Additive manufacturing method for copper/steel composite injection mould

A technology of injection mold and additive manufacturing, which is applied in the direction of manufacturing tools, additive processing, plasma welding equipment, etc., can solve the problems of high-strength bonding, copper/steel interface bonding strength is difficult to meet the requirements, etc., and achieve the effect of uniform thickness

Active Publication Date: 2020-09-29
NANJING ENIGMA IND AUTOMATION TECH CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But no matter what 3D printing method is used, to print and manufacture copper / steel composite structure injection molds, it is necessary to solve the problem of high-strength bonding at the interface of copper and steel heterogeneous materials, so that copper and steel can be directly combined by welding during the printing process , the bonding strength of the copper / steel interface is difficult to meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Additive manufacturing method for copper/steel composite injection mould
  • Additive manufacturing method for copper/steel composite injection mould
  • Additive manufacturing method for copper/steel composite injection mould

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The present invention will be further described below in conjunction with accompanying drawing.

[0033] The invention provides a method for additive manufacturing of a copper / steel composite injection mold based on the progressive forming technology of composite plates. The manufacturing process is as follows figure 1 As shown, the high-strength bonding of the copper / steel interface in the copper / steel composite injection mold is achieved, and the profile of the copper / steel interface remains similar to the surface of the mold cavity.

[0034] The invention adopts the copper / steel composite plate whose bonding strength of the copper / steel interface is close to or exceeds that of the copper base material as the original forming material to solve the problem that the copper matrix and the steel reinforcement layer are difficult to form a high-strength interface bond in the manufacture of the copper / steel composite injection mold. The copper / steel composite plate is used ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an additive manufacturing method for a copper / steel composite injection mould. The additive manufacturing method comprises the following steps of preparing a copper / steel composite plate incrementally formed part through an incremental forming method by taking a copper / steel composite plate as raw forming materials, and 3D-printing a copper base blank of the copper / steel composite injection mould by taking a copper layer of the copper / steel composite plate incrementally formed part as a baseplate; and finally 3D-printing a steel strengthened layer of the copper / steel composite injection mould by taking the copper base blank as a steel cladding. According to the additive manufacturing method, a high-strength copper / steel bonding interface of the copper / steel composite plate is transplanted into the copper / steel composite injection mould, and the problem that the copper base is hard to combine with the steel strengthened layer in the composite injection mould is solved; meanwhile, the contour of the copper / steel bonding interface in the copper / steel composite injection mould remains similar to the curved surface of a mould cavity, and the thickness of the steel strengthened layer is uniform; the whole manufacturing process is dieless forming, and the process is simple; and the high-quality and low-cost additive manufacturing of the copper / steel composite injection mould is achieved.

Description

technical field [0001] The invention relates to a mold manufacturing method, in particular to a method for additive manufacturing of a copper / steel composite injection mold. Background technique [0002] In the manufacturing time of a typical injection molded part, the cooling time of the part after plastic injection accounts for about 40%, which means that the cooling time has the greatest impact on the productivity of injection molded parts, and the cooling speed of injection molded parts has become an important performance of modern injection molds At present, the cooling rate is mainly improved by optimizing the mold structure and the cooling channels in the mold. However, due to the poor thermal conductivity of mold steel itself, it is difficult to achieve a high cooling rate for steel injection molds at present, and the increase in production efficiency is limited. At the same time, it is difficult for the existing steel mold to ensure uniform cooling of each part of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K9/173B23K9/32B23K10/02B33Y10/00
CPCB23K9/173B23K9/32B23K10/02B33Y10/00
Inventor 杨宗辉成家林张旭李晓泉
Owner NANJING ENIGMA IND AUTOMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products