Corporation): 49 parts by mass

[0132] - Dipropylene glycol monomethyl ether (manufactured by Kanto Chemical Co., Ltd.): 50 parts by mass

[0133] - Irgacure 184 (manufactured by BASF): 1 part by mass

[0134] Preparation of Negative Electrode 10

[0135] 97 parts by mass of graphite particles (average particle size: 10 μm) as a negative active material, 1 part by mass of cellulose as a thickener, and 2 parts by mass of acrylic resin as a binder were uniformly dispersed in water to prepare a negative active material Dispersions. The dispersion was applied to a copper foil having a thickness of 8 μm as the negative electrode subst...

Embodiment 2

[0159] ink preparation

[0160] As the ink for forming the insulating layer, the following solutions were prepared:

[0161] - Tricyclodecane dimethanol diacrylate (Daicel-Ornix Corporation): 29 parts by mass

[0162] - Dipropylene glycol monomethyl ether (manufactured by Kanto Chemical Co., Ltd.): 70 parts by mass

[0163] - Irgacure 184 (manufactured by BASF): 1 part by mass

[0164] After preparing the ink, a nonaqueous electrolyte power storage element 1 was prepared in the same manner as described in Example 1.

[0165] As a result of the SEM observation, it was found that the insulating layers 13A and 23A obtained in Example 2 were observed to have pores having a size of about 0.1-1.0 μm. That is, the results of SEM observation indicated that the prepared insulating layers 13A and 23A were porous insulating layers.

[0166] Next, a viscosity measurement test and an impedance measurement test were performed in the same manner as in Example 1 on the ink for forming an ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an electrode, a manufacturing method, an electrode element and a non-aqueous electrolyte power storage element. The electrode comprises an electrode substrate; an electrode mixture layer formed on the electrode substrate and including an active material; and a porous insulating layer formed on the electrode mixture layer, in which the porous insulating layer contains a resin as a main component, and at least a portion of the porous insulating layer is present inside the electrode mixture layer.

Description

[0001] This application is a divisional application of the invention patent application with the Chinese application number 201880080855.6, the application date is December 14, 2018, and the invention title is "electrodes and manufacturing methods, electrode components and non-aqueous electrolyte storage components". technical field [0002] The disclosure discussed herein relates to electrodes and methods of making the same, electrode elements, and nonaqueous electrolyte power storage elements. Background technique [0003] In power storage elements such as batteries and power generation elements such as fuel cells, there is an increasing demand for higher power, higher capacity, and longer life. However, various safety-related issues still exist for element implementation; in particular, preventing thermal runaway reactions caused by short circuits between electrodes is an important issue. [0004] The occurrence of the thermal runaway reaction is considered to be caused b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/02H01M4/04
CPCH01M4/02H01M4/04H01M2004/021H01M4/0404H01M4/366H01M4/483H01M4/583H01M4/604H01M4/622H01M10/0525H01M10/0565H01M4/13H01M4/139H01M4/628H01M50/461Y02E60/10H01G11/06H01G11/26H01G11/86H01M4/62H01M10/052H01M10/0585H01M10/4235H01M50/46H01G11/52H01G11/58
Inventor 鹰氏启吾柳田英雄升泽正弘座间优木村兴利川瀬广光大木本美玖
Owner RICOH KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com