Multifunctional polysiloxane thermoplastic elastomer as well as preparation method and application thereof

A thermoplastic elastomer and polysiloxane technology, which is applied in the field of thermoplastic elastomers, can solve the problems that composite materials do not have reproducible processability, the content of polysiloxane in composite materials cannot be too high, and resources are wasted. Effects of thermo-induced shape memory function, fast shape recovery rate, high shape fixation rate

Active Publication Date: 2020-05-15
SOUTH CHINA UNIV OF TECH
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the content of polysiloxane in the composite material prepared by this method should not be too high; secondly, the composite material does not have reproducibility, resulting in a waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional polysiloxane thermoplastic elastomer as well as preparation method and application thereof
  • Multifunctional polysiloxane thermoplastic elastomer as well as preparation method and application thereof
  • Multifunctional polysiloxane thermoplastic elastomer as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) Add 127.55g of octamethylcyclotetrasiloxane (0.43mol), 24.85g of 1,3-bis(3-aminopropyl) to a round bottom flask connected with mechanical stirring, reflux condenser and inert protection device - 0.12 g of 1,1,3,3-tetramethyldisiloxane (0.1 mol) and catalyst tetramethylammonium hydroxide (25% methanol solution). Raise the reaction temperature to 80°C and react for 10h under the protection of nitrogen; then raise the temperature to 150°C and react for 1.2h to decompose the catalyst to obtain a crude product; finally, distill under reduced pressure in a rotary evaporator at 150°C for 2h to remove small molecular substances , to obtain a colorless and transparent double-terminated aminopolysiloxane named APPS-1500.

[0040] (2) Add 3.71g of 3,3',4,4'-biphenyltetracarboxylic dianhydride (12.6mmol) in a double-necked round-bottomed flask equipped with a constant pressure dropping funnel and an inert protection device. 1,3-bis(3-aminopropyl)-1,1,3, The o-dichlorobenzene ...

Embodiment 2

[0043] In addition to 3,3',4,4'-biphenyltetracarboxylic dianhydride, APPS-1500 and 1,3-bis(3-aminopropyl)-1,1,3,3-tetramethyl The feeding molar ratio of disiloxane is 17.8:10:7, the temperature of hot pressing in step 3 is 90°C, and the rest are the same as in Example 1.

Embodiment 3

[0045] In addition to 3,3',4,4'-biphenyltetracarboxylic dianhydride, APPS-1500 and 1,3-bis(3-aminopropyl)-1,1,3,3-tetramethyl The feeding molar ratio of disiloxane is 23.1:10:12, the temperature of hot pressing in step 3 is 100°C, and the rest are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multifunctional polysiloxane thermoplastic elastomer as well as a preparation method and application thereof. The elastomer is prepared by the following method: taking 1,3-bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane and octamethylcyclotetrasiloxane as raw materials, and carrying out a reaction under the action of a catalyst tetramethylammonium hydroxide pentahydrate,so as to obtain double amino-terminated polysiloxane; with double amino-terminated polysiloxane, 3,3',4,4'-biphenyl tetracarboxylic dianhydride and 1,3-bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane as raw materials, and carrying out a reaction to obtain a polysiloxane-polyamic acid segmented copolymer; and finally, under the action of high temperature, obtaining the polysiloxane-polyimide block polymer with high mechanical properties, a shape memory function and a self-healing function.

Description

technical field [0001] The present invention relates to a thermoplastic elastomer, in particular to a polysiloxane thermoplastic elastomer with high mechanical properties and multifunctionality and a preparation method thereof. The thermoplastic elastomer of the present invention is an intelligent polymer material. The present invention also It relates to the application of polysiloxane thermoplastic elastomer in biomedical devices. Background technique [0002] As a smart material with stimulus-response function, shape memory material can respond to external stimuli (such as temperature, light, electric field and magnetic field, etc.), adjust its own shape, and return to its preset shape. s material. Shape memory polymers have the advantages of low response temperature and fast response speed, and have broad application prospects in aerospace industry, intelligent biomedical equipment, sensors and other fields. The realization of the polymer shape memory function needs to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G77/455C08G73/10C08L83/10
CPCC08G73/1007C08G73/106C08G73/1082C08G77/455C08L83/10
Inventor 陈玉坤范剑锋
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com