Technology for flame-retardant and water-proof coating of fabric

A waterproof coating and fabric technology, applied in fabric surface trimming, textiles and papermaking, etc., can solve the problems of poor synergy of waterproof performance, reduced fabric strength, unstable flame retardant effect, etc., to achieve good flame retardant effect and reduce strength loss , good penetration and binding effect

Pending Publication Date: 2020-11-27
THE QUARTERMASTER RES INST OF THE GENERAL LOGISTICS DEPT OF THE CPLA
View PDF16 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from the public literature that in order to solve the problem of flame retardant and waterproof effects, the existing technical methods mainly use flame retardant glue alone to coat the surface of the fabric, or use multiple intermediate glue coating processes, but the flame retardant effect is unstable, Poor synergy with waterproof performance, reduced fabric strength, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technology for flame-retardant and water-proof coating of fabric
  • Technology for flame-retardant and water-proof coating of fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] 1. Using the leading cloth, the linear density of the package after printing, washing and shaping is 650dtex, and the square meter weight is 243g / m 2 The high-strength polyamide 66 air-changing yarn plain weave fabric is placed on the fabric conveying mechanism, unwound, and wet-steamed through a high-temperature and high-humidity steamer. The hot and humid steam is supersaturated steam at a temperature of 110°C; the pressure is 1.1bar, and then Put the reverse side of the fabric flat on the surface of the high-temperature hollow smooth chrome-plated metal roller, and pass it directly under the action of tension. The tension is 110N, and the temperature of the metal roller surface is 150°C. Cooling, the cooling temperature is normal temperature;

[0047] 2. Transfer the calendered and cooled fabric to the primer coating mechanism through guide rollers, and mix 100 parts by weight of polyurethane glue, 90 parts of flame retardant decabromodiphenylethane, 30 parts of flam...

Embodiment 2

[0053] 1. Using the leading cloth, the linear density of the printed, washed and shaped package is 1000dtex, and the square meter weight is 315g / m 2 The high-strength polyester air-change yarn plain weave fabric is placed on the fabric conveying mechanism, unwound, and steamed through a high-temperature and high-humidity steam drum. The temperature of the steam is 120°C; The surface of the hollow smooth chrome-plated metal drum passes directly under the action of tension, the tension is 150N, and the temperature of the metal drum surface is 160°C to obtain a fabric with a flat and smooth reverse side, and then the fabric is cooled by the cooling drum, and the cooling temperature is normal temperature.

[0054] 2. Transfer the calendered and cooled fabric to the primer coating mechanism through guide rollers, and mix 100 parts by weight of polyurethane glue, 90 parts of flame retardant decabromodiphenylethane, 30 parts of flame retardant Antimony, 3 parts of bridging agent mela...

Embodiment 3

[0060] 1. Using the leading cloth, the linear density of the printed and washed package is 500dtex, and the square meter weight is 202g / m 2 The high-strength polyamide 6 air-changing yarn plain weave fabric is placed on the fabric conveying mechanism, unwound, and under the control of a certain tension, it is wet-steamed through a high-temperature and high-humidity steamer. The hot and humid steam is saturated steam at a temperature of 110°C; the pressure 1.1 bar, and then the reverse side of the fabric is flatly attached to the surface of the high-temperature hollow smooth chrome-plated metal roller, and it passes directly under the action of tension. The fabric is cooled by the cooling drum, and the cooling temperature is normal temperature.

[0061] 2. Transfer the calendered and cooled fabric to the primer coating mechanism through guide rollers, and mix 100 parts by weight of polyurethane glue, 90 parts of flame retardant decabromodiphenylethane, 30 parts of flame retarda...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a technology for a flame-retardant and water-proof coating of a fabric. The technology comprises the following steps that the fabric is subjected to wet steaming first, and theto-be-coated surface of the fabric is polished and flatted by using a high-temperature metal smooth face to obtain a fabric with a flat and smooth reverse side; under the combined action of oscillation and blade coating, the reverse side of the fabric is coated with a primer coating adhesive to obtain a primer adhesive coated fabric; under the combined action of oscillation and blade coating, theprimer adhesive coated surface of the primer adhesive coated fabric is coated with a middle coating adhesive to obtain a primer-middle adhesive coated fabric; and a hot-melt elastic polyurethane filmand the coated surface of the coated fabric are subjected to hot pressing, adhesion and combination to obtain the flame-retardant and water-proof coating.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a flame-retardant and waterproof coating process for fabrics. Background technique [0002] Coating process is a functional fabric production and processing method. Coating can make fabrics have barrier functions, such as windproof, waterproof, flame retardant, and anti-biological and chemical agents, etc. Coated fabrics are widely used in various backpacks, tents, sleeping gear and outdoor clothing, etc., forming A large category of textile products. The basic operation method of fabric coating is to use a certain process to coat high polymer resin on one or both sides of the fabric, so that the resin and the fabric are physically combined to prepare a coated composite fabric, CN 201410345974, CN202157234U, CN201198521Y, CN103361987A, CN1990929A, NL1032490C2, CN 201610202478, CN 201710895898, etc. disclose relevant technical content. It can be seen from the publi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14D06N3/00D06C15/08
CPCD06N3/145D06N3/0034D06N3/0036D06N3/0088D06N3/0086D06N3/0077D06C15/08
Inventor 马天李伟萍龙知洲康越
Owner THE QUARTERMASTER RES INST OF THE GENERAL LOGISTICS DEPT OF THE CPLA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap