A kind of production technology of veneer impregnated with melamine glue

A technology of melamine glue and production process, which is applied in the direction of impregnating wood, wood impregnation, wood processing appliances, etc., can solve the problems of low production efficiency, inability to continuously impregnate, troublesome pressing and pasting process, etc., and achieve good wear resistance, waterproof and flame retardant. performance, simplify the subsequent pressing process, and improve the effect of product quality

Active Publication Date: 2022-03-11
李公浩
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Wooden sheet has strong texture and good visual aesthetics, but its wear resistance is very poor. To improve its wear resistance, it must go through various painting processes, which are complicated, and its flame retardancy and waterproof performance are extremely poor.
Melamine-impregnated paper can achieve strong wear resistance after curing and molding, but its texture and visual aesthetics are poor, and because the surface of substrates such as Polaroid boards and vinyl material boards is relatively smooth, traditional melamine-impregnated paper cannot Forming directly with vinyl materials by direct pressing requires multi-process secondary molding, and the production continuity and mass production capacity are poor; in order to obtain strong texture, good visual appearance, good wear resistance and waterproof performance As a surface-bonded material with flame-retardant properties, researchers began to study combining melamine glue and veneer to obtain melamine glue-impregnated veneer
However, the existing melamine impregnation process is mainly aimed at paper materials. When it is used to impregnate veneer, on the one hand, because the veneer is separate, it cannot be impregnated continuously, resulting in extremely low production efficiency; on the other hand, the final product obtained The quality of melamine-impregnated veneer is poor, and its wear resistance, waterproof and flame-retardant properties cannot meet the needs of use; moreover, when melamine-impregnated veneer is bonded to vinyl substrates, multiple pressings are required, which cannot be formed at one time, resulting in more troublesome pressing process
Therefore, the existing technology has the problems of low production efficiency, poor product quality and complicated follow-up pressing process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1. A production process for melamine glue impregnated veneer, comprising the following steps:

[0020] A. Cutting and trimming the purchased veneer to obtain veneer raw materials;

[0021] B, splicing veneer raw materials into rolls to obtain spliced ​​veneer;

[0022] C. Glue dipping treatment: dipping the spliced ​​veneer twice to obtain melamine glue impregnated veneer; the total amount of glue applied to the spliced ​​veneer is 120-180% of the weight of the spliced ​​veneer.

[0023] The length and width of the veneer raw material are greater than 1-2cm of the length and width of the plate to be pasted.

[0024] Use pressing equipment to cure the non-woven tape or adhesive-coated cloth by hot pressing and stick it on the adjacent veneer. The hot pressing temperature is 150-170°C and the hot pressing time is 10-20 seconds.

[0025] The width of the non-woven tape or adhesive coated cloth is 1.5-2.5cm, and the length is 1.1-1.4m.

[0026] The specific proc...

Embodiment 2

[0035] Example 2. A production process for melamine glue impregnated veneer, comprising the following steps:

[0036] A. Cutting and trimming the purchased veneer to obtain veneer raw materials;

[0037] B, splicing veneer raw materials into rolls to obtain spliced ​​veneer;

[0038] C. Glue dipping treatment: the spliced ​​veneer is dipped twice to obtain a melamine glue-impregnated veneer; the total amount of glue applied to the spliced ​​veneer is 150% of the weight of the spliced ​​veneer.

[0039] The length and width of the veneer raw material are greater than 1-2cm of the length and width of the plate to be pasted.

[0040] The non-woven tape or adhesive-backed film-coated cloth is cured by hot pressing and pasted on the adjacent veneer by using pressing equipment. The hot pressing temperature is 160°C and the hot pressing time is 15 seconds.

[0041] The width of the non-woven tape or adhesive coated cloth is 2cm, and the length is 1.25m.

[0042] The specific proc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process for impregnating veneer with melamine glue, which comprises the following steps: A. cutting and trimming purchased veneer to obtain veneer raw materials; B. splicing veneer raw materials into rolls to obtain spliced ​​veneer; C. Glue treatment; the spliced ​​veneer is dipped twice to obtain a melamine glue-impregnated veneer; the total amount of glue applied to the spliced ​​veneer is 120-180% of the weight of the spliced ​​veneer. In the present invention, the veneer is soaked twice, and by controlling the glue components and dosage in the dipping pool, the amount of glue applied each time, the total amount of glue applied, and the two drying processes, the melamine is guaranteed The glue can be well attached to the surface of the veneer. After curing, the veneer has good wear resistance, waterproof and flame retardant properties, and has a good pressing effect, which can meet the requirements of the subsequent pressing; it can also reduce the cost of glue . It has the characteristics of improving production efficiency, improving product quality and simplifying the subsequent pressing process.

Description

technical field [0001] The invention relates to a veneer production process, in particular to a production process for impregnating veneer with melamine glue. Background technique [0002] With the decrease of forest resources, the demand for panels is rising sharply. In order to meet the market demand, vinyl panels have begun to appear on the market. In order to make the surface of vinyl panels have good aesthetics, vinyl panels A layer of surface bonding material is adhered to the surface of the board, which is convenient for consumers to choose and purchase. Surface bonding materials currently have three bonding methods: PVC color film + wear-resistant, wood sheet and melamine impregnated paper. Wooden sheet has strong texture and good visual aesthetics, but its wear resistance is very poor. To improve its wear resistance, it must go through various painting processes, which are complicated, and its flame retardancy and waterproof performance are extremely poor. Melamin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27K3/02B27K5/04B27M1/08
CPCB27K3/02B27K3/0207B27K5/04B27M1/08
Inventor 李公浩
Owner 李公浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com