A preparation method of high-strength 2000 series aluminum alloy based on selective laser melting forming technology

A laser melting and high-strength technology, which is applied in the direction of improving process efficiency, additive manufacturing, and improving energy efficiency, can solve problems such as limiting industrial applications, poor weldability, and alloys that are prone to thermal cracks, so as to improve the effect of solid solution strengthening , high density, and the effect of improving strength

Active Publication Date: 2021-08-24
CENT SOUTH UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large distance between the liquidus line and the solidus line, the weldability is poor, resulting in hot cracks in the alloy, which greatly limits the further industrial application of this series of alloys.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of high-strength 2000 series aluminum alloy based on selective laser melting forming technology
  • A preparation method of high-strength 2000 series aluminum alloy based on selective laser melting forming technology
  • A preparation method of high-strength 2000 series aluminum alloy based on selective laser melting forming technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027]Prepare the high-strength 2000-series aluminum composite components for 3D printing in the present invention, in terms of mass percentage: Cu: 5.0%, Li: 0.5%, Mg: 0.2%, Zr: 1%, Ti: 0.5%, and the balance for Al. The preparation method of the above-mentioned aluminum alloy powder is as follows: (1) raw material smelting, each element is weighed in proportion to the pure metal block raw material and placed in a vacuum induction furnace for heating and melting; (2) atomization powder making, the above-mentioned pre-alloyed metal after melting Transfer to the atomization tank, use helium to atomize and make powder; (3) Powder sieving: The above-mentioned pre-alloyed metal powder is screened to obtain a metal powder with an average particle size of 38 μm, and the particle size range is 11 μm ~68 μm. (4) Heat preservation and drying: put the above-mentioned sieved powder into a drying oven, heat preservation time is 12 hours, and heat preservation temperature is 95°C.

[0028...

Embodiment 2

[0031] Prepare the high-strength 2000 series aluminum composite components for 3D printing in the present invention, in terms of mass percentage: Cu: 3.5%, Li: 0.5%, Mg: 0.5%, Zr: 2%, Ti: 0.8%, and the balance for Al. The preparation method of the above-mentioned aluminum alloy powder is as follows: (1) raw material smelting, each element is weighed in proportion to the pure metal block raw material and placed in a vacuum induction furnace for heating and melting; (2) atomization powder making, the above-mentioned pre-alloyed metal after melting Transfer to the atomization tank, use helium to atomize and make powder; (3) Powder sieving: The above-mentioned pre-alloyed metal powder is screened to obtain a metal powder with an average particle size of 38 μm, and the particle size range is 11 μm ~68 μm. (4) Heat preservation and drying: put the above-mentioned sieved powder into a drying oven, heat preservation time is 12 hours, and heat preservation temperature is 95°C.

[003...

Embodiment 3

[0035] Prepare the high-strength 2000-series aluminum composite components for 3D printing in the present invention, in terms of mass percentage: Cu: 4%, Li: 0.7%, Mg: 1%, Zr: 1.5%, Ti: 0.7%, and the balance for Al. The preparation method of the above-mentioned aluminum alloy powder is as follows: (1) raw material smelting, each element is weighed in proportion to the pure metal block raw material and placed in a vacuum induction furnace for heating and melting; (2) atomization powder making, the above-mentioned pre-alloyed metal after melting Transfer to the atomization tank, use helium to atomize and make powder; (3) Powder sieving: The above-mentioned pre-alloyed metal powder is screened to obtain a metal powder with an average particle size of 38 μm, and the particle size range is 11 μm ~68 μm. (4) Heat preservation and drying: put the above-mentioned sieved powder into a drying oven, heat preservation time is 12 hours, and heat preservation temperature is 95°C.

[0036]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing high-strength 2000-series aluminum alloys based on selective laser melting technology; wherein, a method for preparing high-strength 2000-series aluminum alloys based on selective laser melting technology includes: weighing raw materials for Melting; sieving after atomization powder making; heat preservation treatment to obtain metal powder; 3D printing with the metal powder; reheat treatment to obtain high-strength 2000 series aluminum alloy products; in terms of mass percentage, the composition and The content is Cu: 2-8%, Li: 0.5-2%, Mg: 0.2-2%, Zr: 1-3%, Ti: 0.4-1.8%, and the balance is Al. The present invention optimizes the traditional 2000-series aluminum composition, has low cost, forms solid solution strengthening, dispersion strengthening, and fine-grain strengthening, improves the strength of aluminum alloys, and develops 3D printing Al-Cu-Li alloy powders, and its printed parts After heat treatment, the mechanical properties are excellent.

Description

technical field [0001] The invention belongs to the technical field of selective laser melting forming, and in particular relates to a preparation method of high-strength 2000 series aluminum alloy based on selective laser melting forming technology. Background technique [0002] Metal-based additive manufacturing, also known as 3D printing (the two processes of special laser selective melting and laser melting deposition in this patent), is a potentially disruptive technology across multiple industries, including aerospace, biomedical and automotive industry. This is due to: First, 3D printing builds metal parts layer by layer, increasing design freedom and manufacturing flexibility, enabling complex geometries. This layered method has unique advantages in the integrated molding of complex structures and thin-walled components, eliminating the need for welding and riveting processes, no molds, shortening the design and production time, promoting customized development of p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/16C22F1/057B22F3/105B22F10/28B33Y10/00B33Y70/00
CPCC22C21/16C22F1/057B33Y10/00B33Y70/00B22F10/00B22F10/34B22F10/36B22F10/28B22F10/64B22F10/366Y02P10/25
Inventor 李瑞迪徐荣袁铁锤
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap