A technology of composition and membrane silk, which is applied in the direction of textiles and papermaking, biochemical fiber treatment, fiber type, etc., can solve the problems of difficult washing and poor anti-firing performance of membrane silk moisturizing composition, and achieve improved moisturizing effect and anti-aging Oxidizing, fast-rinsing effect

Pending Publication Date: 2020-09-04
NINGBO FOTILE KITCHEN WARE CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the defects of difficult washing and poor anti-burning performance of the membrane silk moisturizing composition in the prior art, the present invention provides a membrane silk moisturizing composition, its preparation method and application. The membrane silk moisturizing composition of the present invention has good moisturizing effect , also has antibacterial effect, short flushing time, high production efficiency, low production cost, can be recycled, green and environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Membrane silk moisturizing composition and preparation method and application thereof
  • Membrane silk moisturizing composition and preparation method and application thereof
  • Membrane silk moisturizing composition and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] In the cleaning pool, sodium acetate, water, sodium bisulfite and lauryl dimethyl betaine are prepared in a mass ratio of 5:91.8:0.2:3 at a water temperature of 40°C to prepare a film silk moisturizing composition, specifically as follows Steps: Weigh sodium acetate, water, sodium bisulfite and alkyl dimethyl betaine in proportion; first take a part of pure water and heat it to a constant temperature of 40°C, add sodium acetate and alkyl dimethyl betaine, stir and mix evenly, Then ultrasonicate the sodium bisulfite in an ultrasonic oscillator for 20 minutes, after the sodium bisulfite is evenly dispersed, slowly add it into the mixed solution of sodium acetate, alkyl dimethyl betaine and water, add the remaining pure water and stir evenly , until the solution becomes a transparent and uniform solution, it can be cooled and used.

[0047] Put the entire bundle of membrane filaments into a tank filled with the membrane filament moisturizing composition prepared above, soa...

Embodiment 2

[0053] In the cleaning pool, sodium hyaluronate, water, sodium bisulfite and sodium lauryl sulfate are prepared in a mass ratio of 10:87.7:0.3:2 at a water temperature of 35°C to prepare a film silk moisturizing composition, which specifically includes the following steps : Weigh sodium hyaluronate, water, sodium bisulfite and sodium lauryl sulfate in proportion; first take a part of pure water and heat it to a constant temperature of 40°C, add sodium hyaluronate and sodium lauryl sulfate, stir and mix well , then sonicate the sodium bisulfite in an ultrasonic oscillator for 20 minutes, after the sodium bisulfite is evenly dispersed, slowly add it into the mixed solution of sodium hyaluronate, sodium lauryl sulfate and water, and add the remaining pure water Stir evenly until the solution becomes a transparent and uniform solution, then it can be cooled and used.

[0054] Put the entire bundle of membrane filaments into a tank filled with the membrane filament moisturizing com...

Embodiment 3

[0060] In the cleaning pool, sodium lactate, water, sodium bisulfite and octadecyltrimethylammonium chloride are mixed in a mass ratio of 8:88.9:0.1:3 to prepare a membrane silk moisturizing composition at a water temperature of 30°C, specifically as follows Steps: Weigh sodium lactate, water, sodium bisulfite and octadecyl trimethyl ammonium chloride in proportion; first take a part of pure water and heat it to a constant temperature of 40°C, add sodium lactate and octadecyl trimethyl ammonium chloride, Stir and mix evenly, then ultrasonically ultrasonicate the sodium bisulfite for 20 minutes in an ultrasonic oscillator. After the sodium bisulfite is uniformly dispersed, slowly add it into the mixed solution of sodium lactate, octadecyltrimethylammonium chloride and water, add Stir the remaining pure water evenly until the solution becomes a transparent and uniform solution, then it can be cooled and used.

[0061] Put the entire bundle of membrane filaments into a tank fille...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a membrane silk moisturizing composition and a preparation method and application thereof. The membrane silk moisturizing composition is prepared from following components in percent by mass: 1%-20% of sodium salt humectant, 0.1%-0.5% of sodium hydrogen sulfite, 1%-5% of surfactant and the balance water. The membrane silk moisturizing composition has a good moisturizing effect, meanwhile, has a bacteriostatic effect, has the beneficial effects of being short in flushing time, high in production efficiency and low in production cost when applied to membrane silk production, can be recycled, and is environmentally friendly.

Description

technical field [0001] The invention relates to a membrane silk moisturizing composition, its preparation method and application. Background technique [0002] During the production process of the hollow fiber membrane module, the wet membrane filament needs to be dried, and then the membrane module is cast to ensure the effective curing of the glue. Hollow fiber membranes that have not been treated with humectants are prone to shrinkage of the membrane pores during drying, coupled with the hydrophobicity of the organic polymer material itself, will cause the flux of the membrane module to decrease or even lose flux. In order to solve the above problems, it is usually necessary to add a humectant before the casting of the membrane module to maintain the flux of the membrane module. [0003] Glycerin is the most common humectant at present. It can ensure that the membrane filaments can still maintain a good flux after drying. However, glycerin is sticky, and it is easy to st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/03D06M13/188D06M13/207D06M13/463D06M13/262D06M11/56D06M101/22D06M101/30D06M101/28
CPCD06M11/56D06M13/188D06M13/207D06M13/262D06M13/463D06M15/03D06M16/00D06M2101/22D06M2101/28D06M2101/30
Inventor 龚烨霞陈承王强倪澄峰
Owner NINGBO FOTILE KITCHEN WARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap