A kind of low-viscosity high-strength toughened silicone resin composition and preparation method thereof

A silicone resin composition and high-strength technology, which is applied in the field of silicone polymers, can solve the problems of difficult toughening effects due to co-hydrolysis of functional monomers, and achieve the goals of improving resin strength, excellent comprehensive performance, and improving reinforcement effects Effect

Active Publication Date: 2022-03-18
NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As previously analyzed, co-hydrolysis of monomers with multiple functionalities is difficult to achieve the desired toughening effect, so it is conceivable that it is difficult to withstand severe thermal shocks, and the preparation methods of CN105218825 and CN101070386 all adopt a water washing process, resulting in a large amount of waste water
[0005] At present, there is no low viscosity (≤1000mPa s), high strength (bending strength ≥50N / mm 2 , Tensile strength ≥ 20MPa) and can withstand 300 times 0-220 ℃ cold and heat impact toughened silicone resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low-viscosity high-strength toughened silicone resin composition and preparation method thereof
  • A kind of low-viscosity high-strength toughened silicone resin composition and preparation method thereof
  • A kind of low-viscosity high-strength toughened silicone resin composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Add 172.8 g of deionized water, 400 g of toluene, and 10 g of acetic acid into a four-necked flask equipped with a thermometer, a stirring paddle, and a reflux condenser, stir evenly, and add 1,057 g of phenyltrimethoxysilane dropwise. After the addition, the temperature was raised to reflux, reacted for 2h, and then cooled to room temperature. The low boilers were distilled off at a pressure of less than 10KPa at 80°C to obtain 680g of a liquid trifunctional silicone resin prepolymer.

[0034] Add 270 g of deionized water, 0.38 g of trifluoromethanesulfonic acid, and 500 g of toluene into a four-necked flask equipped with a thermometer, a stirring paddle, and a reflux condenser, stir evenly, and dropwise add 900 g of methylphenyldimethoxysilane, A mixed solution consisting of 261 g of methylvinyldimethoxysilane and 262 g of methylvinyldimethoxysilane. After the addition, the reaction was refluxed for 2 hours, cooled to room temperature, and the layers were separated, ...

Embodiment 2

[0037] Add 172.8 g of deionized water, 400 g of toluene, and 10 g of acetic acid into a four-neck flask equipped with a thermometer, a stirring paddle, and a reflux condenser, stir evenly, and add 952 g of phenyltrimethoxysilane dropwise. After the addition, the temperature was raised to reflux, reacted for 2h, and then cooled to room temperature. The low boilers were distilled off at a pressure of less than 10 KPa at 80° C. to obtain 610 g of a liquid trifunctional silicone resin prepolymer.

[0038] Add 402 g of deionized water, 0.5 g of trifluoromethanesulfonic acid, and 600 g of toluene into a four-necked flask equipped with a thermometer, a stirring paddle, and a reflux condenser, stir evenly, and dropwise add 900 g of methylphenyldimethoxysilane, A mixed solution consisting of 371 g of methylvinyldimethoxysilane and 366 g of methylvinyldimethoxysilane. After the addition, the reaction was refluxed for 2 hours, cooled to room temperature, and the layers were separated, a...

Embodiment 3

[0041] Add 144 g of deionized water, 300 g of toluene, and 8 g of acetic acid into a four-necked flask equipped with a thermometer, a stirring paddle, and a reflux condenser, stir evenly, and add 793 g of phenyltrimethoxysilane dropwise. After the addition, the temperature was raised to reflux, reacted for 2h, and then cooled to room temperature. The low boilers were distilled off at a pressure of less than 10KPa at 80°C to obtain 510g of a liquid trifunctional silicone resin prepolymer.

[0042] Add 355 g of deionized water, 0.4 g of trifluoromethanesulfonic acid, and 500 g of toluene into a four-necked flask equipped with a thermometer, a stirring paddle, and a reflux condenser, stir evenly, and dropwise add 900 g of methylphenyldimethoxysilane, A mixed solution consisting of 293 g of methylvinyldimethoxysilane and 288 g of methylvinyldimethoxysilane. After the addition, the reaction was refluxed for 2 hours, cooled to room temperature, and the layers were separated, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
tensile strengthaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-viscosity high-strength toughened silicone resin composition and a preparation method thereof. The invention hydrolyzes and polycondenses trifunctional siloxane monomers and difunctional siloxane monomers separately to prepare high-crosslinking density body-shaped reinforcing structures and linear toughening structures with a certain molecular weight, and then combines them with monofunctional end-capped The low-viscosity silicone resin (R 1 SiO 1.5 ) a (R 2 R 3 SiO) b (R 4 3 SiO 0.5 ) c . Silicon vinyl and silicon hydrogen groups are introduced into the linear structure of the resin, and mixed with silicone resin-coated platinum complexes, alkyne or polyvinyl-containing inhibitors and tackifiers to obtain low-viscosity, high-strength toughened silicon resin composition. The composition achieves sufficient strength and toughness after being cured under the premise of low viscosity, and is resistant to cold and heat shock at 0°C to 220°C.

Description

technical field [0001] The invention relates to a low-viscosity, high-strength, toughened silicone resin composition and a preparation method thereof, belonging to the technical field of silicone polymers. Background technique [0002] Silicone resin is a thermosetting polysiloxane material with a highly cross-linked structure. It has excellent high temperature resistance (200-250 °C can be used for a long time), outstanding dielectric properties, excellent corona resistance, arc resistance, Low dielectric loss tangent, radiation resistance and flame retardant, especially the unique waterproof and moisture resistance, the insulation performance remains basically unchanged in water or humid environments, and is the first choice for impregnated insulation materials for electronic coils and motors. [0003] In order to improve the integrity of the insulation system and obtain an air-gap-free insulation system, the vacuum pressure impregnation (VPI) process is mostly used for la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G77/44C08G77/06
CPCC08G77/44C08G77/06
Inventor 彭丹牟秋红李金辉王峰
Owner NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap