Production method and device of butyl rubber

A technology of butyl rubber and production methods, applied in chemical instruments and methods, chemical/physical/physical chemical processes, chemical/physical processes, etc., can solve problems such as low production efficiency, achieve high production efficiency, and increase slurry concentration , the effect of high slurry concentration

Active Publication Date: 2021-03-02
ZHEJIANG CENWAY MATERIALS CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because this method adopts air flotation separation, the colloidal particles in the slurry can be separated at low temperature; but because the content of colloidal particles in the slurry is not high, about 30wt%, this method still has the problem of low production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method and device of butyl rubber
  • Production method and device of butyl rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0048] This specific embodiment is only an explanation of the present invention, not a limitation of the present invention. Changes made by those skilled in the art after reading the description of the present invention, as long as they are within the scope of the claims, will be subject to the patent law. Protect.

[0049] Such as figure 1 Shown, the production device of butyl rubber comprises reactor 1, degassing kettle 2, stripping kettle 3, colloidal water storage tank 4 and primary dehydration equipment 5 connected in series successively; The bottom outlet of reactor 1 is connected with the described The feed port of the degassing kettle 2 is connected,

[0050] The outlet at the bottom of the degassing still 2 is connected with the feed port of the stripping still 3; the outlet at the bottom of the stripping still 3 is connected with the feed port of the colloidal water storage tank 4;

[0051] The production device also includes a hot water storage tank 6 and secondar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of high single concentration and high conversion rate of butyl rubber, which belongs to the technical field of rubber production. The method comprises the following steps: a, catalyst and solvent, enter the polymerization reactor from the first passage; b, isoprene monomer, isobutylene monomer and slurry stabilizer, enter the polymerization reactor from the second passage; c, Polymerize in the polymerization reactor to form a butyl rubber suspension; d, make the butyl rubber glue flow into the degassing kettle from the polymerization reactor, and at the same time pass steam and hot water into the suspension; e, degassing still treatment; f, stripping still treatment; g, vibrating dehydration screen treatment, and then through subsequent treatment to obtain butyl rubber. The present invention has adopted polymerization stabilizer and supporting technology, makes the present invention produce the chloromethane slurry containing butyl rubber colloid in production process, and the butyl rubber colloid content in the slurry reaches more than 40wt%; Obviously exceeds 30wt% in the prior art; so that the method of the present invention has the characteristics of high slurry concentration and stability.

Description

technical field [0001] The invention relates to a production method of high single concentration and high conversion rate of butyl rubber, which belongs to the technical field of rubber production. Background technique [0002] Butyl rubber has good chemical stability and thermal stability, and has good air and water tightness. Widely used in the production and manufacture of automobile tires, bladders, sealing rings, etc. [0003] "Butyl rubber" refers to a copolymer composed of C4-C7 isoolefin and C4-C14 conjugated diene, containing about 0.5~15mol% conjugated diene and 85~99.5mol% isoolefin. The isoolefins from which butyl rubber can be prepared are isobutylene 2-methyl-1-propene, 3-methyl-1-butene, 4-methyl-1-pentene and pinene, preferably isobutylene; conjugated diene Can be isoprene, butadiene, 2,3-dimethylbutadiene, piperylene, 2,5-dimethylhexa2,4-diene, cyclopentadiene, cyclohexadiene alkenes and methylcyclopentadiene, preferably isoprene. The viscosity average m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F210/12C08F236/08C08F2/38B01J19/00
CPCB01J19/0006C08F2/38C08F210/12C08F236/08
Inventor 任纪文代俊明朱德权张晓玲邱正茂
Owner ZHEJIANG CENWAY MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com