Racket surface structure of pike racket and preparation method thereof

A surface structure and technology for gram rackets, applied in the field of surface structure and preparation of pickle racquets

Inactive Publication Date: 2021-03-12
界首市扬泰体育用品科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the above-mentioned technical problems, the object of the present invention is to provide a pickle racket surface structure and its preparation method: by adding carbon fiber into the Soxhlet extractor, then adding acetone, heating up to the acetone boiling, and then reflux Extract for 48-72 hours, reflux extraction is completed, filter after cooling, take out the filter cake and vacuum dry to obtain pretreated carbon fiber, mix equal volumes of 0.15mol / L silver nitrate solution and 0.15mol / L potassium persulfate solution Evenly, the first mixed solution is obtained, the pretreated carbon fiber is added to the first mixed solution, and the temperature is 65-75°C. After constant temperature reaction for 1-2h, filter, take out the filter cake and repeat with deionized water Wash 3-5 times, obtain product A after vacuum drying, mix thionyl chloride and N,N-dimethylformamide according to the volume ratio of 18-20:1 to obtain the second mixed solution, add product A into the second mixed solution, and react at a constant temperature for 36-50 hours at a temperature of 75-80°C, then filter, take out the filter cake and wash it repeatedly with deionized water for 3-5 times to obtain product B, and add melamine to In distilled water, then add a condensing agent and mix evenly to obtain the third mixed solution. Add the product B and the third mixed solution to the reaction kettle, and react for 30-40min at a temperature of 280-320°C and a pressure of 12MPa. After cooling, filter, take out the filter cake and wash it repeatedly with ethanol for 3-5 times, obtain modified carbon fiber after vacuum drying, weave the modified carbon fiber to form modified carbon fiber cloth, and use honeycomb aluminum material and modified carbon fiber cloth according to the peak The racket is cut and shaped according to the specifications of the racket, and then the cut modified carbon fiber cloth is glued to the upper and lower surfaces of the cut honeycomb aluminum material to obtain the surface structure of the Peak racket, which solves the problem of the surface and structure of the existing Peak racket made of carbon fiber. It is more complicated and difficult to manufacture, and the existing carbon fiber or glass fiber is prone to monofilament breakage, resulting in a decrease in fiber strength, making the surface quality of the prepared Pickle racket unstable, prone to yarn clamping, material shortage, internal fold or break problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment is a pickle racket surface structure, including a filling plate and a surface layer on the upper and lower surfaces of the filling plate, the material of the filling plate is honeycomb aluminum material, and the material of the surface layer is modified carbon fiber;

[0028] A method for preparing a surface structure of a pickle racket, comprising the following steps:

[0029] Step 1: Add carbon fiber to the Soxhlet extractor, then add acetone, heat up and heat until the acetone boils, then carry out reflux extraction for 48 hours, after reflux extraction is completed, filter after cooling, take out the filter cake and vacuum dry to obtain pretreated carbon fiber;

[0030]Step 2: Mix the silver nitrate solution of 0.15mol / L and the potassium persulfate solution of 0.15mol / L in an equal volume to obtain the first mixed solution, and add the pretreated carbon fiber to the first mixed solution, at a temperature of 65 After constant temperature reaction fo...

Embodiment 2

[0038] This embodiment is a preparation method of a pickle racket surface structure, comprising the following steps:

[0039] Step 1: Add carbon fiber to the Soxhlet extractor, then add acetone, raise the temperature and heat until the acetone boils, and then perform reflux extraction for 60 hours. After the reflux extraction is completed, filter after cooling, take out the filter cake and vacuum dry it to obtain pretreated carbon fiber;

[0040] Step 2: Mix the silver nitrate solution of 0.15mol / L and the potassium persulfate solution of 0.15mol / L in an equal volume to obtain the first mixed solution, and add the pretreated carbon fiber to the first mixed solution, at a temperature of 70 After constant temperature reaction at ℃ for 2 hours, filter, take out the filter cake and wash it repeatedly with deionized water 4 times, and obtain product A after vacuum drying;

[0041] Step 3: Mix thionyl chloride and N,N-dimethylformamide evenly according to the volume ratio of 19:1 t...

Embodiment 3

[0048] This embodiment is a preparation method of a pickle racket surface structure, comprising the following steps:

[0049] Step 1: Add carbon fiber to the Soxhlet extractor, then add acetone, heat up to acetone boiling, then carry out reflux extraction for 72 hours, reflux extraction is completed, filter after cooling, take out the filter cake and vacuum dry to obtain pretreated carbon fiber;

[0050] Step 2: Mix the silver nitrate solution of 0.15mol / L and the potassium persulfate solution of 0.15mol / L in an equal volume to obtain the first mixed solution, and add the pretreated carbon fiber to the first mixed solution, at a temperature of 75 After constant temperature reaction at ℃ for 2 hours, filter, take out the filter cake and wash it repeatedly with deionized water for 5 times, and obtain product A after vacuum drying;

[0051] Step 3: Mix thionyl chloride and N,N-dimethylformamide evenly according to the volume ratio of 20:1 to obtain a second mixed solution, add p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

According to the racket surface structure of a pike racket and a preparation method thereof, sizing treatment is conducted on carbon fibers through acetone, then oxidation treatment is conducted on the carbon fibers through a silver nitrate solution and a potassium peroxodisulfate solution, more oxygen-containing functional groups are formed on the surfaces of the carbon fibers, and therefore theinfiltration degree of the carbon fibers is enhanced; the melamine is grafted to the oxidized carbon fiber, so that the binding force between the carbon fiber and the epoxy resin is enhanced, the crack forming work, the expansion work and the impact work of the carbon fiber are further obviously increased, and corrosion resistance of the carbon fiber is improved; carbon fibers can be broken only by needing higher impact energy, and the mechanical properties of the carbon fibers are effectively improved, so impact resistance of the prepared racket surface structure of the pike racket is obviously improved, and the service life of the racket surface structure is obviously prolonged.

Description

technical field [0001] The invention relates to the field of sporting goods, in particular to a pickle racket surface structure and a preparation method thereof. Background technique [0002] Pickleball is a sport of hitting a ball with a racket, and it is also a hybrid sport that combines tennis, badminton and table tennis. [0003] The existing pickle racket head structure is made of wood or made of carbon fiber or glass fiber. The surface of the Pickleball racket made of wood is heavy, has poor hand feeling and hard hardness; when athletes are exercising, it has poor elasticity, bad hand feeling, poor durability and short service life. The surface of a pickle racquet made of carbon fiber or glass fiber has a complex structure, is difficult to manufacture, and takes a long time. Moreover, the existing carbon fiber or glass fiber is prone to single-filament breakage, resulting in a decrease in fiber strength. The quality of the surface of the obtained Pickle racket is uns...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A63B59/42D06M13/127D06M11/65D06M11/50D06M13/364D04C1/02D06M101/40
CPCA63B59/42D06M13/127D06M11/65D06M11/50D06M13/364D04C1/02D06M2101/40D06M2200/40D10B2101/12
Inventor 杨晓燕
Owner 界首市扬泰体育用品科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products