Manufacturing method of super-strong bamboo fiber composite board

A manufacturing method, bamboo fiber technology, applied to flat products, other household appliances, household appliances, etc., can solve the problems of unfavorable tensile properties, unfavorable tension transmission, etc., and achieve the effect of realizing multi-function and increasing added value

Inactive Publication Date: 2020-12-04
张毅
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Bamboo fibers in the boards prepared in Documents 1 to 4 are all in a “felt” or free state, which is not conducive to tension transmission; Document 5 is compounded by dipping and rolling, which is not conducive to the development of tensile properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1 of the manufacture method of a kind of bamboo fiber composite board plate of the present invention is:

[0022] Step 1: The equivalent diameter is 0.5mm and the bamboo fiber of length 200mm and thermoplastic short fiber are carried out mixing and twisting into bamboo-plastic blended rope with bamboo 20% plastic 80% mass ratio;

[0023] Step 2: uniformly mixing 70% of thermoplastic powder and 30% of bamboo fiber powder by mass ratio to form bamboo-plastic mixed powder;

[0024] Step 3: In the autoclave, cross the bamboo-plastic blended rope according to the "warp" and "weft" at a certain angle and the number of meshes to form a plurality of tendons, and apply a tension of 50 MPa to the bamboo-plastic blended rope;

[0025] Step 4: Fill the bamboo-plastic mixed powder into the autoclave, apply a pressure of 20MPa, and a temperature of 230°C for 30 minutes;

[0026] Step 5: Keep the tension cool to room temperature.

Embodiment 2

[0028] Step 1: the bamboo green fiber with an equivalent diameter of 0.3mm and a length of 100mm and thermoplastic short fibers are mixed and twisted into a bamboo-plastic blended rope with a mass ratio of 50% bamboo to 50% plastic;

[0029] Step 2: uniformly mixing 50% of thermoplastic powder and 50% of bamboo fiber powder by mass to form bamboo-plastic mixed powder;

[0030] Step 3: In the autoclave, cross the bamboo-plastic blended rope according to the "warp" and "weft" at a certain angle and the number of meshes to form multiple tendons, and apply a tension of 30 MPa to the bamboo-plastic blended rope;

[0031] Step 4: Fill the mixed powder of bamboo and plastic into the autoclave, apply a pressure of 15MPa and a temperature of 180°C for 20 minutes;

[0032] Step 5: Keep the tension cool to room temperature.

Embodiment 3

[0034] Step 1: the bamboo fiber with an equivalent diameter of 0.2mm and a length of 50mm and thermoplastic short fibers are mixed and twisted into a bamboo-plastic spinning rope with a mass ratio of 80% of bamboo and 20% of plastic;

[0035] Step 2: uniformly mix 30% of thermoplastic powder and 70% of bamboo fiber powder into bamboo-plastic mixed powder;

[0036] Step 3: In the autoclave, cross the bamboo-plastic blended rope according to the "warp" and "weft" at a certain angle and the number of meshes to form a plurality of ribs, and apply a tension of 10 MPa to the bamboo-plastic blended rope;

[0037] Step 4: Fill the mixed powder of bamboo and plastic into the autoclave, apply a pressure of 10MPa and a temperature of 140°C for 10 minutes;

[0038] Step 5: Keep the tension cool to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a manufacturing method of a super-strong bamboo fiber composite board. The manufacturing method includes the steps that bamboo fibers with the equivalent diameter of (0.2-0.5) mm and the length of (30-100) mm are blended with thermoplastic plastic short fibers according to the mass ratio of (70-30)%:(30-70)% to form a blended rope, and uniformly mixing is conducted on thermoplastic powder (80-20)% and bamboo fiber powder (20-80)% to form mixed powder. By means of the manufacturing method of the super-strong bamboo fiber composite board, a reinforced bamboo-plastic composite material is prepared by taking the blended rope as a reinforcing rib and taking the mixed powder as filler, so that the application limitation of a traditional bamboo material is broken through, the multifunction property of the bamboo fiber material is achieved, and the additional value of the bamboo fiber material is greatly improved.

Description

technical field [0001] The invention relates to a manufacturing method of a super-strong bamboo fiber composite board, in particular to a reinforced composite board prepared with bamboo fiber and thermoplastic as main raw materials. Background technique [0002] Bamboo fiber is a kind of natural fiber (also known as bamboo fiber) derived from bamboo. It has the advantages of low density, high strength, high rigidity, and wear resistance. It is a green, renewable, and degradable plant fiber. According to data, the tensile strength of bamboo fiber prepared by advanced technology is equivalent to that of carbon steel, and the mechanical properties of composite materials prepared by bamboo fiber are comparable to those of glass fiber reinforced plastics. Therefore, bamboo fiber is also called "natural glass fiber". [0003] Using bamboo fiber as a reinforcing material and thermoplastic as a matrix for composite, it can be prepared into a thermoplastic bamboo fiber composite mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29D7/00
CPCB29D7/00
Inventor 张毅彭建新
Owner 张毅
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com