Novel negative oxygen ion composite rock plate formula and manufacturing method thereof

A technology of negative oxygen ions and slate, applied to clay products, other household appliances, household appliances, etc., can solve the problems of low environmental quality and inability to produce negative oxygen ions, improve sleep quality, increase body immunity, prevent The effect of myopia

Inactive Publication Date: 2021-09-07
邵珠蕾
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the existing technology, the invention provides a new negative oxygen ion composite rock plate formula and its manufacturing method. The prepared composite plate has the advantages of releasing negative oxygen ions and improving human health, which solves the problem of the current common ceramic tiles. Can not produce negative oxygen ions, the problem of low environmental quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel negative oxygen ion composite rock plate formula and manufacturing method thereof
  • Novel negative oxygen ion composite rock plate formula and manufacturing method thereof
  • Novel negative oxygen ion composite rock plate formula and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A new type of negative oxygen ion composite rock plate formula comprises resin, curing agent, accelerator, granite stone powder, crushed stone particles, inorganic clay, and water.

[0040] Wherein, the curing agent is methyl ethyl ketone, and the curing of the resin is through chemical reactions such as condensation, ring closure, addition or catalysis, so that the thermosetting resin undergoes an irreversible change process, and the curing agent is added to complete the curing, and the curing agent accelerates the curing of the composite board speed, improve product quality and speed up production processes.

[0041] Wherein, the accelerator comprises stannous octoate, zinc isooctanoate and ferric chloride, and the ratio of the stannous octoate, zinc isooctanoate and ferric chloride is 1:1:1, the accelerator and curing According to different types of adhesives, select an effective accelerator; the accelerator and the curing agent must have a good match, and should be ...

Embodiment 2

[0055] A method for manufacturing a novel composite rock plate with negative oxygen ions, comprising the following steps:

[0056] S1. Prepare the following materials in corresponding quantities: 25 parts of resin, 6 parts of curing agent, 9 parts of accelerator, 110 parts of granite stone powder, 90 parts of gravel particles, 70 parts of inorganic clay, and 220 parts of water;

[0057] S2. Mix the granite stone powder and crushed stone particles with the inorganic clay in the corresponding parts by mass, and then add the water in the corresponding parts to fully mix in the mixing cylinder;

[0058] S3, adding resin to the material mixed in S1 and continuing to stir;

[0059] S4, adding curing agent and accelerator into the mixing cylinder at the same time, and continuing to stir for 2.5 hours;

[0060] S5. Pour the mixed material into the mold prepared in advance, and then press it through a press;

[0061] S6, the pressed slate in the mold is put into the temperature of 1200...

Embodiment 3

[0066] A method for manufacturing a novel composite rock plate with negative oxygen ions, comprising the following steps:

[0067] S1. Prepare the following materials in corresponding quantities: 30 parts of resin, 7 parts of curing agent, 10 parts of accelerator, 120 parts of granite stone powder, 100 parts of gravel particles, 80 parts of inorganic clay, and 240 parts of water;

[0068] S2. Mix the granite stone powder and crushed stone particles with the inorganic clay in the corresponding parts by mass, and then add the water in the corresponding parts to fully mix in the mixing cylinder;

[0069] S3, adding resin to the materials mixed in S1 and continuing to stir;

[0070] S4, adding curing agent and accelerator into the mixing cylinder at the same time, and continuing to stir for 2.5 hours;

[0071] S5. Pour the mixed material into the mold prepared in advance, and then press it through a press;

[0072] S6, the pressed slate in the mold is put into the temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of composite rock plate manufacturing, and discloses a novel negative oxygen ion composite rock plate formula and a manufacturing method thereof. The novel composite rock plate formula comprises resin, a curing agent, an accelerant, granite stone powder, gravel particles, inorganic clay and water. The manufacturing method of the novel negative oxygen ion composite rock plate comprises the following steps that S1, granite stone powder, gravel particles and inorganic clay with corresponding mass parts are weighed and fully mixed in a mixing barrel; S2, resin is added into the materials mixed in the step S1, and continuously stirring is conducted; S3, a curing agent and an accelerant are simultaneously added into the mixing barrel, and continuously stirring is conducted; S4, pressing is conducted through a pressing machine; S5, the rock plate pressed in the mold iscalcined at the temperature of 1200 DEG C; S6, the front face of the manufactured finished rock plate is coated with an adhesive, and then a negative ion layer is coated; S7, the back face of the rock plate is coated with ceramic tile back glue; and S8, the novel negative oxygen ion composite plate is manufactured.

Description

technical field [0001] The invention relates to the technical field of composite rock slab manufacturing, in particular to a new negative oxygen ion composite rock slab formula and a manufacturing method thereof. Background technique [0002] Rock slab is a kind of stone sintered, fired at high temperature, and then through the action of pressure, its hardness is improved, which can reach grade 6, and its scratch resistance and wear resistance have also been improved. However, it retains the texture of the board. It is a more practical board. Slate is often used for kitchen countertops, dining table or cooking countertops, and it can also be used for decoration in bathrooms; air negative oxygen ions are The general term for negatively charged single gas molecules and hydrogen ion groups. In natural ecosystems, forests and wetlands are important places for generating air negative (oxygen) ions, which play a regulating role in air purification and urban microclimate. The conce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/24C04B41/89
CPCC04B33/1305C04B33/131C04B33/1315C04B33/24C04B41/89C04B41/52C04B41/009C04B2235/449C04B2235/444
Inventor 邵珠蕾
Owner 邵珠蕾
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products