Preparation method of double-sided PERC battery

A battery, double-sided technology, applied in the direction of circuits, photovoltaic power generation, electrical components, etc., can solve the problems of affecting the opening voltage and conversion efficiency of the battery, destroying the passivation film, and reducing the conversion efficiency of the front side, so as to improve the open circuit voltage and conversion efficiency , reduce erosion, shorten the effect of reaction time

Pending Publication Date: 2020-06-26
CSI CELLS CO LTD +1
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the double-sided PERC cell due to SiN x The thickness of the film is reduced, and the above-mentioned "burning aluminum platform" will cause part of the paste to burn through SiN x Thin film, destroys the passivation film, and then affects the opening voltage and conversion efficiency of the battery
According to field tests, compared with single-sided PERC cells, the opening voltage Voc of double-sided PERC cells will drop by about 2mV, and the front-side conversion efficiency will also drop by about 0.1%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of double-sided PERC battery
  • Preparation method of double-sided PERC battery
  • Preparation method of double-sided PERC battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be described in detail below with reference to the embodiments shown in the accompanying drawings. However, this embodiment does not limit the present invention, and any structural, method, or functional changes made by those skilled in the art according to this embodiment are included in the protection scope of the present invention.

[0019] The preparation method of the double-sided PERC battery provided by the present invention mainly includes the steps of texturing, diffusion, edge etching and back surface polishing, coating, slotting, printing and sintering. Wherein, the coating step includes sequentially preparing a passivation film and a back anti-reflection film on the back surface of the silicon wafer, and preparing a front anti-reflection film on the front surface of the silicon wafer; the slotting step includes opening electrodes on the passivation film and the back anti-reflection film Opening; the printing step includes printing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a double-sided PERC battery, and the method comprises the steps of film coating, slotting, printing and sintering in sequence; the sintering step comprises a drying stage, a first heating stage, a second heating stage and a third heating stage; the initial temperature of the second heating stage is 480-520 DEG C, the final temperature of the second heating stage is 550-580 DEG C, and the heating rate of the second heating stage is set to be 7-25 DEG C / s. According to the preparation method provided by the invention, a relatively slow temperature rise interval is arranged, so the formation of an aluminum back surface field BSF is facilitated, the aluminum burning reaction time is reasonably shortened, the erosion of back electrode aluminum paste is reduced, and the open-circuit voltage and the conversion efficiency of the double-sided PERC battery are improved.

Description

technical field [0001] The invention relates to the technical field of photovoltaic production, in particular to a preparation method of a double-sided PERC battery. Background technique [0002] Solar energy is a clean and sustainable energy source with great potential. In recent years, the number of photovoltaic power stations invested and operated at home and abroad has increased year by year. With the rapid development of photovoltaic technology, the market has become increasingly concerned about the performance and conversion efficiency of solar cells and components. put forward higher requirements. Among them, the PERC (Passivated Emitter and Rear Cell) battery can greatly reduce the recombination speed of the back surface by setting a passivation film on the back surface. It is a high-efficiency battery that is widely concerned in the industry. [0003] Generally, the passivation film on the back of the PERC cell can be made of aluminum oxide or silicon oxide film, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L31/18H01L31/0224H01L31/068
CPCH01L31/1804H01L31/1868H01L31/022441H01L31/0684Y02E10/547Y02P70/50
Inventor 李兵刘运宇陈瑶邓伟伟
Owner CSI CELLS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com