Preparation method of carbon aerogel containing double metal sites and application of aluminum-air battery

A carbon aerogel, battery application technology, used in battery electrodes, fuel cell-type half-cells and primary battery-type half-cells, circuits, etc., can solve problems such as slow kinetics and low ionic conductivity

Inactive Publication Date: 2021-07-06
CENT SOUTH UNIV
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, neutral media usually have low ionic conductivity and very low OH - concentration, the oxygen reduction reaction (ORR) kinetics of common air cathode catalysts in neutral salt solutions is slow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of carbon aerogel containing double metal sites and application of aluminum-air battery
  • Preparation method of carbon aerogel containing double metal sites and application of aluminum-air battery
  • Preparation method of carbon aerogel containing double metal sites and application of aluminum-air battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The embodiment of the present invention designs a method for preparing carbon aerogels containing bimetallic sites, and its specific technical scheme is as follows:

[0040]Synthesis of S100 gelatin hydrogel: 60 mg of gelatin with a freezing capacity of 250 bloom, 30 mg of silica nanoparticles with a particle size of 15 nm and 2.51 mL of deionized water were placed in a 20 mL small glass bottle, stirred at room temperature for 40-60 min, and then Stir in a water bath at 60°C for 10-20min, return to room temperature after it is completely dissolved, add 150μL of iron-phenanthroline complex at a concentration of 0.2mol / L, 100μL of copper-o-phenanthroline complex at a concentration of 0.2mol / L Nitrophenanthrene complex, 80 μL, zinc acetate solution with a concentration of 1mol / L were mixed evenly, and the obtained solution was frozen in a -4°C refrigerator for 20 minutes to form a hydrogel, which was named G / Fe(PM) 3 -Cu(PM) 3 ;

[0041] Preparation of S200 iron-copper d...

Embodiment 2

[0048] A method for preparing a bimetallic site carbon airgel catalyst provided in the embodiment of the present invention, the specific steps are as follows:

[0049] S100, the synthesis of biomass hydrogel: Weigh 60mg of 250bloom gelatin and 30mg of silica nanoparticles (15nm) in a small glass bottle, add 2.51mL of deionized water, stir at room temperature for 40min to make it completely absorbed, and then Heated in a water bath at 60°C for 10 minutes, and returned to room temperature after it was completely dissolved, then added 150 μL of 0.2M iron-phenanthroline complex, 100 μL of 0.2M copper-phenanthroline complex, and 80 μL of 1M The zinc acetate solution was mixed evenly, and the obtained solution was placed in a -4°C refrigerator for 20 minutes to form a hydrogel, which was named G / Fe(PM) 3 -Cu(PM) 3 .

[0050] Preparation of S200 iron-copper double-site carbon airgel: G / Fe(PM) synthesized in step S100 3 -Cu(PM) 3 After the hydrogel was freeze-dried overnight, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of carbon aerogel containing double metal sites and application of an aluminum-air battery. The aerogel takes gelatin as a monomer, silicon dioxide as a hard template and an iron / copper-phenanthroline complex as a hydrogel precursor synthesized from a nitrogen source and a metal source; the preparation method comprises the following steps: carrying out freeze drying, high-temperature pyrolysis and acid pickling to obtain iron and copper double-site-doped carbon aerogel, and meanwhile, due to the fact that the carbon aerogel has rich three-dimensional wrinkles, a porous structure and active double metal sites, the carbon aerogel shows excellent oxygen reduction (ORR) electrocatalytic activity under alkaline and neutral conditions. The performance of a neutral aluminum-air battery assembled by taking the carbon aerogel as a positive electrode is obviously superior to that of a commercial Pt / C electrocatalyst, so that the catalyst prepared by the invention has potential guiding significance for research, development and production of a non-corrosive flexible wearable metal-air battery.

Description

technical field [0001] The invention relates to the technical field of energy storage and conversion, in particular to a method for preparing a nitrogen-doped biomass carbon airgel-supported FeCu bimetallic site porous material and its application in an aluminum-air battery. Background technique [0002] The non-renewability of fossil energy and the increasing environmental pollution have promoted the development of sustainable energy technologies, such as metal-air batteries. Among them, the aluminum-air battery has a high theoretical energy density (2796Whkg -1 ), low cost, and environmentally friendly, and has the characteristics of abundant reserves, light weight, and low cost, it is considered to be a promising battery. Aluminum-air batteries use metal aluminum as the negative electrode and oxygen in the air as the positive electrode to generate electricity through oxidation-reduction reactions. The performance of the battery depends to a large extent on the catalyst o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/88H01M4/90H01M12/06
CPCH01M4/8825H01M4/9041H01M4/9083H01M12/06H01M2004/8689
Inventor 张翼陈阳何庭宋娅娅尹春阳
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com