Method for producing high-cleanliness hot-series variety steel at low cost

A high-cleanliness, low-cost technology, applied in the direction of manufacturing converters, etc., can solve the problem of high production cost of clean steel, shorten the production process, avoid uncontrollable inclusions, and improve efficiency.

Active Publication Date: 2021-08-24
SHOUGANG JINGTANG IRON & STEEL CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the technical problem of high production cost of existing clean steel, the present invention provides a low-cost method for producing high-cleanliness thermal grade steel, which can Reduce the production cost of clean steel and effectively control the content of sulfur and inclusions in clean steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing high-cleanliness hot-series variety steel at low cost
  • Method for producing high-cleanliness hot-series variety steel at low cost

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0092] A low-cost production of high-cleanliness thermal grade steel, which is produced by the following method:

[0093] (1) Desulfurization of molten iron: adding fluorine-free desulfurizer to molten iron for KR desulfurization, the amount of said fluorine-free desulfurizer is 8kg / t molten iron, and then carry out slag removal, the liquid surface exposure rate of molten iron reaches 99.5%, obtain desulfurized molten iron, control the The sulfur content of the desulfurized molten iron is ≤10ppm.

[0094] In terms of mass fraction, the chemical composition of the fluorine-free desulfurizer is:

[0095] CaO: 92%, Al 2 o 3 : 3%, SiO 2 : 1%, MgO: 1%, Al: 3%.

[0096] (2) Converter smelting: The desulfurized molten iron is subjected to converter steelmaking, and auxiliary materials are added during the converter smelting process. The amount of the auxiliary materials is 130-140kg / t molten steel. The content is controlled at 25-45ppm.

[0097] Optionally, in terms of mass fra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for producing high-cleanliness hot-series variety steel at low cost, and belongs to the technical field of steelmaking processes. The method comprises the steps that KR desulfurization is carried out on molten iron to acquire desulfurized molten iron, and the sulfur content of the desulfurized molten iron is controlled to be less than or equal to 10 ppm; the desulfurized molten iron is subjected to converter steelmaking, and the sulfur content at the converter steelmaking end point is controlled to be 25-45 ppm; converter tapping is carried out, a desulfurizing agent is added in the tapping process, and the sulfur content of tapping molten steel is controlled to be less than or equal to 20 ppm; the molten steel is subjected to RH refining to acquire refined molten steel, the calcium content in the refined molten steel is controlled to be 8-12 ppm, the oxygen content is controlled to be less than or equal to 12 ppm, and the sulfur content is controlled to be 14-20 ppm; and the refined molten steel is subjected to continuous casting to acquire the high-cleanliness hot-series variety steel produced at low cost. The method can reduce the production cost of the clean steel, and effectively control the content of sulfur and inclusions in the clean steel.

Description

technical field [0001] The invention belongs to the technical field of steelmaking technology, and in particular relates to a method for producing high-cleanliness hot grade steel at low cost. Background technique [0002] In recent years, the domestic iron and steel industry is facing serious overcapacity, and the homogeneous competition of high-end products of advanced steel mills is also becoming more and more serious. For example, some advanced domestic steel mills can produce high-grade pipeline steel, automotive sheets and oriented silicon steel. Therefore, high-efficiency and low-cost production of high-quality steel has become a powerful way for iron and steel enterprises to seek development. [0003] High-grade pipeline steel is a typical representative of clean steel. At present, the domestic production process is mainly molten iron pretreatment→converter steelmaking→LF refining→RH / VD refining→continuous casting. The existing clean steel production process mainly h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C1/02C21C5/28C21C7/064C21C7/10
CPCC21C1/02C21C1/025C21C5/28C21C7/064C21C7/10Y02P10/20
Inventor 刘延强李向奎张丙龙乔焕山韩乐李欢宋冉缪成亮杜金磊赵三元詹美珠沙远洋陈虎周东谨刘浩王章岭赵旭陈守关杨晋姜博徐华刘应心田贵昌商艳民
Owner SHOUGANG JINGTANG IRON & STEEL CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com