Low-freezing-point wetting type dust suppressant and preparation method thereof

A technology of dust suppressant and freezing point, which is applied in the field of low freezing point wetting dust suppressant and its preparation, can solve problems such as relatively large impact, achieve the effects of reducing water loss, improving dust suppression effect, and strengthening anti-destructive effect

Active Publication Date: 2020-04-10
ANSTEEL GRP MINING CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as a kind of salt, calcium chloride has obvious acidity in its aqueous solution, which has a great impact on the environment. Therefore, the existing antifreeze dust suppressant needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-freezing-point wetting type dust suppressant and preparation method thereof
  • Low-freezing-point wetting type dust suppressant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] This embodiment provides a low freezing point wetting dust suppressant, which consists of the following components in parts by mass:

[0041] Sodium Lactate: 0.3%, Polypropylene Alcohol: 0.9%, Epoxy Resin: 0.2%, Glycerin: 5%, Methyl Cellulose: 1%, Sodium Dodecyl Benzene Sulfonate: 0.4%, Styrene Acrylic Emulsion: 0.3% , Water: 91.9%.

[0042] The preparation method of the present embodiment dust suppressant comprises the steps:

[0043] (1) Divide water into two parts A, B, A541g, B378g, A is heated to 60°C, B is heated to 40°C;

[0044] (2) Stir 4g of sodium dodecylbenzenesulfonate, 9g of polyacryl alcohol, 10g of methyl cellulose, and 2g of epoxy resin evenly, then add part A of water, stir for 30min at a rotational speed of 100rpm / min, and then cool to room temperature. Obtain the aqueous solution a;

[0045] (3) Add 3 g of sodium lactate, 50 g of glycerin, and 3 g of styrene-acrylic emulsion into the water of part B, and stir for 30 min at a rotational speed of 10...

Embodiment 2

[0059] This embodiment provides a low freezing point wetting dust suppressant, which consists of the following components in parts by mass:

[0060] Sodium lactate: 0.5%, polyacryl alcohol: 1%, epoxy resin: 0.4%, glycerin: 8%, xanthan gum: 1%, polyacrylamide: 0.5%, fatty alcohol polyoxyethylene alcohol ether: 0.4%, pure Acrylic emulsion: 0.3%, water: 87.9%.

[0061] The preparation method of the present embodiment dust suppressant comprises the steps:

[0062] (1) Divide water into two parts A and B, A475g and B378g, A is heated to 65°C, B is heated to 45°C;

[0063] (2) Stir 4g of fatty alcohol polyoxyethylene alcohol ether, 10g of polypropylene alcohol, 10g of xanthan gum, 5g of polyacrylamide, and 4g of epoxy resin evenly, then add part A of water, stir at 150rpm / min for 25min and then cool to room temperature to obtain aqueous solution a;

[0064] (3) Add 5 g of sodium lactate, 80 g of glycerin, and 3 g of pure acrylic emulsion into part B water, and stir for 25 min at ...

Embodiment 3

[0068] This embodiment provides a low freezing point wetting dust suppressant, which consists of the following components in parts by mass:

[0069] Sodium Lactate: 0.3%, Polypropylene Alcohol: 0.9%, Epoxy Resin: 0.2%, Glycerin: 0.5%, Hydroxymethyl Cellulose: 1%, Sodium Dodecyl Benzene Sulfonate: 0.4%, Styrene Acrylic Emulsion: 0.3 %, water: 96.4%.

[0070] The preparation method of the present embodiment dust suppressant comprises the steps:

[0071] (1) Divide the water into two parts A and B, A:B is 1:1, A482g, B482g, A is heated to 70°C, B is heated to 50°C;

[0072] (2) Stir 4g of sodium dodecylbenzenesulfonate, 9g of polypropylene alcohol, 10g of xanthan gum, 10g of binder, and 2g of epoxy resin evenly, then add part A of water, and stir for 20min at a speed of 200rpm / min Cool to room temperature to obtain aqueous solution a;

[0073] (3) Add 3 g of sodium lactate, 5 g of glycerin, and 3 g of pure acrylic emulsion into part B water, and stir for 20 min at a rotation s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention aims to further improve the dust suppression performance of an anti-freezing dust suppressant, provides a low-freezing-point wetting type dust suppressant and a preparation method thereof, and belongs to the technical field of dust suppressants. The dust suppressant is prepared from the following raw material components in percentage by mass: 0.1 to 2% of sodium lactate, 0.1 to 6% ofpolypropylene glycol, 2 to 10% of glycerol, 0.1 to 5% of an adhesive, 0.2 to 2% of epoxy resin, 0.1 to 1% of a surfactant, 0.1 to 3% of an emulsion and the balance water. The dust suppressant is reasonable in price, convenient to popularize and use, wide in raw material source and easy to implement, and has the characteristics of being non-toxic, tasteless, non-corrosive, easy to spray and the like. The dust suppressant can be used for dust suppression of exposed places such as mine roads, urban roads, municipal construction, coal mine transportation and storage yards.

Description

technical field [0001] The invention belongs to the technical field of dust suppressants, and in particular relates to a low-freezing-point wetting dust suppressant and a preparation method thereof. Background technique [0002] With the rapid development of my country's economy and the improvement of people's living standards, people's attention to the environment is also increasing day by day. The problem of environmental pollution caused by flying dust in our country is relatively serious, which has aroused strong reactions from the society. [0003] Since the 1920s, western countries have begun to use the simplest dust suppressant to reduce coal dust in mines. Since then, chemical dust suppressants have appeared and been gradually used in mines, fossil fuel mining, transportation and storage, etc. area. With the continuous innovation and development of chemical processes and polymer materials, more and more materials and methods have been applied to the innovative deve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/22C09K3/18
CPCC09K3/22C09K3/18
Inventor 高江许灏孙健徐连生赵虹崔兆杰崔媚华杜冰峰
Owner ANSTEEL GRP MINING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap