Breathable anti-hollowing ceramic tile back adhesive and preparation method thereof

A breathable, ceramic tile technology, applied in the direction of adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve the problems of tiles falling off, tile hollowing, etc., to prevent tiles from hollowing, hardening The effect of scope promotion

Inactive Publication Date: 2020-05-15
GUANGDONG ORIENT RESIN
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When laying tiles, the common way of laying tiles is to use cement to lay tiles. The cement has a high viscosity and can firmly stick the tiles on the wall. However, after the cement dries, the tiles are likely to become hollow and cause the tiles to fall off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A breathable air-proof drum tile adhesive, comprising the following raw materials: 10g of dimethylaminoethyl methacrylate, 1g of carbon nanotubes, 2g of allyl pyrrolidine dithiocarbamate, 1g of Tween 80, and 1g of N-methyl 4g of pyrrolidone, 40g of aqueous epoxy resin emulsion, 10g of styrene, 10g of acrylamide, and 15g of deionized water.

[0017] A preparation method of air-permeable anti-aircraft drum ceramic tile adhesive, comprising the following steps: (1) weighing each component raw material, for later use; (2) putting acrylamide, dimethylaminoethyl methacrylate, and styrene into a dispersing machine disperse for 3 minutes to obtain mixed liquid A; (3) after mixing allyl pyrrolidine dithiocarbamate, N-methylpyrrolidone, and water-based epoxy resin emulsion, heat it in a water bath to 40 ° C, and at this temperature Open and stir for 2 minutes to obtain a mixed solution B; (4) mix Tween 80, carbon nanotubes, and deionized water together, and oscillate with microwa...

Embodiment 2

[0019] A breathable air-proof drum tile adhesive, including the following raw materials: dimethylaminoethyl methacrylate 30g, carbon nanotubes 5g, allyl pyrrolidine dithiocarbamate 8g, Tween 80 6g, N-methyl Pyrrolidone 8g, water-based epoxy resin emulsion 80g, styrene 20g, acrylamide 20g, deionized water 30g.

[0020] A preparation method of air-permeable anti-aircraft drum ceramic tile adhesive, comprising the following steps: (1) weighing each component raw material, for later use; (2) putting acrylamide, dimethylaminoethyl methacrylate, and styrene into a dispersing machine (3) After mixing allyl pyrrolidinedithiocarbamate, N-methylpyrrolidone, and water-based epoxy resin emulsion, heat it in a water bath to 50°C, and at this temperature Open and stir for 4 minutes to obtain a mixed solution B; (4) mix Tween 80, carbon nanotubes, and deionized water together, and oscillate in a microwave for 10 minutes to obtain a mixed solution C; (5) mix the mixed solution A, mixed soluti...

Embodiment 3

[0022] A breathable air-proof drum tile adhesive, including the following raw materials: dimethylaminoethyl methacrylate 15g, carbon nanotubes 2g, allyl pyrrolidine dithiocarbamate 3g, Tween 80 2g, N-methyl Pyrrolidone 5g, water-based epoxy resin emulsion 45g, styrene 12g, acrylamide 12g, deionized water 18g.

[0023] A preparation method of air-permeable anti-aircraft drum ceramic tile adhesive, comprising the following steps: (1) weighing each component raw material, for later use; (2) putting acrylamide, dimethylaminoethyl methacrylate, and styrene into a dispersing machine disperse for 4 minutes to obtain mixed liquid A; (3) after mixing allyl pyrrolidinedithiocarbamate, N-methylpyrrolidone, and water-based epoxy resin emulsion, heat it in a water bath to 45°C, and at this temperature Open and stir for 3 minutes to obtain a mixed solution B; (4) mix Tween 80, carbon nanotubes, and deionized water together, and oscillate in a microwave for 8 minutes to obtain a mixed soluti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an air-permeable anti-hollowing ceramic tile back adhesive and a preparation method thereof. The air-permeable anti-hollowing ceramic tile back adhesive is prepared from, by weight, 10-30 parts of dimethylaminoethyl methacrylate, 1-5 parts of carbon nanotubes, 2-8 parts of allyl pyrrolidine dithiocarbamate, 1-6 parts of Tween 80, 4-8 parts of N-methyl-2-pyrrolidone, 40-80 parts of a waterborne epoxy resin emulsion, 10-20 parts of styrene, 10-20 parts of acrylamide and 15-30 parts of deionized water. The preparation method is simple, easy to operate and convenient to promote in a large range, and the breathable anti-hollowing ceramic tile back adhesive prepared by the method is simple and convenient to construct, can be smeared on the back surface of a ceramic tile,is firm in adhesion, good in breathability and small in hardening shrinkage, and can effectively prevent hollowing of the ceramic tile.

Description

technical field [0001] The invention specifically relates to the technical field of chemical industry, in particular to a breathable anti-aircraft drum tile back glue and a preparation method thereof. Background technique [0002] Ceramic tile is a kind of acid and alkali-resistant porcelain or stone, construction or decoration materials formed by grinding, mixing, pressing, glazing and sintering of refractory metal oxides and semi-metal oxides. It's tiles. Its raw materials are mostly mixed with clay, quartz sand and so on. [0003] When laying tiles, the common way of laying tiles is to use cement to lay tiles. The cement has a high viscosity and can firmly stick the tiles on the wall. However, after the cement dries, the tiles are likely to become hollow and cause the tiles to fall off. . Contents of the invention [0004] The object of the present invention is to provide a ventilating anti-aircraft drum tile adhesive and its preparation method, so as to solve the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J4/02C09J4/06C09J11/04
CPCC09J4/06C09J11/04
Inventor 张炜祺
Owner GUANGDONG ORIENT RESIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com