Ceramic on-glaze new color aluminum tube pigment and preparation method thereof

A technology of ceramic glaze and color aluminum, applied in the field of ceramic glaze color, can solve the problems of excessive time wasting of abrasives, poor safety factor, unenvironmental protection, etc., and achieve the effect of reducing waste of resources

Inactive Publication Date: 2021-01-08
谌国星
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, mineral pigments are directly finely ground into powder for sale. The disadvantages are easy to waste, poor safety factor, not environmentally friendly, and a lot of time wasted on abrasives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A new color aluminum tube pigment on ceramic glaze, which is a product obtained by blending inorganic mineral pigment powder and oil material in a ratio of 1:2 through mineral processing, crushing, grinding, and grading of natural ore; the oil material is frankincense oil; inorganic mineral pigment The varieties of powder include: yellow vermilion, red vermilion, black vermilion, copper green, lead red, lead white, ink black and other colors.

Embodiment 2

[0019] A preparation method of a new color aluminum tube pigment on ceramic glaze, comprising the following steps:

[0020] (1) Select heavy-colored, high-grade natural ore and send it to the pulverizer, which will be continuously crushed into 0.2mm mineral particles, and then sent to the ball mill. The ball mill is a zirconia ball with a diameter of 1-5mm. 35:1, the rotating speed of the ball mill is 300 rpm, and the ball milling time is 30 hours to obtain a fine powder; the fine powder of 20-35 microns is classified, and the fine powder classified is dried at a temperature of 100 ℃ for 6 hour, obtain inorganic mineral pigment powder after drying;

[0021] (2) Weigh the inorganic mineral pigment powder and frankincense oil respectively according to the ratio of 1:2, put the frankincense oil in the blender and stir, then slowly add the inorganic mineral pigment powder obtained in step (1), blend and stir until the cream is saturated shape mixture;

[0022] (3) Put the satura...

Embodiment 3

[0024] A preparation method of a new color aluminum tube pigment on ceramic glaze, comprising the following steps:

[0025] (1) Select heavy-colored, high-grade natural ore and send it to the pulverizer, continuously crush it into 0.1mm mineral particles, and send the mineral particles into the ball mill. The ball mill is a zirconia ball with a diameter of 1-5mm. The mass ratio of the ball material 30:1, the rotating speed of the ball mill is 350 rpm, and the ball milling time is 10 hours to obtain a fine powder; the fine powder of 20-35 microns is classified, and the fine powder classified is dried at a temperature of 100 ℃ for 5 hour, obtain inorganic mineral pigment powder after drying;

[0026] (2) Weigh the inorganic mineral pigment powder and frankincense oil respectively according to the ratio of 1:2, put the frankincense oil in the blender and stir, then slowly add the inorganic mineral pigment powder obtained in step (1), blend and stir until the cream is saturated s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a ceramic on-glaze new color aluminum tube pigment and a preparation method thereof. The ceramic on-glaze new color aluminum tube pigment is a product obtained by blending inorganic mineral pigment powder formed by mineral separation, crushing, grinding and grading of natural ores and an oil material according to a ratio of 1:2, wherein the oil material is frankincense oil.The preparation method comprises the following steps: stirring frankincense oil in a stirrer, slowly adding inorganic mineral pigment powder, blending and stirring to obtain a saturated cream mixture;and filling the saturated cream mixture into an aluminum tube, sealing the aluminum tube by using a sealing machine, sealing the aluminum tube, storing and selling the aluminum tube. According to theinvention, the ceramic on-glaze new color mineral pigment powder and the oil material are blended and ground according to a corresponding ratio, are put into the aluminum pipe and are sold in a sealed manner, so that resource waste caused by cracking and unavailability of the raw materials due to long-time placement is reduced.

Description

technical field [0001] The invention belongs to the technical field of ceramic overglaze color, and in particular relates to a ceramic overglaze new color aluminum tube pigment and a preparation method thereof. Background technique [0002] Ceramic decorative pigments are very rich, including underglaze blue and white, high-temperature color glaze and overglaze pastel, ancient colors and new colors, especially new color pigments. New color is a ceramic overglaze porcelain decoration technique, which belongs to ceramic overglaze color. In terms of craftsmanship, there are three major types of decorations: overglaze, underglaze, inglaze and ceramics. Ceramic new color decoration has also aroused people's great attention, and the application of new color is becoming more and more extensive. [0003] The pigments used in Xincai are low-temperature pigments on glaze, and Xincai decoration is a product obtained by using low-temperature new color pigments to paint on the porcelai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/00C09C3/08
CPCC09C1/0009C09C3/08
Inventor 谌国星
Owner 谌国星
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com