Antique white-green glaze and preparation method thereof, and preparation method of antique white-green glaze ceramic product

A technology of ceramic products and white-green glaze, applied in the field of ceramics, can solve problems such as broken and achieve the effect of stable molding

Pending Publication Date: 2021-08-10
DEHUA HENGHAN ARTS
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, whether it is tableware or handicrafts, most of the products now are relatively bright and innovative ceramic products, and most of the ceramic products that look more age-like are passed down from ancestors and are relatively rare in the market. The outer surface of ceramic products with a sense of age will feel broken, which also has a certain degree of appreciation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antique white-green glaze and preparation method thereof, and preparation method of antique white-green glaze ceramic product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The antique white-green glaze includes the following components in parts by mass: 70 parts of kaolin, 6 parts of feldspar, 5 parts of quartz, 2 parts of zinc oxide, 3 parts of calcium carbonate, 13 parts of antimony ore, and 7 parts of wollastonite 6 parts of chalk, 11 parts of diabase, 1 part of iron oxide, and 5 parts of medical stone.

[0032] The preparation method of antique white-green glaze comprises the following steps:

[0033] Step 1. Broken

[0034] According to the number of parts by mass, the kaolin, feldspar, quartz, calcium carbonate, antimony ore, wollastonite, chalk, diabase and medical stone are respectively crushed and then mixed and stirred to obtain crushed material, and sieved for later use;

[0035] Step two, ball milling

[0036] According to the number of parts by mass, the crushed material obtained in step 1 is mixed with the zinc oxide and iron oxide, then ball milled, and sieved to obtain a ball mill;

[0037] Step 3. Beating

[0038] Be...

Embodiment 2

[0049] Antique white and green glaze, including the following components in terms of parts by mass: 75 parts of kaolin, 7 parts of feldspar, 6 parts of quartz, 3 parts of zinc oxide, 5 parts of calcium carbonate, 16 parts of antimony ore, and 8 parts of wollastonite 7 parts of chalk, 14 parts of diabase, 2 parts of iron oxide, 7 parts of medical stone.

[0050] The preparation method of antique white-green glaze comprises the following steps:

[0051] Step 1. Broken

[0052] According to the number of parts by mass, the kaolin, feldspar, quartz, calcium carbonate, antimony ore, wollastonite, chalk, diabase and medical stone are respectively crushed and then mixed and stirred to obtain crushed material, and sieved for later use;

[0053] Step two, ball milling

[0054] According to the number of parts by mass, the crushed material obtained in step 1 is mixed with the zinc oxide and iron oxide, then ball milled, and sieved to obtain a ball mill;

[0055] Step 3. Beating

[...

Embodiment 3

[0067] Antique white and green glaze, including the following components in parts by mass: 80 parts of kaolin, 8 parts of feldspar, 7 parts of quartz, 5 parts of zinc oxide, 6 parts of calcium carbonate, 20 parts of antimony ore, and 8 parts of wollastonite 9 parts of chalk, 17 parts of diabase, 3 parts of iron oxide, 11 parts of medical stone.

[0068]The preparation method of antique white-green glaze comprises the following steps:

[0069] Step 1. Broken

[0070] According to the number of parts by mass, the kaolin, feldspar, quartz, calcium carbonate, antimony ore, wollastonite, chalk, diabase and medical stone are respectively crushed and then mixed and stirred to obtain crushed material, and sieved for later use;

[0071] Step two, ball milling

[0072] According to the number of parts by mass, the crushed material obtained in step 1 is mixed with the zinc oxide and iron oxide, then ball milled, and sieved to obtain a ball mill;

[0073] Step 3. Beating

[0074] Bea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antique white-green glaze and a preparation method thereof, and a preparation method of an antique white-green glaze ceramic product, and belongs to the technical field of ceramics. The antique white-green glaze is characterized by comprising the following components in parts by mass: 70-80 parts of kaolin, 6-8 parts of feldspar, 5-7 parts of quartz, 2-5 parts of zinc oxide, 3-6 parts of calcium carbonate, 13-20 parts of stibnite, 7-8 parts of wollastonite, 6-9 parts of chalk soil, 11-17 parts of diabase, 1-3 parts of iron oxide and 5-11 parts of medical stone. The prepared antique white-green glaze ceramic product is high in glaze stability, high in strength and old-fashioned.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to an antique white-green glaze material and a preparation method thereof, and a preparation method of antique white-green glaze ceramic products. Background technique [0002] Ceramic products are already a must-have item in every household in our country. Whether it is tableware or handicrafts, they can be seen everywhere. However, whether it is tableware or handicrafts, most of the products now are relatively bright and innovative ceramic products, and most of the ceramic products that look more age-like are passed down from ancestors and are relatively rare in the market. The outer surface of ceramic products with a sense of age will feel broken, which also has a certain degree of appreciation. Therefore, how to prepare ceramic products with a sense of age has certain significance. Contents of the invention [0003] The object of the present invention is to over...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B33/04C04B33/13C04B33/132C04B33/34C04B38/00C04B38/02C04B35/18C04B35/622C04B41/86
CPCC03C8/00C04B41/86C04B41/5022C04B33/04C04B33/34C04B33/1324C04B33/13C04B38/0025C04B38/02C04B35/18C04B35/62204C04B41/009C04B2235/3463C04B2235/3418C04B2235/6562Y02P40/60
Inventor 林锦明
Owner DEHUA HENGHAN ARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com