A concrete and anti-radiation technology, applied in the field of concrete, can solve problems such as difficulty in preventing radiation, difficult construction, and easy cracking

Pending Publication Date: 2021-05-04
山东阳华建筑安装工程有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary concrete is difficult to play a good role in radiation protection, and the strength of ordinary concrete is low, easy to crack, and it is difficult to construct.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-radiation and anti-crack concrete
  • Anti-radiation and anti-crack concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This embodiment provides a radiation-proof and crack-resistant concrete, which includes the following raw materials: 150kg of cement, 45kg of mineral admixture, 1300kg of magnetite placer, 1700kg of magnetite ore, 20kg of anti-cracking agent, 5kg of water reducing agent and 120kg of water , wherein, the above-mentioned cement is Portland cement, the above-mentioned mineral admixture is a mixture of fly ash above the national standard II level and concrete slag above the S95 level in a ratio of 1:1, and the above-mentioned magnetite placer and the above-mentioned magnetite ore The effective content of iron element is 70%, and the apparent density in the dry state is 4700kg / m 3 , the fineness modulus of the above-mentioned magnetite placer is 3, the particle size of the above-mentioned magnetite ore is 20mm, and the content of needle flake ore is 10%.

[0037] The above-mentioned anti-cracking agent includes 2% of corn starch dextrin cement hydration control material, 30%...

Embodiment 2

[0039] This embodiment provides a kind of anti-radiation and anti-crack concrete, which includes the following raw material components: 450kg of cement, 200kg of mineral admixture, 1600kg of magnetite placer, 2100kg of magnetite ore, 50kg of anti-cracking agent, 15kg of water reducing agent and 220kg of water , wherein, the above-mentioned cement is 42.5 grade ordinary Portland cement, the above-mentioned mineral admixture is made by mixing the fly ash above the national standard II grade and the concrete slag above the S95 grade in a ratio of 1:2, and the above-mentioned magnetite placer and The effective iron content of the above-mentioned magnetite ore is 75%, and the apparent density in the dry state is 4800kg / m 3 , the fineness modulus of the above-mentioned magnetite placer is 2.3, the particle size of the above-mentioned magnetite ore is 5mm, and the content of needle flake ore is 8%.

[0040] The above-mentioned anti-cracking agent includes 4% of corn starch dextrin ce...

Embodiment 3

[0042] This embodiment provides a kind of anti-radiation and anti-crack concrete, which includes the following raw materials: 200 kg of cement, 50 kg of mineral admixture, 1400 kg of magnetite placer, 1800 kg of magnetite ore, 25 kg of anti-cracking agent, 6 kg of water reducing agent and 150 kg of water , wherein, the above-mentioned cement is 52.5 grade ordinary Portland cement, the above-mentioned mineral admixture is a mixture of fly ash above national standard II and above concrete slag in a ratio of 2:1, and the above-mentioned magnetite placer and The effective iron content of the above-mentioned magnetite ore is 80%, and the apparent density in the dry state is 4900kg / m 3 , the fineness modulus of the above-mentioned magnetite placer is 2.3, the particle size of the above-mentioned magnetite ore is 15mm, and the content of needle flake ore is 5%.

[0043] The anti-cracking agent includes 4% of corn starch dextrin cement hydration control material, 30% of light-burned c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apparent densityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Molar massaaaaaaaaaa
Login to view more

Abstract

The invention provides anti-radiation and anti-crack concrete, and relates to the technical field of concrete. The anti-radiation and anti-crack concrete comprises the following raw materials: cement, a mineral admixture, magnetite sand ore, magnetite ore, an anti-crack agent, a water reducing agent and water. The anti-radiation and anti-crack concrete is capable of effectively shielding rays, good in anti-radiation effect, high in concrete strength, not easy to crack, easy to construct, economical and environment-friendly.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a radiation-proof and crack-resistant concrete. Background technique [0002] Concrete is a general term for engineering composite materials in which aggregates are cemented into a whole by cementitious materials. Generally speaking, the term concrete refers to the cement concrete obtained by using cement as the cementitious material, sand and stone as the aggregate; mixed with water (may contain admixtures and admixtures) in a certain proportion, and stirred. Concrete, which is widely used in civil engineering. Ordinary concrete is difficult to play a good role in radiation protection, and ordinary concrete is low in strength, easy to crack, and difficult to construct. Contents of the invention [0003] The object of the present invention is to provide a radiation-proof and crack-resistant concrete, which can effectively shield radiation, has good radiation protection effec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2201/50C04B18/08C04B18/141C04B18/12C04B22/064C04B22/066C04B22/143C04B24/38C04B2103/302
Inventor 吴传英
Owner 山东阳华建筑安装工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap