Camouflage reinforced space cloth and preparation method thereof

A reinforced, camouflage technology, applied in the field of textile materials, can solve the problems that the pattern is easily worn or scratched, affecting the appearance of the space cloth, and achieves the effects of good peel strength, improved deformation, and less ink usage.

Pending Publication Date: 2020-04-21
FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, the mask layer is pasted on both sides of the brushed cloth. Since the space cloth is mostly used for air cushion products, in order to prevent the mask layer from leaking, the mask layer of the space cloth requires higher strength; in order to improve the ornamental value of the br

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The invention provides a method for preparing a camouflage reinforced space cloth, wherein the camouflage reinforced space cloth comprises PVC camouflage clip mesh cloth, space cloth and PVC clip mesh cloth bonded sequentially from top to bottom;

[0015] The PVC camouflage sandwich cloth layer includes a printed transparent PVC film, a first sandwich cloth layer and a transparent PVC film laminated sequentially from top to bottom; the printed transparent PVC film is: a transparent film with a pattern printed on the lower surface PVC film, the distribution area of ​​the pattern on the printed transparent PVC film is 10-30% of the area of ​​the printed transparent PVC film; the first sandwich layer is made of polyester fiber mesh cloth impregnated with colored paste made after coating;

[0016] The PVC mesh cloth includes a transparent PVC film, a second mesh cloth layer and a transparent PVC film laminated sequentially from top to bottom; Prepared after dip coating.

...

Embodiment 1

[0028] A camouflage reinforced space cloth, the camouflage reinforced space cloth comprises PVC camouflage sandwich cloth, space cloth and PVC sandwich cloth bonded sequentially from top to bottom;

[0029] The PVC camouflage sandwich cloth layer includes a printed transparent PVC film, a first sandwich cloth layer and a transparent PVC film laminated sequentially from top to bottom; the printed transparent PVC film is: a transparent film with a pattern printed on the lower surface PVC film, the distribution area of ​​the pattern on the printed transparent PVC film is 10% of the area of ​​the printed transparent PVC film;

[0030] The colored paste is composed of the following raw materials in parts by weight: 100 parts of PVC paste resin; 60 parts of DINP; 5 parts of heavy calcium carbonate; 3 parts of carboxylated nitrile rubber; 3 parts of chlorinated polyethylene; 2 parts of barium zinc stabilizer; Polyisocyanurate 3 parts and Phthalocyanine blue: 2 parts.

[0031] The PV...

Embodiment 2

[0036] A camouflage reinforced space cloth, the camouflage reinforced space cloth comprises PVC camouflage sandwich cloth, space cloth and PVC sandwich cloth bonded sequentially from top to bottom;

[0037] The PVC camouflage sandwich cloth layer includes a printed transparent PVC film, a first sandwich cloth layer and a transparent PVC film laminated sequentially from top to bottom; the printed transparent PVC film is: a transparent film with a pattern printed on the lower surface PVC film, the distribution area of ​​the pattern on the printed transparent PVC film is 20% of the area of ​​the printed transparent PVC film; the colored paste is composed of the following raw materials in parts by weight: the colored paste is composed of the following raw materials in parts by weight : 100 parts of PVC paste resin; 70 parts of DINP; 7 parts of heavy calcium carbonate; 4 parts of carboxylated nitrile rubber; 4 parts of chlorinated polyethylene; 3 parts of barium zinc stabilizer; 4 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of textile materials, in particular to camouflage reinforced space cloth and a preparation method thereof. The camouflage reinforced space cloth comprisesPVC camouflage netted sandwich cloth, space cloth and PVC netted sandwich cloth which are sequentially bonded from top to bottom; the PVC camouflage netted sandwich cloth layer comprises a printed transparent PVC film, a first netted sandwich cloth layer and a transparent PVC film which are sequentially laminated from top to bottom; the printed transparent PVC film is a transparent PVC film with apattern printed on the lower surface, and the distribution area of the pattern on the printed transparent PVC film is 10-30% of the area of the printed transparent PVC film; and the first netted sandwich cloth layer is prepared by performing dip coating on polyester fiber mesh cloth by using colored paste. The PVC camouflage sandwich screen cloth has the beneficial effects that the PVC camouflagesandwich screen cloth is additionally arranged on the surface of the space cloth, so the pattern of the space cloth is not prone to abrasion, and strength is higher.

Description

technical field [0001] The invention relates to the technical field of textile materials, in particular to a camouflage reinforced space cloth and a preparation method thereof. Background technique [0002] At present, space cloth composite materials have been widely used in various fields, such as being used as a waterproof membrane on the wall or bottom of a swimming pool, as a material for kayaking, or as an air cushion film for various air cushion products, etc. [0003] In order to improve the wear resistance and strength of the space cloth, it can withstand greater external force and increase the service life of the product. Usually, the mask layer is pasted on both sides of the brushed cloth. Since the space cloth is mostly used for air cushion products, in order to prevent the mask layer from leaking, the mask layer of the space cloth requires higher strength; in order to improve the ornamental value of the brushed cloth surface, often Patterns are screen-printed or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/02B32B27/06B32B27/12B32B27/30B32B33/00
CPCB32B5/02B32B33/00B32B2262/0238
Inventor 林生雄何超金廖八生吴星星
Owner FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap