A light-cured 3D printing nanoparticle-reinforced metal part and its preparation method

A 3D printing and nanoparticle technology, applied in metal processing equipment, additive manufacturing, additive processing, etc., can solve the problems of unavailable photocurable structure, uncurable photosensitive resin, poor dispersion of metal powder, etc., to achieve good dispersion, Easy to crystallize and release heat, lowering the effect of sintering degreasing temperature

Active Publication Date: 2022-01-11
INST OF METAL RESEARCH - CHINESE ACAD OF SCI
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at this stage, when metal materials are prepared by photocuring 3D printing, due to the high surface energy of metal powder, it is easy to cause agglomeration between particles, resulting in poor dispersion of metal powder in photosensitive resin; Penetration, the photosensitive resin in the slurry cannot be cured, and finally a complete photo-cured structure cannot be obtained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A light-cured 3D printing nanoparticle-reinforced metal part and its preparation method
  • A light-cured 3D printing nanoparticle-reinforced metal part and its preparation method
  • A light-cured 3D printing nanoparticle-reinforced metal part and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] This embodiment prepares a light-cured 3D printing nanoparticle-reinforced metal part, which specifically includes the following steps:

[0067] Preparation of amorphous layer coating metal powder material: first with 250g particle diameter FeCrMoCB amorphous powder (wherein, the mass fraction of Fe is 57%, the mass fraction of Cr is 23%, the mass fraction of Mo is 18%, C The mass fraction of B is 1.5%, the mass fraction of B is 0.5%) and 100g of polyacrylic acid are placed in a beaker and mixed and heated to 50 ° C, and after mechanical stirring for 60 minutes, the temperature is raised to 100 ° C, while mechanical stirring Slowly add 50g of benzoyl peroxide and 700g of FeCrTiAlWMoTaCBZr metal powder (wherein, the massfraction of Fe is 58.25, the massfraction of Cr is 21%, the massfraction of Ti is 8%, the massfraction of Al is 10 microns) The mass fraction is 4.5%, the mass fraction of W is 4%, the mass fraction of Mo is 2%, the mass fraction of Ta is 2%, the mass fra...

Embodiment 2

[0075] This embodiment prepares a light-cured 3D printing nanoparticle-reinforced metal part, which specifically includes the following steps:

[0076] Preparation of amorphous layer coated metal powder material: first 150g of FeAlNbB amorphous powder with particle diameter of 120nm (wherein, the mass fraction of Fe is 71.5%, the mass fraction of Al is 24%, the mass fraction of Nb is 4%, B The mass fraction is 0.5%) and 150g of chloroacrylic acid are mixed in a beaker and heated to 60°C, and after 90 minutes of mechanical stirring, the temperature is raised to 90°C, and 100g of benzene peroxide is slowly added to it while mechanically stirring tert-butyl formate and 600g particle diameter are the FeTiAlNbCB metal powder (alloy powder of 30 microns, wherein, the massfraction of Fe is 60%, the massfraction of Ti is 18%, the massfraction of Al is 17%, the massfraction of Nb is 4%, the mass fraction of C is 0.5, and the mass fraction of B is 0.5%), and the coating step is carried ...

Embodiment 3

[0084] This embodiment prepares a light-cured 3D printing nanoparticle-reinforced metal part, which specifically includes the following steps:

[0085] Preparation of amorphous layer coated metal powder material: first 200g of FeCrSiBMn amorphous powder with a particle diameter of 100nm (the mass fraction of Fe is 69.5%, the mass fraction of Cr is 24%, the mass fraction of Si is 4%, the mass fraction of B Fraction is 0.5%, the mass fraction of Mn is 2%) and 120g polyacrylic acid are placed in the beaker and mixed and heated up to 55 ℃, and after mechanical stirring for 100 minutes, then raise the temperature to 80 ℃, while mechanical stirring Slowly add 80g of benzoyl peroxide and 600g of FeCrAlSiMoBMn metal powder (alloy powder, wherein the massfraction of Fe is 58%, the massfraction of Cr is 21%, the massfraction of Al is 17%, Si The mass fraction of Mo is 2%, the mass fraction of Mo is 1%, the mass fraction of B is 0.5%, and the mass fraction of Mn is 0.5%), and the coating...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a light-cured 3D printing nanoparticle-reinforced metal piece and a preparation method thereof. The preparation method includes the following steps: after mixing amorphous powder and a coating agent, adding a coupling agent and a coating agent to it at a set temperature The metal powder is stirred to carry out the coating step; the product obtained in the coating step is post-treated to obtain an amorphous layer coated metal powder material; the amorphous layer is coated with the metal powder material, photosensitive resin, ultraviolet photoinitiator, and dispersant Prepare light-curable 3D printing paste; use light-curable 3D printer to carry out light-curing molding treatment on light-curable 3D printing paste to obtain light-curable 3D printing blank; degrease and sinter light-curable 3D printing blank to obtain light-curable 3D printing paste Curing 3D printed nanoparticle-reinforced metal parts. The invention improves the dispersibility of the metal powder in the photosensitive resin slurry by making the metal powder into an amorphous layer-coated metal powder material with a powdery core-shell structure, and prepares a light-cured 3D printing nanoparticle-reinforced metal piece.

Description

technical field [0001] The invention relates to the technical field of 3D printing additive manufacturing, in particular to a light-cured 3D printing nanoparticle-reinforced metal part and a preparation method thereof. Background technique [0002] At present, my country's machinery industry is accelerating the transformation of the development mode, and the production mode is striving to change to energy saving, emission reduction, and green manufacturing. The traditional subtractive manufacturing is developing in the direction of additive manufacturing. The near-net shape manufacturing technology of additive manufacturing has attracted widespread attention. Metal additive manufacturing technology mainly focuses on selected area laser melting (SLM), electron beam melting (EBM) and other technologies, but the above-mentioned processes cause thermal cracks or thermal stress material defects due to the huge energy input to the material during the preparation process. . In ord...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F10/10C22C45/02B33Y10/00B33Y80/00
CPCB22F3/22B22F3/1021C22C45/02B33Y10/00B33Y80/00B22F1/17
Inventor 李金国李乔磊梁静静周亦胄孙晓峰
Owner INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com