PP calcium plastic material for improving printing suitability for packaging box and preparation method of PP calcium plastic material

A calcium-plastic material and technology for suitability are applied to improve the printing suitability of PP calcium-plastic materials for packaging boxes. In the field of preparation of this material, problems such as poor polar ink adsorption, poor printing tinting strength, and increased production links can be solved. , to achieve the effect of improving grip, printing, and high production efficiency

Inactive Publication Date: 2020-11-17
烟台融晟新材料有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the production of PP calcium-plastic materials for the existing packaging boxes, in order to ensure the rigidity and mechanical properties of the packaging box, the content of polyolefin resin is relatively high; in order to ensure the processing flow performance of the material, various lubricants and additives need to be added; in order to improve the coloring of the product Try to add various polar substances; in order to ensure the dispersibility of the filler, it is necessary to carry out functional treatment on the filler in advance, increase the production process and increase the production cost; because polyolefin resins are mostly non-polar macromolecules, and the lubricant’s Adding it will make the poor adsorption of polar ink when printing the packaging box, resulting in poor printing coloring power, poor adhesion, easy fading of printed products, low temperature ink flow and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PP calcium plastic material for improving printing suitability for packaging box and preparation method of PP calcium plastic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A PP calcium-plastic material for improving printing suitability for packaging boxes, including the following raw materials in parts by mass: 53.5 parts of a mixture of homopolymerized PP resin and copolymerized PP resin with a mass ratio of 1:1, 1.5 parts of LLDPE, and heavy calcium carbonate 45 parts, 1.5 parts of borate multifunctional additives, 0.5 parts of a mixture of anti-aging agent hindered phenolic antioxidant and phosphite antioxidant with a mass ratio of 1:1.

[0032] The preparation method of the above-mentioned PP calcium-plastic material for improving the printing suitability of the packaging box is as follows: weigh each raw material according to the above-mentioned raw material composition, put it into a high-speed blender, and stir at a temperature of 90°C for 35min at a stirring speed of 1600rpm. The obtained blending components were added to a twin-screw extruder for extrusion and granulation. The temperature of each zone was 200°C, 210°C, 220°C, and...

Embodiment 2

[0034] A PP calcium-plastic material for improving printing suitability for packaging boxes, including the following raw materials in parts by mass: 48 parts of a mixture of homopolymerized PP resin and copolymerized PP resin with a mass ratio of 1.5:1, 2 parts of LLDPE, and heavy calcium carbonate 50 parts, 2 parts of borate multifunctional additives, 0.8 parts of a mixture of anti-aging agent hindered phenolic antioxidant and phosphite antioxidant with a mass ratio of 1:1.

[0035] The preparation method of the above-mentioned PP calcium-plastic material for improving the printing suitability of the packaging box is as follows: weigh each raw material according to the above-mentioned raw material composition, put it in a high-speed blender, and stir for 30 minutes at a temperature of 100 ° C. The stirring speed is 1550 rpm. The obtained blended components were added to a twin-screw extruder for extrusion and granulation. The temperature of each zone was 205°C, 215°C, 225°C, a...

Embodiment 3

[0037] A PP calcium-plastic material for improving printing suitability for packaging boxes, including the following raw materials in parts by mass: 47 parts of a mixture of homopolymerized PP resin and copolymerized PP resin with a mass ratio of 1.5:1, 3 parts of LLDPE, and heavy calcium carbonate 50 parts, 2.5 parts of borate multifunctional additives, 0.8 parts of a mixture of anti-aging agent hindered phenolic antioxidant and phosphite antioxidant with a mass ratio of 1:1.

[0038] The preparation method of the above-mentioned PP calcium-plastic material for improving the printing suitability of the packaging box is as follows: weigh each raw material according to the above-mentioned raw material composition, put it into a high-speed blender, and stir for 25 minutes at a temperature of 105 ° C. The stirring speed is 1500 rpm. The obtained blended components were added to a twin-screw extruder for extrusion and granulation. The temperature of each zone was 205°C, 215°C, 225°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a PP calcium plastic material for improving printing suitability for a packaging box body and a preparation method of the PP calcium plastic material. The PP calcium plastic material for improving the printing suitability for the packaging box body is prepared from the following raw materials in parts by mass: 30-60 parts of PP resin, 1-5 parts of PE resin, 40-65 parts of ground calcium carbonate, 1-3 parts of borate multifunctional additive and 0.5-1 part of anti-aging agent. The PP calcium plastic material for improving the printing suitability for the packaging box body is obtained by conducting uniform stirring, conducting granulating by a double-screw extruder and finally conducting extruding and molding by a single screw. According to the PP calcium plastic material for the packaging box body and the preparation method thereof, the formula is simple, printing coloring is obviously improved, and the mechanical property is good; and the preparation method issimple in process, convenient to operate and control, high in production efficiency and low in production cost.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a PP calcium-plastic material for packaging boxes with improved printing suitability, and further relates to a preparation method of the material. Background technique [0002] Calcium-plastic composite materials are high-density polyethylene (HDPE), polypropylene (PP), polyvinyl chloride (PVC) and other thermoplastic resins, adding high-content inorganic fillers such as calcium carbonate, various antioxidants, lubricants, etc. This kind of additive is made by heating, plasticizing, extruding / calendering. Compared with traditional carton packaging materials, the packaging box prepared by using it has the advantages of compression resistance, impact resistance, moisture resistance, recyclability, green environmental protection, etc. be widely used. [0003] With the wide application of calcium-plastic composite materials in the outer packaging of commodities, and the different e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L23/08C08K3/26C08K5/55C08K5/524C08K5/13C08K13/02
CPCC08L23/12C08L23/14C08K2003/265C08L2205/03C08L2205/02
Inventor 王源理刘杰刘本国
Owner 烟台融晟新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com