Electrochemical sensor for detecting dopamine in gastric juice as well as preparation method and application of electrochemical sensor
A dopamine and sensor technology, applied in the field of electrochemical sensors and preparations for the detection of dopamine in gastric juice, can solve the problems of high sensor performance and stability requirements, achieve excellent reproducibility and stability, low detection limit, and overcome stability poor sex effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] (1) Nb 2 Preparation of C-MXene
[0045] Add Nb to 40% HF solution 2 AlC powder was reacted for 24 h under 25°C with 700 r / min magnetic stirring to obtain corrosion products; the corrosion products were continuously washed with deionized water until the pH of the supernatant was 7; washed with absolute ethanol for 5 After drying the product in a vacuum oven at 60°C for 12 h, the Nb 2 C matrix material.
[0046] (2) NS-Nb 2 Preparation of C-MXene
[0047] 100 mg Nb prepared in step (1) 2 C powder was ground and mixed with 300 mg thiourea evenly, then put into an atmosphere furnace and heated to 500°C under an argon atmosphere, kept for 3 h, and then cooled to 25°C with the furnace; the prepared material was ground again, and used The deionized water is continuously washed until the pH of the supernatant is 7; the obtained powder is dried to obtain nitrogen and sulfur co-doped Nb 2 C nano powder NS-Nb 2 C-MXene.
[0048] figure 1 Be the NS-Nb that the embodiment...
Embodiment 2
[0057] (1) Nb 2 Preparation of C-MXene
[0058] Add Nb to 50% HF solution 2 AlC powder was reacted at 20°C with 800 r / min magnetic stirring for 20 h to obtain corrosion products; the corrosion products were continuously washed with deionized water until the pH of the supernatant was 6; washed with absolute ethanol for 7 After the second time, the product was dried in a vacuum oven at 60°C for 10 hours to obtain Nb 2 C matrix material.
[0059] (2) NS-Nb 2 Preparation of C-MXene
[0060] 200 mg Nb prepared in step (1) 2 C powder was ground and mixed with 700 mg thiourea evenly, and then put into an atmosphere furnace and heated to 600°C under an argon atmosphere, kept for 4 h, and then cooled to 20°C with the furnace; the prepared material was ground again, and used Wash with deionized water until the pH of the supernatant is 6; dry the obtained powder to obtain NS-Nb 2 C-MXene.
[0061] (3) NS-Nb 2 Preparation of C-MXene / Nafion Modified Electrode
[0062] The NS-Nb p...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com