Preparation method of diamond rope saw bead string based on metal powder extrusion molding

A diamond wire saw and diamond bead technology, applied in metal processing equipment, other manufacturing equipment/tools, manufacturing tools, etc., can solve problems affecting the cutting speed and service life of diamond wire saws, uneven distribution of matrix alloys and diamond particles, problems such as low production efficiency, to achieve the effect of high production efficiency, stable quality and convenient operation

Active Publication Date: 2020-04-10
荣成中磊科技发展有限公司
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing diamond wire saw beading injection molding beading process has the phenomenon that the matrix alloy and diamond particles are unevenly distributed due to the retardation effect of the injection mold runner and the cavity gate on the diamond particles, which seriously affects the cutting speed and cutting speed of the diamond wire saw. Service life and other issues, and low production efficiency, complicated process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of diamond rope saw bead string based on metal powder extrusion molding
  • Preparation method of diamond rope saw bead string based on metal powder extrusion molding
  • Preparation method of diamond rope saw bead string based on metal powder extrusion molding

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] A method for preparing diamond wire saw beads based on metal powder extrusion molding, comprising the following steps:

[0034] Step A, dry-mix metal pre-alloy powder and diamond particles to obtain matrix alloy powder, heat and knead the matrix alloy powder and high-viscosity water-based binder, and then granulate to form matrix alloy for extrusion feeding;

[0035] Step B, extruding and molding the carcass alloy into a carcass alloy tube;

[0036] Step C, cutting the carcass alloy round tube into a ring blank to obtain a diamond beaded ring blank;

[0037] Step D, degreasing and drying the diamond beaded ring blank by soaking in water;

[0038] Step E, putting an iron core support in the diamond beaded ring blank processed in step D, the diamond beaded ring blank covers the iron core support, and then vacuum thermal degreasing and vacuum pressurization Sintering to make diamond wire saw beads.

[0039] Put the iron core support body in the diamond beaded ring blan...

Embodiment 1～5

[0077] Examples 1-5 Weigh each raw material according to Table 1, wherein the electrolytic Cu powder and CuSn 15 The particle size of the pre-alloyed powder is 500 mesh, the particle size of the carbonyl Ni powder, WC powder and Cr powder are respectively 2 / g;

[0078] The particle size classification of the diamond particles is as follows: 35-40 mesh accounts for 30%, 40-45 mesh accounts for 30%, 45-50 mesh accounts for 20% and 50-60 mesh accounts for 20%.

[0079] And Examples 1-5 prepare diamond wire saw beads extruded from metal powder according to the following steps, and the beaded products are subjected to conventional surface treatment and then connected to the steel wire rope to obtain a diamond wire saw:

[0080] Table 1- Raw material composition of diamond wire saw beads

[0081]

[0082]

[0083]

[0084] Step A, preparation of carcass alloy extrusion feed

[0085] Step A1, weighing the metal pre-alloyed powder and diamond particles according to Table 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of diamond rope saw bead strings, in particular to a preparation method of a diamond rope saw bead string based on metal powder extrusion molding. The preparation method of the diamond rope saw bead string based on metal powder extrusion molding comprises the following steps of A, performing dry mixing on metal pre-alloy powder and diamond particles, and heatingand kneading matrix alloy powder and a high-viscosity water-based binder; B, extruding and molding the matrix alloy extrusion feed into a matrix alloy round tube; C, cutting the matrix alloy round tube into a circular ring blank; and D, carrying out dip soaking water solvent degreasing and drying treatment on the diamond bead string ring blank. By means of the preparation method of the diamond rope saw bead string based on metal powder extrusion molding, a diamond rope saw bead string with uniformly-distributed diamond particles in an alloy matrix is prepared, the cutting speed of a diamond rope saw is improved, and the service life is prolonged.

Description

technical field [0001] The invention relates to the field of diamond wire saw beads, in particular to a method for preparing diamond wire saw beads based on metal powder extrusion molding. Background technique [0002] The diamond wire saw is made of cylindrical diamond wire saw beads strung on the wire rope, and then each diamond wire saw bead is fixed through a rubber-plastic spacer to form a complete diamond wire saw, in which the cylindrical diamond wire saw beaded It is composed of a cylindrical iron core support body and a diamond alloy matrix containing diamond particles on the periphery of the core body. However, the existing diamond wire saw beading injection molding beading process has the phenomenon that the matrix alloy and diamond particles are unevenly distributed due to the retardation effect of the injection mold runner and the cavity gate on the diamond particles, which seriously affects the cutting speed and cutting speed of the diamond wire saw. Problems ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F3/20B22F3/10B22F3/15B22F1/00C22C30/04C22C30/02C22C26/00C22C32/00B22F5/00
CPCB22F3/20B22F3/1025B22F3/15C22C30/04C22C30/02C22C9/00C22C9/06C22C19/002C22C19/057C22C19/056C22C26/00C22C32/0052B22F5/00B22F2003/208C22C2026/006B22F2999/00B22F2005/002B22F1/052B22F1/103B22F1/10B22F2201/20
Inventor 高忠麟
Owner 荣成中磊科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com