Biodegradable insect trapping plate and preparation method thereof

A biodegradable and insect trapping technology, which is applied to devices for capturing or killing insects, animal husbandry, and applications, etc., can solve the problems of polluted environment, non-degradable insect trapping plates, and inconvenient field cleaning, etc. Conducive to the effect of promotion and expansion of use

Inactive Publication Date: 2020-05-19
SHANGHAI CHANGFA NEW MATERIAL CO LTD
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The base material used in the existing insect trap board is PP or PVC derived from the petrochemical industry. Hang it in the use area; when using it to kill pests, it can avoid pesticide pollution to the environment, but it is mainly made of PP plastic, which is not easy to degrade. The discarded insect traps will still pollute the environment because they are not easy to degrade. It has caused serious secondary pollution to the agricultural ecological environment, and the follow-up treatment is extremely troublesome, which has brought inconvenience to field cleaning; in recent years, the existing insect traps have been used more and more widely, and the number of uses has also increased year by year, causing damage to the agricultural ecological environment more serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A biodegradable insect trap, the insect trap includes the following components in parts by weight: 70 parts of PBAT, 10 parts of PLA, 10 parts of wood cellulose, 10 parts of cornstarch, 3 parts of biodegradable yellow mother, 1 part of DCP , 6 parts of glycerin and 1 part of stearic acid.

[0026] The preparation method of the above-mentioned biodegradable insect trap comprises the following steps:

[0027] S1: Mix the above-mentioned wood cellulose, corn starch, DCP, glycerin, stearic acid, PBAT, PLA and biodegradable yellow masterbatch uniformly according to the proportion to obtain the primary mixture;

[0028] S2: Put the primary mixture prepared in step S1 into the silo of the twin-screw extruder, extrude and granulate. ℃, the head temperature is 190 ℃, the screw speed is 200rpm, the masterbatch is prepared, the masterbatch is added to the sheet extruder, extruded and cut, and the biodegradable insect trap substrate is obtained. The mechanical properties are as fo...

Embodiment 2

[0032] A biodegradable insect trap, the insect trap includes the following components by weight: 40 parts of PBAT, 10 parts of PLA, 40 parts of wood cellulose, 10 parts of cornstarch, 3 parts of biodegradable yellow mother, 1 part of DCP , 6 parts of epoxidized soybean oil and 1 part of calcium stearate.

[0033] The preparation method of the above-mentioned biodegradable insect trap comprises the following steps:

[0034] S1: Mix the above-mentioned wood cellulose, corn starch, DCP, epoxidized soybean oil, calcium stearate, PBAT, PLA and biodegradable yellow masterbatch evenly according to the proportion to obtain the primary mixture;

[0035] S2: Put the primary mixture prepared in step S1 into the silo of the twin-screw extruder, extrude and granulate. ℃, the head temperature is 150℃, the screw speed is 300rpm, and the masterbatch is prepared, and the masterbatch is added to the sheet extruder, extruded and cut, and the biodegradable insect trap substrate is obtained. The ...

Embodiment 3

[0039] A biodegradable insect trap, the insect trap includes the following components by weight: 40 parts of PBAT, 40 parts of PLA, 10 parts of cotton fiber, 10 parts of corn starch, 3 parts of biodegradable yellow mother, 1 part of DCP, 6 parts of glycerin and 1 part of calcium stearate.

[0040] The preparation method of the above-mentioned biodegradable insect trap comprises the following steps:

[0041] S1: Mix the above-mentioned cotton fiber, corn starch, DCP, glycerin, calcium stearate, PBAT, PLA and biodegradable yellow masterbatch uniformly according to the proportion to obtain the primary mixture;

[0042] S2: Put the primary mixture prepared in step S1 into the silo of the twin-screw extruder, extrude and granulate. ℃, the head temperature is 170 ℃, the screw speed is 200rpm, the masterbatch is prepared, the masterbatch is added to the sheet extruder, extruded and cut, and the biodegradable insect trap substrate is obtained. The mechanical properties are as follows...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a biodegradable insect trapping plate and a preparation method thereof. The insect trapping plate comprises the following components in parts by weight: 40-70 parts of PBAT, 10-40 parts of PLA, 10-40 parts of cellulose, 10-20 parts of starch, 1-15 parts of biodegradable color masterbatch / toner and 2-15 parts of an auxiliary agent. The cellulose and the starch are added intothe biodegradable resin, so that the cost of the biodegradable insect trapping plate is greatly reduced, the popularization is facilitated, the application of the cellulose is expanded, and the economic benefits of the cellulose and the starch are improved; in addition, the biodegradable insect trapping plate can be completely degraded by microorganisms in the nature, finally carbon dioxide, water and minerals are generated, and the environment is not polluted.

Description

technical field [0001] The invention relates to the technical field of agricultural and forestry pest control, in particular to a biodegradable insect trap and a preparation method thereof. Background technique [0002] Small pests such as thrips, whitefly, aphids, and Liriomyza sativae have always been the main pests on vegetables, flowers, and important economic crops. Their tiny individuals, fast reproduction speed, hidden activities, and wide host range are extremely harmful to crops. As an important physical pest control product, the insect trap has been widely used in the monitoring and control of pests in the production of vegetables, flowers, and forest fruits following the concept of green, safe and environmentally friendly plant protection; It effectively reduces the use of chemical pesticides, delays the development of pest resistance, reduces pesticide residues in the environment and in fruits and vegetables, and improves food quality and quality. [0003] The b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L67/04C08L1/02C08L3/02C08L97/02A01M1/14A01M1/02
CPCA01M1/02A01M1/14C08L67/02C08L67/04C08L2201/06C08L2205/035C08L2205/16C08L1/02C08L3/02C08L97/02
Inventor 施晓旦郝鲁峰金霞朝
Owner SHANGHAI CHANGFA NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap