Glass and preparation method thereof

A technology of glass and molten glass, which is applied in the field of glass and its preparation, can solve the problems of poor quality of transmission fringes, achieve clear texture, good commercial prospects, and improve the quality of transmission fringes

Inactive Publication Date: 2020-09-15
XINYI GLASS (TIANJIN) CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of this application is to provide a glass and its preparation method, which aims to solve the problem of poor transmission streak quality of existing automotive grade glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] Correspondingly, a kind of preparation method of glass, comprises the following steps:

[0029] S01. Provide glass liquid, glass liquid contains SiO 2 、Al 2 o 3 , CaO, MgO, Na 2 O and Fe 2 o 3 , with SiO 2 The weight is 71.9-72.1 parts, Al 2 o 3 1.25-1.35 parts, CaO 8.65-8.75 parts, MgO 3.35-3.45 parts, Na 2 O is 13.4-13.6 parts, Fe 2 o 3 0.595-0.605 copies;

[0030] S02. Flowing molten glass into a molten metal tank containing molten metal, forming the molten glass on the surface of the molten metal to obtain glass.

[0031] The glass preparation method provided in the embodiment of the present application adjusts the composition and content of the glass liquid, and prepares the glass by using the float process, thereby increasing the softening point temperature and hardening molding temperature of the glass, so that the transmission of the obtained glass The stripes are uniform in light and shade, clear in texture and high in glass quality, which is conduc...

Embodiment 1

[0040] This embodiment provides a kind of green glass original sheet, is made by adopting float process, and its preparation method comprises the following steps:

[0041] 1) forming molten glass, wherein, taking the total weight of the molten glass as 100 parts, the molten glass comprises: SiO 2 72 copies, Al 2 o 3 1.3 parts, CaO 8.7 parts, MgO 3.4 parts, Na 2 O 13.51 parts, K 2 O 0.3 parts, Fe 2 o 3 0.6 parts, SO 3 0.17 parts, TiO 2 0.02 copies;

[0042] 2) A cooling water bag is set in the high temperature zone of the tin tank; then, the molten glass flows into the tin tank containing molten tin metal, so that the molten glass hardens and forms on the surface of the molten tin metal, and then the glass is collected.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of glass preparation, and provides glass and a preparation method thereof. The glass provided by the invention is prepared from SiO2, Al2O3, CaO, MgO, Na2Oand Fe2O3, in terms of 71.9 to 72.1 parts by weight of SiO2, the content of Al2O3 is 1.25 to 1.35 parts, the content of CaO is 8.65 to 8.75 parts, the content of MgO is 3.35 to 3.45 parts, the content of Na2O is 13.4 to 13.6 parts, and the content of Fe2O3 is 0.595 to 0.605 part. The components and the content of the glass are adjusted; the softening point temperature and the hardening forming temperature of the glass are effectively increased under the condition that the original main body performance of the glass is kept unchanged, and the influence of a forming area in a float process on glass transmission stripes is reduced by promoting rapid forming and hardening of the glass, so that the quality of the glass transmission stripes is improved.

Description

technical field [0001] The application belongs to the technical field of glass preparation, and in particular relates to a glass and a preparation method thereof. Background technique [0002] The front windshield of a car is usually produced by sandwiching a layer of film between two original glass sheets with a thickness of 2.1mm. The quality of the original glass sheets used is directly related to the effect of the car glass. The quality of the transmission stripes is It is an inspection standard for judging the quality of automotive grade glass produced by float glass. The detection method of the quality of the transmission stripes is as follows: the direction of the light source and the direction of the glass plane form an angle of 45°, use a point light source to irradiate the glass plate, and project the stripes generated by the transmission onto the screen, and visually measure the brightness and uniformity of the stripes. If the lightness and darkness of the transm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/087C03B18/02C03B18/18
CPCC03C3/087C03B18/02C03B18/18
Inventor 董清世陈领民冯长海谢丽宋清超
Owner XINYI GLASS (TIANJIN) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap