Modified polypropylene PP plastic

A polypropylene and plastic technology, applied in the direction of zinc oxide/zinc hydroxide, etc., can solve the problems of breeding bacteria, virus infection, low antibacterial durability of polypropylene PP plastic, etc., and achieve the effect of preventing cell respiration

Inactive Publication Date: 2020-12-29
骆家宽
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing modified polypropylene PP plastics have low antibacterial properties. After long-term use, bacteria are easy to breed on the surface of the plastics, which in turn causes virus infection, and some polypropylene PP plastics are added with antibacterial agents to increase antibacterial properties. The antibacterial agent has a single antibacterial effect, which makes the antibacterial effect poor and easy to precipitate, which makes the antibacterial durability of polypropylene PP plastics low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified polypropylene PP plastic
  • Modified polypropylene PP plastic
  • Modified polypropylene PP plastic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A modified polypropylene PP plastic, made of the following raw materials in parts by weight: 80 parts of polypropylene, 8 parts of antibacterial filler, 2 parts of antimony trioxide, 3 parts of monoglyceride stearate, 3 parts of dioctyl sebacate 2 parts, glass fiber 2 parts;

[0042] The modified polypropylene PP plastic is made by the following steps:

[0043]Step S1: stirring the polypropylene and monoglyceride stearate for 10 minutes at a rotational speed of 300 r / min to obtain the first mixture;

[0044] Step S2: Stir the antibacterial filler and glass fiber for 3 minutes at a rotational speed of 500 r / min, then add antimony trioxide, and continue stirring for 10 minutes to obtain a second mixture;

[0045] Step S3: Melt and stir the first mixture and the second mixture at a speed of 1000r / min and a temperature of 160°C for 5 minutes, then add dioctyl sebacate and continue stirring for 20 minutes to obtain a molten material ;

[0046] Step S4: Put the molten mate...

Embodiment 2

[0055] A modified polypropylene PP plastic, made of the following raw materials in parts by weight: 85 parts of polypropylene, 9 parts of antibacterial filler, 3 parts of antimony trioxide, 4 parts of monoglyceride stearate, 4 parts of dioctyl sebacate 2 parts, glass fiber 2 parts;

[0056] The modified polypropylene PP plastic is made by the following steps:

[0057] Step S1: stirring the polypropylene and monoglyceride stearate for 13 minutes at a rotational speed of 400 r / min to obtain the first mixture;

[0058] Step S2: Stir the antibacterial filler and glass fiber for 4 minutes at a rotational speed of 600 r / min, then add antimony trioxide, and continue stirring for 13 minutes to obtain a second mixture;

[0059] Step S3: Melt and stir the first mixture and the second mixture for 8 minutes under the conditions of rotation speed of 1100 r / min and temperature of 170 ° C, then add dioctyl sebacate and continue stirring for 25 minutes to obtain a molten material ;

[0060...

Embodiment 3

[0069] A modified polypropylene PP plastic, made of the following raw materials in parts by weight: 90 parts of polypropylene, 9 parts of antibacterial filler, 4 parts of antimony trioxide, 4 parts of monoglyceride stearate, and 4 parts of dioctyl sebacate , 4 parts of glass fiber;

[0070] The modified polypropylene PP plastic is made by the following steps:

[0071] Step S1: stirring the polypropylene and monoglyceride stearate for 13 minutes at a rotational speed of 400 r / min to obtain the first mixture;

[0072] Step S2: Stir the antibacterial filler and glass fiber for 4 minutes at a rotational speed of 700 r / min, then add antimony trioxide, and continue stirring for 13 minutes to obtain a second mixture;

[0073] Step S3: Melt and stir the first mixture and the second mixture at a speed of 1200r / min and a temperature of 170°C for 8 minutes, then add dioctyl sebacate and continue stirring for 25 minutes to obtain a molten material ;

[0074] Step S4: Put the molten mat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The modified polypropylene PP plastic is prepared from the following raw materials in parts by weight: 80-100 parts of polypropylene, 8-10 parts of an antibacterial filler, 2-5 parts of a flame retardant, 3-5 parts of a dispersing agent, 3-5 parts of a plasticizer and 2-3 parts of glass fibers. The antibacterial filler can act on lipid or peptidoglycan in bacterial cell walls to destroy the structure of the lipid or peptidoglycan and cause damage to the bacterial cell walls, and after the antibacterial filler is mixed with a polymer, antibacterial substances in the antibacterial filler cannotmigrate and separate out in the long-term use process of the polymer, so that the antibacterial property of the polymer is more durable, and the service life of the polymer is prolonged. When the polymer is illuminated, the antibacterial filler can form positive holes and release free electrons at the same time, the free electrons can be absorbed by oxygen molecules and become negative oxygen ionswith extremely high chemical activity, and the negative oxygen ions can oxidize organic matters in bacteria so as to kill the bacteria.

Description

technical field [0001] The invention belongs to the technical field of plastic preparation, and in particular relates to a modified polypropylene PP plastic. Background technique [0002] Polypropylene is a colorless, odorless, non-toxic, translucent solid substance. Polypropylene is a thermoplastic synthetic resin with excellent performance. It is a colorless and translucent thermoplastic lightweight general-purpose plastic with chemical resistance and heat resistance. properties, electrical insulation, high-strength mechanical properties and good high wear-resistant processing properties, etc., which makes polypropylene rapidly used in machinery, automobiles, electronic appliances, construction, textiles, packaging, agriculture, forestry, fishery and food industries, etc. Many fields have been widely developed and applied. In recent years, with the rapid development of packaging, electronics, automobiles and other industries, polypropylene materials are gradually replacing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L79/04C08K13/06C08K9/12C08K5/29C08K3/22C08K5/103C08K5/11C08K7/14C08G73/06C01G9/02
CPCC01G9/02C08G73/0633C08L23/12C08L79/04C08K13/06C08K9/12C08K5/29C08K3/2279C08K5/103C08K5/11C08K7/14
Inventor 骆家宽
Owner 骆家宽
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap